Electrochemical copolymerization and stability of crosslinked bis[1,2‐(pyrrol)ethoxy]ethane with pyrrole

Abstract The copolymers, pyrrole‐co‐bis[1,2‐(pyrrol)ethoxy]ethane (PEE), were produced by electropolymerization in acetonitrile (containing 0.1 mol L⁻¹ lithium perchlorate). The properties and morphology of these polymers were investigated by cyclic voltammetry, UV–vis absorption spectra and scanning electron microscopy (SEM), respectively. The results exhibit that the cyclic voltammograms and rates of electropolymerization of the prepared copolymers were significantly affected by PEE concentration in water and acetonitrile solution. Higher applied potential was required for the polymerization with decreasing the ratio of pyrrole/PEE. This was ascribed to the steric hindrance of high concentration of N‐substituted groups. The SEM images of the poly(pyrrole‐co‐PEE) and PPEE films show more compact and more smooth morphology compared with that of PPy and cyclic voltammogram of the poly(pyrrole‐co‐PEE) films, which display good electrochemical stability in the mixed solution, indicating that the modification of crosslinked structure was effective for the stabilization of the redox cycles. POLYM. COMPOS., 2009. © 2008 Society of Plastics Engineers