Extensional processing behavior of thermoplastics reinforced with a melt processable glass

Abstract This work was concerned with investigating the processing behavior of thermoplastics reinforced with a melt processable phosphate glass under extensional flows at temperatures used for forming and shaping operations. Injection molded blends consisting of polyetherimide (PEI) and polyphenylene sulfide (PPS) reinforced with 30‐60 wt% phosphate glass were exposed to uniaxial and planar deformation at temperatures above the T_g of the phosphate glass (234°C) to evaluate the effects on the morphology and mechanical properties of the composites. Tensile testing at elevated temperatures (250‐300°C) was used to evaluate the forming behavior and ascertain the conditions most suited for the deformation of the composite blends. A temperature approximately 35°C above the T_g of the P‐glass was found to offer conditions most conducive to the deformation of the PEI/P‐glass blends. The phosphate glass reinforced PEI was found to offer greater retention of properties and smoother surfaces than an E‐glass filled material when exposed to shearfree deformation similar to that seen in a process such as thermoforming. For PPS based composites, the application of planar shearfree deformation near the melting point of the PPS (≈︁ 283°C) resulted in the elongation of the phosphate glass phase which served to enhance the stiffness of the composite blends along the principal deformation direction.