Mechanical, thermal and morphological analysis of polylactic acid‐woven glass fiber composites fabricated by additive manufacturing

Abstract Polylactic acid (PLA), a biodegradable thermoplastic, is being used significantly in a wide range of applications because of its environmentally friendly nature. 3D printing is an innovative technique that is used to fabricate polymer composites with complex contours and high precision. Conventional 3D printing technologies use fiber reinforcement in the form of filament. However, fibers in the form of sheets, when used in composite materials, improve the distribution of load and enhance the multi‐directional strength. This study investigates the improvement in the tensile strength of PLA‐based composite by integrating woven glass fibers (WGF) during 3D printing processing. The composites were fabricated using an FDM‐based 3D printer where the WGF sheet was used as reinforcement and PLA filament was used as the matrix material. The main input parameters consist of the number of WGF layers and the orientation of the WGF. Taguchi orthogonal array was used to fabricate composite samples with different combinations of input parameters and then these samples were tested to evaluate the tensile properties. The finding shows that PLA composites reinforced with four layers of glass fiber at 0/90° fiber orientation showed the highest tensile strength of 52.85 MPa and a thermal degradation temperature of 330.49 °C. Highlights 3D printing of WGF‐PLA composite and mechanical characterization. The composite specimen showed the highest tensile strength of 52.85 MPa. The thermal degradation temperature reached 330.49 °C in TGA analysis. ANN predicted the optimal combination of 4 fiber layers with 0/90° orientation. Uniform PLA deposition reduced voids and enhanced interlayer adhesion.