Performance evaluation of synthesized acrylic acid grafted polypropylene within CaCO₃/polypropylene composites

Abstract A polymeric coupling agent acrylic acid grafted polypropylene (AAgPP) was synthesized and its efficiency in CaCO₃/PP composite was investigated. The grafting of acrylic acid monomer (AA) onto polypropylene was performed using an internal mixer. The effect of peroxyde, acrylic acid monomer content, temperature and RPM was studied. A grafting reaction between the polypropylene and the acrylic acid was evidenced through FTIR, UV, DSC and MFI testing. The highest grafting yield was obtained at 0.85 phr peroxide and 5 phr acrylic acid. The selected mixing temperature was 200°C, the rotor speed 150 rpm and the residence time 5 min. The obtained coupling agent (AAgPP) was used with 30 wt% CaCO₃ filled polypropylene. Strong interactions with the composite were observed. The effect of increasing the coupling agent content on Izod impact and tensile properties was investigated. A maximum in the above properties is attained at 15 wt% AAgPP. The most important effect is clearly shown in the Izod test. In fact, a threefold increase has been observed for either notched and untoched specimen. The 15 wt% AAgPP is considered to be a critical concentration for the composite considered. This corresonds to maximum interactions occurring between the matrix and the filler. SEM analysis clearly shows strong interactions between the filler and the matrix in the presence of acrylic acid grafted polypropylene. This is another proof of the efficiency of the synthesized AAgPP as a potential coupling agent for CaCO₃ filled PP.