High‐performance polyimide film based hybrid nanostructures: Synthesis, characterization, and properties investigation
Source abstract
Abstract
In this research work, multihybrid nanostructures (carbon nanotube‐graphene oxide‐zinc oxide) based high‐performance polyimide (PI) nanocomposites were prepared via in situ polymerization and their properties (morphological, electrical, and viscous behaviors) were investigated. PI of industrial and laboratory grades was used to study their thermal imidization step after addition of various loadings of multihybrid nanostructures. The use of optimum amount of multihybrid nanostructures seems to be useful to overcome the use of higher amount of different conductive fillers to prepare PI‐based high‐performance nanocomposites for various applications. This study also provides a facile and promising strategy to fabricate multihybrid nanostructured high‐performance PI nanocomposites, which can be used as coating materials in various harsh conditions. POLYM. COMPOS., 39:2650–2661, 2018. © 2016 Society of Plastics Engineers
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Synthesis and properties of polymers · Tribology and Wear Analysis · Conducting polymers and applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Chemistry University of Mumbai, Kalina, Santacruz East Mumbai Maharashtra 400 098 India
University Institute of Chemical Technology, North Maharashtra University Jalgaon Maharashtra 425 001 India
Funding
Council of Scientific and Industrial Research (CSIR), New Delhi, India
References (92)
Show source-provided references
1. 10.1007/978-3-642-19077-3_110.1007/978-3-642-19077-3_1 ↗
2. 10.1016/j.progpolymsci.2012.02.00510.1016/j.progpolymsci.2012.02.005 ↗
3. Ataei S.M. · Adv. Polym. Technol. · 2014 · 33 · 3
4. 10.1016/j.jcis.2009.12.04710.1016/j.jcis.2009.12.047 ↗
5. 10.1039/C5TA01078K10.1039/C5TA01078K ↗
6. 10.3144/expresspolymlett.2007.6010.3144/expresspolymlett.2007.60 ↗
7. 10.1016/j.progpolymsci.2010.04.00310.1016/j.progpolymsci.2010.04.003 ↗
8. 10.1016/j.apsusc.2009.12.04110.1016/j.apsusc.2009.12.041 ↗
9. 10.1007/BF0321876210.1007/BF03218762 ↗
10. S.P.Bapat “Processable High Performance Polymers: Synthesis Characterization and Application ” Ph.D. Thesis University of Pune Pune (2007).
11. 10.1016/j.polymdegradstab.2010.06.02610.1016/j.polymdegradstab.2010.06.026 ↗
12. 10.1016/j.compscitech.2009.06.01810.1016/j.compscitech.2009.06.018 ↗
13. 10.1016/j.synthmet.2011.08.04610.1016/j.synthmet.2011.08.046 ↗
14. 10.1016/j.compscitech.2008.04.00810.1016/j.compscitech.2008.04.008 ↗
15. 10.1016/j.compositesa.2003.09.00310.1016/j.compositesa.2003.09.003 ↗
16. 10.1016/j.eurpolymj.2007.06.02510.1016/j.eurpolymj.2007.06.025 ↗
17. 10.1116/1.325019210.1116/1.3250192 ↗
18. 10.1016/j.polymer.2005.05.12710.1016/j.polymer.2005.05.127 ↗
19. 10.1080/15685551.2012.70549710.1080/15685551.2012.705497 ↗
20. 10.1002/mame.20080024110.1002/mame.200800241 ↗
21. 10.1016/j.compscitech.2005.10.02310.1016/j.compscitech.2005.10.023 ↗
22. 10.1016/j.surfcoat.2009.02.03910.1016/j.surfcoat.2009.02.039 ↗
23. 10.1016/j.compositesb.2013.10.07410.1016/j.compositesb.2013.10.074 ↗
24. 10.1016/j.compositesb.2013.08.06410.1016/j.compositesb.2013.08.064 ↗
25. M.L.ColónandM.A.Meador Modified Single‐Wall Carbon Nanotubes for Reinforce Thermoplastic Polyimide National Aeronautics and Space Administration Glenn Research Center Materials and Structures Division Cleveland OH. Retrived from:ntrs.nasa.gov/archive/nasa/casi.ntrs.nasa.gov/20060013348.pdf.
