Effect of micro‐/nano‐scale aramid fibrillated fibers on the tensile properties of styrene‐butadiene latex
Source abstract
Abstract
Abstract Micro−/nanofibers attract extensive attention of being used as reinforcing agents in polymer composites. Fibrillated fibers have a hierarchical network structure, and a larger specific surface area. Thus, they provide additional anchorage sites in the composite, enhancing the bonding strength between different constituents. In this work, aramid fibrillated micro−/nanofibers (AFMNs) were prepared by a refining process. Styrene‐butadiene latex (SBL) was used as the matrix, and it was mixed with AFMNs, formed AFMN/SBL composites. The mass fractions of AFMNs in the matrix are adjusted to 2%, 4%, 6%, and 8%. The microstructure of AFMNs and the fracture surfaces of AFMN/SBL composites were investigated by microscopical techniques. The results showed that the elastic modulus and tensile strength of AFMN/SBL composites are higher than that of the pure styrene‐butadiene latex film, except tensile strain. With the increase of fiber content, the elastic modulus and tensile strength of AFMN/SBL composites increased from 5.15 MPa to 19.66 MPa and 2.35 MPa to 4.23 MPa, respectively. However, the tensile strain decreased from 101% to 35%. The calculated elastic modulus of Halpin‐Tsai equation is close to the experimental values when the mass fractions of AFMNs is less than 6%.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Fiber-reinforced polymer composites · Natural Fiber Reinforced Composites · Advanced Sensor and Energy Harvesting Materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
School of Light Industry and Engineering South China University of Technology Guangzhou China
References (30)
Show source-provided references
1. Fiber Technology for Fiber‐Reinforced Composites (1st Edition)
2. 10.1002/pol.1983.18021100610.1002/pol.1983.180211006 ↗
3. 10.1177/0307174X110380050110.1177/0307174X1103800501 ↗
4. Yang H. H. · 1993
5. Tsimpris C. W. · Dupont. Tech. Pap. · 2004 · 42 · 2
6. 10.1007/s00289-018-2550-410.1007/s00289-018-2550-4 ↗
7. 10.1002/app.4870210.1002/app.48702 ↗
8. 10.1002/app.4669310.1002/app.46693 ↗
9. 10.1007/s00339-003-2453-510.1007/s00339-003-2453-5 ↗
10. 10.1016/j.compscitech.2018.04.00510.1016/j.compscitech.2018.04.005 ↗
11. Nano‐Aramid Fiber Reinforced Polyurethane Foam
12. E. B.Semmes. U.S. Patent 0292035A1 (2009).
13. R. J.KellyandA.Frances. U.S. Patent 0114641A1 (2003).
14. 10.1016/j.jnoncrysol.2016.10.01510.1016/j.jnoncrysol.2016.10.015 ↗
15. 10.1016/B978-0-08-006421-5.50041-110.1016/B978-0-08-006421-5.50041-1 ↗
16. Pol V. D. · J. F. Rubber World · 1994 · 210 · 1
17. Part 1: Valley beater method
18. FS5 Metso Automation. Product information.https://www.metso.com/.
19. Determination of the specific surface area of solids by gas adsorption‐BET method. ISO 9277‐2010 (2010).
20. Plastics‐Determination of tensile properties · ISO · 2012 · 527 · 2012
21. 10.1007/BF0054792410.1007/BF00547924 ↗
22. 10.1002/pen.76016051210.1002/pen.760160512 ↗
23. Tsai S. W. · 1980
24. 10.1002/pen.76018061210.1002/pen.760180612 ↗
25. Lavengood R. · 1971
26. Twaron Tenjin Company. Product information.https://www.teijinaramid.com.
27. 10.1007/BF0029490910.1007/BF00294909 ↗
28. 10.1007/BF0167205910.1007/BF01672059 ↗
29. 10.1002/pc.1061410.1002/pc.10614 ↗
30. Zheng Y. S. · Rubber Industry · 1998 · 45 · 462