Dielectric response of conducting carbon‐black‐filled ethylene–octene copolymer microcellular foams

Dielectric response of conducting carbon‐black‐filled ethylene–octene copolymer microcellular foams has been investigated with variation of blowing agent and filler loading in the frequency range of 100 Hz to 5 MHz and temperature range from 30 to 100°C. With increase in blowing agent loading, the dielectric permittivity increases for both unfilled as well as carbon‐black‐filled microcellular foams. The experimental complex impedance plots were compared with model‐fitted plots obtained by taking an equivalent circuit of (CQR) (CR).The values of R_b (bulk resistance), R_gb (grain boundary resistance), bulk capacitance (C_b), and grain boundary capacitance (C_gb) at different temperatures were calculated and compared with experimental values. The relaxation time due to bulk effect (τ_b) has been calculated from relaxation frequency (f_r). The dc conductivity (σ_dc) decreases with rise in temperature indicating the existence of positive temperature coefficient of resistance in the material. The activation energy (E_a) calculated from the relaxation time due to bulk effect (τ_b) was found to be 0.446 eV, whereas it was 0.363 eV from the dc conductivity plot in the temperature range of 30–100°C. POLYM. COMPOS., 37:3398–3410, 2016. © 2015 Society of Plastics Engineers