26. 10.1007/BF0321879910.1007/BF03218799 ↗
27. 10.1016/j.compscitech.2006.12.00610.1016/j.compscitech.2006.12.006 ↗
28. 10.1021/am900682s10.1021/am900682s ↗
29. 10.1002/pi.285510.1002/pi.2855 ↗
30. 10.1002/app.2765710.1002/app.27657 ↗
31. 10.1016/j.compositesa.2012.08.01410.1016/j.compositesa.2012.08.014 ↗
32. 10.1021/nn302871y10.1021/nn302871y ↗
33. 10.1016/j.polymer.2011.09.03310.1016/j.polymer.2011.09.033 ↗
34. 10.1021/am300999g10.1021/am300999g ↗
35. 10.1016/j.eurpolymj.2012.05.01510.1016/j.eurpolymj.2012.05.015 ↗
36. 10.1016/j.compositesa.2012.03.02610.1016/j.compositesa.2012.03.026 ↗
37. 10.1016/j.compositesb.2013.08.06510.1016/j.compositesb.2013.08.065 ↗
38. 10.1016/j.compscitech.2011.06.01310.1016/j.compscitech.2011.06.013 ↗
39. 10.1016/j.polymer.2010.03.02010.1016/j.polymer.2010.03.020 ↗
40. 10.1016/j.polymdegradstab.2010.05.02310.1016/j.polymdegradstab.2010.05.023 ↗
41. 10.1016/j.sna.2013.05.02310.1016/j.sna.2013.05.023 ↗
42. 10.1016/j.synthmet.2010.05.00610.1016/j.synthmet.2010.05.006 ↗
43. D.H.Kim J.M.Caruthers R.B.Pipes andY.Y.Won In Situ‐Polymerized CNT/Polyimide Nanocomposites: Effect of Reaction Stoichiometric on the Glass Transition Properties of the Nanocomposites (2010). Available at:https://aiche.confex.com/aiche/2010/webprogram/Paper199216.html.
44. 10.1016/j.compositesb.2003.09.00710.1016/j.compositesb.2003.09.007 ↗
45. 10.1021/ma049100610.1021/ma0491006 ↗
46. 10.1016/j.compscitech.2005.05.03810.1016/j.compscitech.2005.05.038 ↗
47. 10.1002/pc.2056310.1002/pc.20563 ↗
48. 10.1016/j.polymdegradstab.2007.12.01210.1016/j.polymdegradstab.2007.12.012 ↗
49. 10.1016/j.wear.2011.03.01510.1016/j.wear.2011.03.015 ↗
50. 10.1007/s10965-014-0630-110.1007/s10965-014-0630-1 ↗
51. 10.1016/j.matchemphys.2012.11.06710.1016/j.matchemphys.2012.11.067 ↗
52. 10.1016/j.solidstatesciences.2013.06.01210.1016/j.solidstatesciences.2013.06.012 ↗
53. 10.1016/S0925-4005(97)80011-110.1016/S0925-4005(97)80011-1 ↗
54. 10.1016/j.snb.2009.11.04510.1016/j.snb.2009.11.045 ↗
55. Li X. · J. Appl. Polym. Sci. · 2015 · 133 · 4235510.1002/app.42355 ↗
56. 10.1016/j.carbon.2011.12.03210.1016/j.carbon.2011.12.032 ↗
57. 10.1016/S0266-3538(03)00067-810.1016/S0266-3538(03)00067-8 ↗
58. 10.1016/j.electacta.2011.03.12810.1016/j.electacta.2011.03.128 ↗
59. 10.1016/j.carbon.2011.02.01910.1016/j.carbon.2011.02.019 ↗
60. 10.1016/j.carbon.2012.03.02010.1016/j.carbon.2012.03.020 ↗
61. 10.1039/c3ta15436j10.1039/c3ta15436j ↗
62. 10.1016/j.memsci.2010.08.02310.1016/j.memsci.2010.08.023 ↗
63. S.H.Gardner “An Investigation of the Structure–Property Relationships for High Performance Thermoplastic Matrix Carbon Fiber Composites with a Tailored Polyimide Interphase ” Ph.D. Theses Virginia Polytechnic Institute and State University Virginia (1998).
