Structure development in thermoset recyclate‐filled polypropylene composites
Source abstract
Abstract
Abstract Polypropylene containing comminuted fiber reinforced thermoset recyclate has been shown to exhibit enhanced mechanical properties relative to particulate‐filled materials. Optimum mechanical performance in these recyclate‐filled materials is achieved in compositions made from rubber‐modified polypropylene containing maleic anhydride‐modified PP in conjuction with silane coupling agent. Although matrix crosslinking was found to enhance properties in both filled and unfilled systems, composite properties are dominated by the development of strong interfacial bonding between polypropylene and recyclate reinforcement. A mechanism for the formation of interfacial bonding is proposed involving reaction between maleic anhydride functionalized PP, formation of trisilanol groups and their subsequent condensation with hydroxyl groups on the recyclate surfaces, together with molecular entanglement and co‐crystallization of the grafted and ungrafted polypropylene molecules. Furthermore, in the absence of treatment there is evidence that the elastomer particles encapsulate the filler particles. However, this effect is strongly hindered when functionalized‐PP is added, either in isolation or in combination with the silane co‐treatment. The crystalline nucleation of PP by thermoset recyclate and treatment is also considered. The treatment system investigated was found to promote interfacial bonding to both the polyester (DMC) and woven glassreinforced phenolic recyclates investigated, suggesting it may be suitable for treating mixed composite scrap.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Polymer crystallization and properties · Polymer Nanocomposites and Properties · Fiber-reinforced polymer composites
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (25)
Show source-provided references
1. Bream C. E. · 1997 · 202
2. “Recycling of thermoset composites as a structural filler in thermoplastics ” C. E. Bream PhD thesis Brunel University U.K. (1998).
3. 1992
4. Exxon Chemical Ltd. “ Exxcelor PO 1015 ”Technical Data Sheet and Certificate of Analysis.
5. 10.1002/app.1991.07048003510.1002/app.1991.070480035 ↗
6. ASTMD 2765–90 “Standard test methods for determination of gel content and swell ratio of crosslinked ethylene plastics ” Published August (1990).
7. BS 2782: Part 11: Method 1106E Plastics piping systems‐Crosslinked polyethylene (PE‐X) pipes‐Determination of the degree of crosslinking by solvent extraction British Standards Institution.
8. 10.1002/pola.1995.08033050910.1002/pola.1995.080330509 ↗
9. 10.1002/(SICI)1097-4628(19970118)63:3<283::AID-APP2>3.0.CO;2-J10.1002/(SICI)1097-4628(19970118)63:3<283::AID-APP2>3.0.CO;2-J ↗
10. Haslam J. · 1972
11. Silane treatment of mineral fillers—practical aspects
12. “ Silcat crosslinking chemicals for polyolefins ”OSI Specialties (formerly Union Carbide) technical data sheet August (1991).
13. 10.1016/0141-3910(95)00053-O10.1016/0141-3910(95)00053-O ↗
14. Evidence for chemical grafting during extrusion of copoly(ethylene/vinylacetate)‐aminopropyltris (alkoxy) silane mixtures
15. 10.1002/app.1989.07037021310.1002/app.1989.070370213 ↗
16. 10.1007/BF0072104110.1007/BF00721041 ↗
17. 10.1002/app.1994.07053021210.1002/app.1994.070530212 ↗
18. Filler surface treatments for particulate mineral/thermoplastic composites10.1177/147776069501100204 ↗
19. 10.1002/pc.75013050610.1002/pc.750130506 ↗
20. 10.1002/pol.1982.13020050410.1002/pol.1982.130200504 ↗
21. 10.1002/pc.75009050910.1002/pc.750090509 ↗
22. Structure and molecular motions in crosslinked isotactic polypropylene10.1177/147823919300100601 ↗
23. Chemical modification of polypropylene
24. 10.1007/BF0037527110.1007/BF00375271 ↗
25. 10.1007/BF0037629210.1007/BF00376292 ↗