Film formation from nano‐sized polystrene latex covered with various TiO₂ layers

Abstract Steady‐state fluorescence technique was used for studying film formation from TiO₂ covered nano‐sized polystyrene latex particles. The composite films were prepared from pyrene (P)‐labeled PS particles by covering them with various layers of TiO₂ at room temperature. These films then annealed at elevated temperatures in 10 min time interval above glass transition (T_g) temperature of polystyrene. Five different composite films were studied in various TiO₂ layer contents. Fluorescence emission intensity, I_P from P was measured after each annealing step to monitor the stages of film formation. Films present significant increase in I_P above the certain onset temperature called minimum film forming temperature, T₀. However, at higher annealing temperatures, I_P showed a decrease. Increase and decrease in I_P were modeled by void closure and interdiffusion processes and related activation energies were determined, respectively. Dissolution of annealed PS film, with high TiO₂ content presented a nice, ordered nano‐sized ceramic structure, which may predict the construction of nano‐layer photonic crystals. POLYM. COMPOS., 27:651–659, 2006. © 2006 Society of Plastics Engineers