Improved interlaminar crack resistance of glass fiber/poly (phenylene sulfide) thermoplastic composites modified with multiwalled carbon nanotubes
Source abstract
Abstract
ABSTRACT The influences of carboxyl multiwalled carbon nanotubes (MWNTs) on the interlaminar crack initiation and propagation behaviors of glass fiber reinforced poly(phenylene sulphide) (PPS) composites prepared by aqueous suspension prepregging were studied. Interlaminar shear strength (ILSS) as well as the mode‐I fracture toughness was evaluated as a function of the MWNTs contents in the PPS resin. Failure morphology was also investigated to figure out the toughening mechanism. The laminates modified with 1 wt% MWNTs were found to perform 23% and 25% higher ILSS and fracture toughness, respectively. The significant increase indicated that interlaminar damage resistance and tolerance were raised by the addition of MWNTs.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Epoxy Resin Curing Processes · Mechanical Behavior of Composites · Fiber-reinforced polymer composites
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
School of Materials Science and Engineering Beihang University Beijing 100083 China
Funding
National Natural Science Foundation of China
References (46)
Show source-provided references
1. 10.1016/0266-3538(86)90002-310.1016/0266-3538(86)90002-3 ↗
2. 10.1016/j.matdes.2006.03.00610.1016/j.matdes.2006.03.006 ↗
3. 10.1016/j.engfracmech.2008.08.00310.1016/j.engfracmech.2008.08.003 ↗
4. 10.1016/j.compscitech.2006.07.01810.1016/j.compscitech.2006.07.018 ↗
5. 10.1002/pc.1019110.1002/pc.10191 ↗
6. 10.1016/0032-3861(83)90070-810.1016/0032-3861(83)90070-8 ↗
7. 10.1016/S0014-3057(01)00194-X10.1016/S0014-3057(01)00194-X ↗
8. 10.1016/j.polymer.2007.11.03010.1016/j.polymer.2007.11.030 ↗
9. 10.1016/0032-3861(89)90107-910.1016/0032-3861(89)90107-9 ↗
10. 10.1016/S0032-3861(96)01031-210.1016/S0032-3861(96)01031-2 ↗
11. 10.1016/1359-835X(96)00043-710.1016/1359-835X(96)00043-7 ↗
12. 10.1016/j.compositesa.2010.02.00810.1016/j.compositesa.2010.02.008 ↗
13. 10.1016/j.compositesa.2017.06.00110.1016/j.compositesa.2017.06.001 ↗
14. 10.1177/08927057970100030210.1177/089270579701000302 ↗
15. 10.1016/j.compositesa.2018.04.02810.1016/j.compositesa.2018.04.028 ↗
16. 10.1016/j.compositesb.2005.05.01910.1016/j.compositesb.2005.05.019 ↗
17. 10.1016/j.compositesa.2004.06.02910.1016/j.compositesa.2004.06.029 ↗
18. 10.1016/j.compositesa.2007.11.01310.1016/j.compositesa.2007.11.013 ↗
19. 10.1177/002199830303700505310.1177/0021998303037005053 ↗
20. 10.1016/j.engfracmech.2017.05.03010.1016/j.engfracmech.2017.05.030 ↗
21. 10.1016/j.compositesa.2006.03.00110.1016/j.compositesa.2006.03.001 ↗
22. 10.1016/j.carbon.2010.06.01010.1016/j.carbon.2010.06.010 ↗
23. 10.1016/j.carbon.2008.08.01010.1016/j.carbon.2008.08.010 ↗
24. 10.1177/002199830809773510.1177/0021998308097735 ↗
25. 10.1007/s10853-005-5472-010.1007/s10853-005-5472-0 ↗
26. 10.1016/j.compscitech.2010.09.01510.1016/j.compscitech.2010.09.015 ↗
27. 10.1016/j.msea.2007.04.04310.1016/j.msea.2007.04.043 ↗
28. 10.1016/j.compscitech.2007.05.00610.1016/j.compscitech.2007.05.006 ↗
29. Y‐n S. · Carbon · 2017 · 124 · 723
30. 10.1016/j.compositesa.2018.02.03010.1016/j.compositesa.2018.02.030 ↗
31. 10.3390/ma608317110.3390/ma6083171 ↗
32. 10.1016/j.compositesa.2006.09.01010.1016/j.compositesa.2006.09.010 ↗
33. 10.1016/j.compositesb.2014.09.03310.1016/j.compositesb.2014.09.033 ↗
34. 10.1016/j.carbon.2011.03.01110.1016/j.carbon.2011.03.011 ↗
35. 10.1016/0956-7143(93)90096-Q10.1016/0956-7143(93)90096-Q ↗
36. 10.1002/pc.2483010.1002/pc.24830 ↗
37. 10.1016/j.polymertesting.2013.03.02010.1016/j.polymertesting.2013.03.020 ↗
38. 10.1016/j.compositesa.2009.10.00510.1016/j.compositesa.2009.10.005 ↗
39. Plueddemann E. P. · 2016
40. 10.1016/j.compscitech.2009.10.01210.1016/j.compscitech.2009.10.012 ↗
41. 10.1016/0266-3538(92)90099-O10.1016/0266-3538(92)90099-O ↗
42. 10.1016/j.carbon.2012.07.01110.1016/j.carbon.2012.07.011 ↗
43. 10.1177/073168441142163710.1177/0731684411421637 ↗
44. 10.1002/app.4630810.1002/app.46308 ↗
45. 10.1002/(SICI)1521-4095(200005)12:10<750::AID-ADMA750>3.0.CO;2-610.1002/(SICI)1521-4095(200005)12:10<750::AID-ADMA750>3.0.CO;2-6 ↗
46. 10.1016/0001-6160(83)90046-910.1016/0001-6160(83)90046-9 ↗