64. 10.1016/S0921-5093(03)00669-510.1016/S0921-5093(03)00669-5 ↗
65. 10.1021/cm200909x10.1021/cm200909x ↗
66. 10.1002/pola.2674210.1002/pola.26742 ↗
67. 10.1016/j.carbon.2013.04.00310.1016/j.carbon.2013.04.003 ↗
68. 10.1016/j.sna.2009.07.00710.1016/j.sna.2009.07.007 ↗
69. 10.1016/j.ijadhadh.2006.06.00110.1016/j.ijadhadh.2006.06.001 ↗
70. 10.1016/j.snb.2009.11.05410.1016/j.snb.2009.11.054 ↗
71. 10.1016/j.compscitech.2006.01.03810.1016/j.compscitech.2006.01.038 ↗
72. 10.1016/j.compscitech.2013.08.00810.1016/j.compscitech.2013.08.008 ↗
73. 10.1016/j.compscitech.2013.05.01110.1016/j.compscitech.2013.05.011 ↗
74. 10.1016/j.snb.2010.09.01610.1016/j.snb.2010.09.016 ↗
75. 10.1016/j.snb.2013.04.11710.1016/j.snb.2013.04.117 ↗
76. 10.1016/j.seppur.2013.11.01510.1016/j.seppur.2013.11.015 ↗
77. 10.1016/j.carbon.2013.06.09210.1016/j.carbon.2013.06.092 ↗
78. 10.1016/j.cplett.2005.10.08810.1016/j.cplett.2005.10.088 ↗
79. 10.1021/ma051826u10.1021/ma051826u ↗
80. 10.1016/j.polymer.2011.12.05010.1016/j.polymer.2011.12.050 ↗
81. 10.1016/j.snb.2009.11.04110.1016/j.snb.2009.11.041 ↗
82. 10.1016/j.compscitech.2007.10.01110.1016/j.compscitech.2007.10.011 ↗
83. 10.1016/j.polymdegradstab.2007.10.01010.1016/j.polymdegradstab.2007.10.010 ↗
84. 10.1016/j.eurpolymj.2004.08.01410.1016/j.eurpolymj.2004.08.014 ↗
85. S.Ando “Organic/Inorganic‐Polyimide Nanohybrid Materials for Advanced Opto‐Electronic Applications ” inProceedings of the SPIE 7213 Org. Phot. Mater. Devices XI 72130B (2009). doi:10.1117/12.814976.www.op.titech.ac.jp/polymer/lab/sando/Paper_09/Ando_SPIE7213.pdf.10.1117/12.814976 ↗
86. 10.1007/s11705-008-0059-310.1007/s11705-008-0059-3 ↗
87. 10.5772/5345610.5772/53456 ↗
88. 10.1016/j.sna.2006.04.02010.1016/j.sna.2006.04.020 ↗
89. 10.1016/j.snb.2008.08.03410.1016/j.snb.2008.08.034 ↗
90. 10.1039/C5RA16479F10.1039/C5RA16479F ↗
91. 10.1007/s00339-013-7791-310.1007/s00339-013-7791-3 ↗
92. 10.1088/1468-6996/15/1/01420610.1088/1468-6996/15/1/014206 ↗