Fabrication of amorphous calcium carbonate composite particles‐polymer multilayer films by a layer‐by‐layer method

Organic–inorganic hybrid multilayer films were prepared on a precoated cationic glass substrate by using a layer‐by‐layer (LbL) electrostatic self‐assembly technique with poly(diallyldimethylammonium chloride) as a polycation and submicron‐sized stable amorphous calcium carbonate (ACC) composite particles. The ACC composite particles (ACP) stabilized with poly(acrylic acid) were obtained by a carbonate controlled‐addition method. The average particles size of ACP was (1.8 ± 0.4) × 10² nm. An ethanolic dispersion of ACP was used for the LbL electrostatic self‐assembly technique on the precoated substrate due to instability of ACP in water. The deposition of the particles was confirmed by SEM analysis. The film thickness of the multilayer assembly increased from 230 to 710 nm with increasing the deposition layers. The FTIR spectra of scratched multilayer samples showed characteristic broaden peaks of ACC. The amorphous phase was stable after the LbL assembly process as well as after 2 months in a dry film state. POLYM. COMPOS., 36:330–335, 2015. © 2014 Society of Plastics Engineers