Crosslinking characterization of a polyimide: AFR700B

John D. Russell, John L. Kardos

Polymer Composites· Volume 18· Issue 5
Publisher page

Abstract

Abstract Crosslinking in AFR700B polyimide was studied using several techniques. Crosslinking could not be detected using Fourier transform infrared spectroscopy (FTIR) and differential scanning calorimetry (DSC). Swelling in n‐methyl pyrrolidone (NMP) showed network formation occurs at cure temperatures ≥325°C (617°F), but the reaction kinetics could not be determined from the data. Dynamic mechanical analysis (DMA) studies have shown that the storage modulus (G′) increased with increasing cure temperature up to 350°C (662°F), and was constant above 350°C (662°F), indicating that crosslinking via the reverse Diels‐Alder reaction was occurring. A broad secondary transition was seen in the loss modulus (G″) curves, centered between 150 and 180°C (302 and 356°F). This secondary transition appeared at a cure temperature of 300°C (572°F) and became more dominant with increasing temperature and time. This secondary transition was not seen for cures <300°C (572°F) when the chains have not crosslinked. Therefore, this is likely due to a crosslink bond rather than one in the backbone. At 1 atm, crosslinking followed second‐order kinetics based on the increase in glass transition temperature (Tg). The Arrhenius plot of the rate constant showed a break in the slope, possibly indicating a change in reaction mechanism. At 1.38 MPa (200 psi), the Tg data was too scattered to determine the kinetics.
Source: crossref · Quality: baseline

Research context

OpenAlex topics: Synthesis and properties of polymers · Epoxy Resin Curing Processes · Polymer Nanocomposites and Properties

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (27)

Show source-provided references
1. Reardon J. P. · Mater. Eng. · 1992 · 109 · 8
2. T. T.Serafini P. G.Cheng K. K.Ueda andW. F.Wright presented 22nd Intern. SAMPE Tech. Conf. Boston (1990).
3. 10.1002/app.1982.07027112010.1002/app.1982.070271120 ↗
4. General Electric Aircraft Engines “High Temperature Organic Matrix Composite Technology Transition ” USAF Contract F33615–92–C–5957.
5. D. Warnock A. Hakim 1993 Wright‐Patterson AFB Ohio
6. K. E. G.ThorpandA. S.Crasto presented Amer. Soc. Compos. 10th Tech. Conf. Santa Monica Calif. (1995).
7. D.Cornelia presented 39th Intern. SAMPE Symp. Anaheim Calif. (1994).
8. B. P.Rice presented 1st AFR700 Symp. Fairborn Ohio (1991).
9. B.Rice W.Price J.Lute andK.Johnson presented 23rd Intern. SAMPE Tech. Conf. Kiamesha Lake N.Y. (1991).
10. J. L.Kardos M. P.Dudukovic B.Joseph J. L.Vasat D. H.Kim andF.Wang‐Hanratty Control of Polyimide Condensation Composite Processing Air Force Technical Report WL‐TR‐94–4039 Materials Directorate Wright Laboratory Air Force Materiel Command Wright‐Patterson AFB OH 45433 (1994).
11. Also published in part inIntern. SAMPE Tech. Conf. R. J. Martinez H. Arris J. A. Emerson and G. Pike eds. 27 843(1995).
12. 10.1002/pi.498020050510.1002/pi.4980200505 ↗
13. Wilson D. · SAMPE J. · 1987 · 3 · 35
14. 10.1021/ma50004a06910.1021/ma50004a069 ↗
15. 10.1016/0032-3861(89)90075-X10.1016/0032-3861(89)90075-X ↗
16. Tungare A. V. · SPE ANTEC Tech. Papers · 1989 · 35 · 568
17. 10.1002/app.1974.07018071010.1002/app.1974.070180710 ↗
18. Alston W. B. · SAMPE J. · 1981 · 17 · 5
19. Chen L. W. · J. Chinese Inst. Chem. Eng. · 1989 · 20 · 233
20. 10.1002/pol.1979.17017082510.1002/pol.1979.170170825 ↗
21. Wasserman A. · 1965
22. B.BuynyandG. D.Mayorga presented High Temple XV Workshop Santa Fe N.M. (1995).
23. Browning C. E. · 1986
24. 10.1080/1558372690854589710.1080/15583726908545897 ↗
25. 10.1080/1060132690805381110.1080/10601326908053811 ↗
26. 10.1002/polb.1995.09033101210.1002/polb.1995.090331012 ↗
27. 10.1063/1.174765010.1063/1.1747650 ↗