Poly(lactic acid)/palygorskite nanocomposites: Enhanced the physical and thermal properties
Source abstract
Abstract
Poly(lactic acid)/palygorskite (PA) nanocomposites were fabricated through the melt compounding. The significant finding by differential scanning calorimetry (DSC) showed that PA acted as a nucleating agent and accelerated the crystallization process of neat PLA. Consequently, a PLA crystallization peak appeared in all nanocomposites. With increasing PA content, the crystallization temperature increased from 92.1°C to 99.6°C. Dynamic Mechanical Analysis (DMA) indicated that the incorporation of PA hindered the motion of the PLA chains in the matrix, thereby increasing the maximum service temperature of the PLA. The storage modulus, , of the nanocomposite reached a plateau in the low frequency region which indicated formation of a network structure due to the increased interaction sites. The PLA/PA nanocomposites showed significant improvement in physical and thermal properties. POLYM. COMPOS., 38:1600–1608, 2017. © 2015 Society of Plastics Engineers
Source: crossref · Quality: baseline
Research context
OpenAlex topics: biodegradable polymer synthesis and properties · Polymer Nanocomposites and Properties · Bone Tissue Engineering Materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Key Laboratory of New Animal Drug Project, Gansu Province, Key laboratory of Veterinary Pharmaceutical Development, Ministry of Agriculture Lanzhou institute of Husbandry and Pharmaceutical Sciences of CAAS Lanzhou 730050 People's Republic of China
College of Food Science and Engineering Gansu Agricultural University Lanzhou 730070 People's Republic of China
Funding
National Natural Science Foundation of China · Natural Science Foundation of Gansu Province
References (47)
Show source-provided references
1. 10.1016/j.progpolymsci.2008.05.00410.1016/j.progpolymsci.2008.05.004 ↗
2. 10.1111/j.1750-3841.2007.00301.x10.1111/j.1750-3841.2007.00301.x ↗
3. 10.1023/A:102020082243510.1023/A:1020200822435 ↗
4. 10.1016/j.polymer.2010.06.02510.1016/j.polymer.2010.06.025 ↗
5. 10.1016/j.polymer.2007.09.02010.1016/j.polymer.2007.09.020 ↗
6. 10.1002/app.3476110.1002/app.34761 ↗
7. 10.1016/j.polymer.2005.12.06610.1016/j.polymer.2005.12.066 ↗
8. 10.1002/polb.2198610.1002/polb.21986 ↗
9. 10.1002/masy.20055062510.1002/masy.200550625 ↗
10. 10.1021/ma100304n10.1021/ma100304n ↗
11. 10.1016/S0032-3861(03)00583-410.1016/S0032-3861(03)00583-4 ↗
12. 10.1002/app.2510910.1002/app.25109 ↗
13. 10.3139/217.218510.3139/217.2185 ↗
14. 10.1016/j.compscitech.2010.01.01810.1016/j.compscitech.2010.01.018 ↗
15. 10.1021/ma00119a01010.1021/ma00119a010 ↗
16. 10.1016/j.progpolymsci.2012.07.00510.1016/j.progpolymsci.2012.07.005 ↗
17. 10.1016/S0169-1317(00)00016-810.1016/S0169-1317(00)00016-8 ↗
18. 10.1016/j.polymer.2010.08.03710.1016/j.polymer.2010.08.037 ↗
19. 10.1016/j.polymer.2005.05.06710.1016/j.polymer.2005.05.067 ↗
20. 10.1002/pc.2268310.1002/pc.22683 ↗
21. 10.1016/j.polymertesting.2005.11.01210.1016/j.polymertesting.2005.11.012 ↗
22. 10.1016/S0032-3861(97)10203-810.1016/S0032-3861(97)10203-8 ↗
23. 10.1021/ma071258d10.1021/ma071258d ↗
24. 10.1016/j.polymer.2005.07.10110.1016/j.polymer.2005.07.101 ↗
25. 10.1021/ma050739z10.1021/ma050739z ↗
26. 10.1016/j.polymer.2006.07.00110.1016/j.polymer.2006.07.001 ↗
27. 10.1016/j.tca.2004.09.00110.1016/j.tca.2004.09.001 ↗
28. 10.1021/cm03436910.1021/cm034369 ↗
29. 10.1002/polb.2036610.1002/polb.20366 ↗
30. 10.1016/j.compositesb.2006.06.01010.1016/j.compositesb.2006.06.010 ↗
31. 10.1016/j.compscitech.2006.12.01210.1016/j.compscitech.2006.12.012 ↗
32. 10.1016/S0032-3861(01)00086-610.1016/S0032-3861(01)00086-6 ↗
33. 10.1016/j.compscitech.2010.07.00510.1016/j.compscitech.2010.07.005 ↗
34. 10.1016/j.polymdegradstab.2012.06.02810.1016/j.polymdegradstab.2012.06.028 ↗
35. 10.1023/A:101018591030110.1023/A:1010185910301 ↗
36. 10.1016/j.colsurfa.2013.06.01910.1016/j.colsurfa.2013.06.019 ↗
37. 10.1016/j.polymer.2005.05.04010.1016/j.polymer.2005.05.040 ↗
38. 10.1002/app.3093310.1002/app.30933 ↗
39. 10.1016/j.polymertesting.2006.10.00510.1016/j.polymertesting.2006.10.005 ↗
40. 10.1002/pc.2102310.1002/pc.21023 ↗
41. 10.1002/app.1216210.1002/app.12162 ↗
42. 10.1016/j.polymer.2006.03.07410.1016/j.polymer.2006.03.074 ↗
43. 10.1016/j.eurpolymj.2004.10.02010.1016/j.eurpolymj.2004.10.020 ↗
44. 10.1007/s11814-008-0101-710.1007/s11814-008-0101-7 ↗
45. 10.1002/pc.2252110.1002/pc.22521 ↗
46. 10.1016/0032-3861(83)90129-510.1016/0032-3861(83)90129-5 ↗
47. 10.1016/j.tca.2010.08.00410.1016/j.tca.2010.08.004 ↗