One‐step synthesis of highly conductive PPy/graphite nanosheets/Gd3+ composites
Source abstract
Abstract
Abstract Highly conductive polypyrrole/graphite nanosheets/Gd3+ (PPy/nanoG/Gd3+) composites are fabricated via in situ polymerization using p‐toluenesulfonic acid as a dopant and FeCl3 as an oxidant. The effects of the graphite nanosheets and Gd3+ loading on the electrical conductivity are investigated. The maximum conductivity of PPy/nanoG/Gd3+ composites about 17.86 S/cm found with 3 wt% graphite nanosheets and 6 wt% Gd3+ at room temperature. The results showed that the high‐aspect‐ratio structure of graphite nanosheets played an important role in forming a conducting network in PPy matrix. Thermal gravimetric analysis demonstrates an improved thermal stability of PPy in the PPy/nanoG/Gd3+ composites. The microstructures of PPy/nanoG/Gd3+ are evidenced by the SEM and TEM examinations. POLYM. COMPOS., © 2011 Society of Plastics Engineers.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Conducting polymers and applications · Supercapacitor Materials and Fabrication · Advanced Sensor and Energy Harvesting Materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (34)
Show source-provided references
1. 10.1016/j.carbon.2007.03.02910.1016/j.carbon.2007.03.029 ↗
2. 10.1016/j.compscitech.2009.02.02810.1016/j.compscitech.2009.02.028 ↗
3. 10.1002/polb.1004210.1002/polb.10042 ↗
4. 10.1016/j.synthmet.2004.05.00710.1016/j.synthmet.2004.05.007 ↗
5. 10.1023/A:100666552780610.1023/A:1006665527806 ↗
6. 10.1002/pc.1029910.1002/pc.10299 ↗
7. 10.1063/1.233715710.1063/1.2337157 ↗
8. 10.1088/0022-3727/38/16/01810.1088/0022-3727/38/16/018 ↗
9. 10.1016/j.synthmet.2006.05.00610.1016/j.synthmet.2006.05.006 ↗
10. 10.1016/j.polymer.2006.03.10710.1016/j.polymer.2006.03.107 ↗
11. 10.1016/j.eurpolymj.2003.08.00510.1016/j.eurpolymj.2003.08.005 ↗
12. 10.1038/442254a10.1038/442254a ↗
13. 10.1016/j.apsusc.2009.08.00610.1016/j.apsusc.2009.08.006 ↗
14. 10.1021/ac902426c10.1021/ac902426c ↗
15. 10.1016/j.cap.2009.11.03910.1016/j.cap.2009.11.039 ↗
16. 10.1021/cm049264110.1021/cm0492641 ↗
17. 10.1021/jp106246310.1021/jp1062463 ↗
18. 10.1016/j.apsusc.2010.02.02810.1016/j.apsusc.2010.02.028 ↗
19. 10.1016/j.electacta.2009.11.08710.1016/j.electacta.2009.11.087 ↗
20. 10.1016/j.jpowsour.2010.09.07510.1016/j.jpowsour.2010.09.075 ↗
21. 10.1016/j.synthmet.2010.09.00810.1016/j.synthmet.2010.09.008 ↗
22. 10.1016/j.matchemphys.2010.07.04910.1016/j.matchemphys.2010.07.049 ↗
23. 10.1016/j.eurpolymj.2006.11.02310.1016/j.eurpolymj.2006.11.023 ↗
24. 10.1016/j.eurpolymj.2004.02.00910.1016/j.eurpolymj.2004.02.009 ↗
25. 10.1016/j.scriptamat.2005.03.03410.1016/j.scriptamat.2005.03.034 ↗
26. 10.1016/j.compscitech.2005.10.01410.1016/j.compscitech.2005.10.014 ↗
27. 10.1016/S0032-3861(02)00599-210.1016/S0032-3861(02)00599-2 ↗
28. 10.1016/j.carbon.2003.12.07410.1016/j.carbon.2003.12.074 ↗
29. 10.1016/j.polymer.2010.10.01410.1016/j.polymer.2010.10.014 ↗
30. 10.1021/cm101132g10.1021/cm101132g ↗
31. 10.1021/jp054335k10.1021/jp054335k ↗
32. 10.1021/jp911766y10.1021/jp911766y ↗
33. 10.1016/j.synthmet.2010.09.01110.1016/j.synthmet.2010.09.011 ↗
34. 10.1021/jp108826e10.1021/jp108826e ↗