The powder recycled rubber (PRR) can be used as a filler and a modifier for elastomeric materials and asphalt. Composites based on elastomers and recycled rubber powders are a serious challenge for the environment. The main goal of this paper was to study the effect of rubber powder on the mechanical properties of elastomeric composites based on three precursors of the network. Triple blends were prepared using non‐polar natural rubber (NR), polyisoprene rubber (BR), and styrene‐butadiene rubber (SBR) (mass ratio 40/40/20). In all rubber compounds, the carbon black (CB)/PRR mass ratio is constant (60). Samples were prepared using two roll mill. The characteristics of hardening (optimum cure time, scorch time, minimum and maximum torque) of rubber mixtures were tested. Tensile strength, modulus at 100% elongation and elongation at break are decreasing with PRR ratio is increasing. It is due to poor adhesion of PRR into NR/BR/SBR/CB matrix. The thermal degradation temperature shifts to a higher temperature up to 5 phr of PRR in NR/BR/SBR/CB rubber blends. Fourier‐transform infrared spectra of NR/BR/SBR/CB/PRR samples show that the absorption bands shifted 7–15 cm−1 to higher wavenumbers and confirmed rubber–filler interaction. Morphology was assessed by scanning electron microscopy. POLYM. COMPOS., 40:1307–1314, 2019. © 2018 Society of Plastics Engineers
Source: crossref · Quality: baseline
Affiliations
Faculty of Natural Science and Mathematics, Department of Chemistry, University of Priština Kosovska Mitrovica 38220 Serbia
Mitas d.o.o, Department of Wheel System, Industrijska bb Ruma 22400 Serbia
Tigar AD, Quality department Pirot 18300 Serbia
Institute of Nuclear Science Vinča, Laboratory for Radiation Chemistry and Physics, University of Belgrade Belgrade 11000 Serbia
Faculty of Technology, Department of Materials Engineering, University of Novi Sad, 21000 Novi Sad Serbia
Funding
Ministry of Education, Science and Technological Development of the Republic of Serbia