The effect of pyrolysis on the properties of stabilized PAN fabric reinforced phenolic resins for 2D carbon/carbon composites

Abstract Two‐dimensional (2D) carbon/carbon composites were prepared with phenol‐formaldehyde resin and a commercial stabilized PAN fabric. The effect of pyrolysis on the microstructure and flexural strength of the composites during the carbonization process was studied. The interaction between fabric and matrix inhibited the decomposition and the thermal fragmentation, leading to a higher carbon yield for the final composition. Because of the formation of strong bonding in the fiber/matrix interface, the composites made with stabilized PAN fabric showed catastrophic failure and low flexural strength below carbonization temperatures of 600°C. Above 600°C, the flexural strength of the composites increased with the increase in the carbonization temperatures, even when the fracture behavior showed catastrophic failure.