Structures and properties of thermoregulated acrylonitrile–methyl acrylate sheet containing microphase change materials

Abstract A series of melt processable poly(acrylonitrile–methyl acrylate) copolymers with a feeding ratio of 85/15 mol% (abbreviated as 85/15 AN/MA below) containing 0–25 wt% of microencapsulated phase change materials (micro‐PCMs) were synthesized by aqueous precipitation polymerization. The number average sequence lengths (NASLs) and tacticity of 85/15 AN/MA were determined using ¹³ C‐NMR. The results showed that the NASL of contiguous AN sequences is 10.00 and the tacticity is atactic with approximately 51% m and 49% r diads (the relative orientation of two adjacent cyanogroup). 85/15 AN/MA containing various contents of micro‐PCMs were processed into sheets in melt condition at 210°C and 20 MPa. The structures and properties of the copolymers and sheets containing micro‐PCMs were studied by using Fourier transform infrared spectroscopy, nuclear magnetic resonance ( ¹ H‐NMR), scanning electron microscopy, differential scanning calorimetry, gel permeation chromatography, X‐ray diffraction, and dynamic mechanical analysis. The composition of AN/MA copolymer agreed well with its monomer feed ratio. The melting enthalpy of the sheets containing 25 wt% of micro‐PCMs was approximately 25 J/g, which increased steadily as the micro‐PCMs content increased. The modulus of the sheets decreased with the micro‐PCMs content increased. The glass transition temperature ( T _g ) of the sheets was in the range of 79.7–81.7°C, which also increased with the micro‐PCMs content increasing. POLYM. COMPOS., 2013. © 2013 Society of Plastics Engineers