In situ preparation and characterization of biocompatible acrylate‐terminated polyurethane containing chemically modified multiwalled carbon nanotube
Source abstract
Abstract
Biodegradable acrylate‐terminated polyurethane/acrylate (APUA) filled with 2‐hydroxyethyl methacrylate functionalized carbon nanotube (CNT‐HEMA) was prepared by in situ free radical crosslinking. CNT‐HEMA enhanced crystallinity of soft domain and caused more phase separation between hard and soft domains of APUA. Tensile testing showed a considerable improvement in elastic modulus (∼160%) and tensile strength (∼30%) at 1 wt% loading. Morphological features of APUA induced by nanotubes were found to be dominant on mechanical properties of APUA/CNT‐HEMA. CNT‐HEMA increased water contact angle of APUA; however, wettability of APUA/CNT‐HEMA maintained in acceptable range for biomedical applications. APUA/CNT‐HEMA exhibited lower hydrophobic nature compared to many CNT filled polyurethanes reported in literature due to HEMA functional group, making APUA/CNT‐HEMA nanocomposites adequate for biomedical applications. POLYM. COMPOS., 39:E297–E307, 2018. © 2017 Society of Plastics Engineers
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Polymer composites and self-healing · Polymer Nanocomposites and Properties · Polymer Foaming and Composites
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Chemical and Petroleum Engineering Sharif University of Technology Tehran Iran
Funding
Sharif University of Technology
References (70)
Show source-provided references
1. 10.1002/pc.2353210.1002/pc.23532 ↗
2. 10.1002/pi.496410.1002/pi.4964 ↗
3. 10.1016/j.compositesb.2015.03.04910.1016/j.compositesb.2015.03.049 ↗
4. 10.1002/pi.297110.1002/pi.2971 ↗
5. Li L. · Polym. Compos. · 2016 · 37 · 2248
6. 10.1016/j.carbon.2005.10.01110.1016/j.carbon.2005.10.011 ↗
7. Sundar L.S. · 2012
8. 10.1016/j.biomaterials.2006.07.04410.1016/j.biomaterials.2006.07.044 ↗
9. 10.1016/j.bone.2008.04.01310.1016/j.bone.2008.04.013 ↗
10. 10.1016/j.apsusc.2014.09.19810.1016/j.apsusc.2014.09.198 ↗
11. 10.1021/ma400035j10.1021/ma400035j ↗
12. 10.1002/adfm.20030520010.1002/adfm.200305200 ↗
13. 10.1080/1539445X.2010.52517310.1080/1539445X.2010.525173 ↗
14. 10.1016/j.polymer.2010.04.06910.1016/j.polymer.2010.04.069 ↗
15. 10.1016/j.eurpolymj.2007.05.01410.1016/j.eurpolymj.2007.05.014 ↗
16. 10.1016/j.eurpolymj.2011.01.00510.1016/j.eurpolymj.2011.01.005 ↗
17. 10.1002/jbm.a.3209510.1002/jbm.a.32095 ↗
18. 10.1016/j.biomaterials.2005.05.07910.1016/j.biomaterials.2005.05.079 ↗
19. 10.1002/jbm.a.3070810.1002/jbm.a.30708 ↗
20. 10.4236/jbise.2009.2100710.4236/jbise.2009.21007 ↗
21. 10.1016/j.actbio.2010.01.03010.1016/j.actbio.2010.01.030 ↗
22. Pereira I.H. · Acta Biomater. · 2010 · 8 · 305610.1016/j.actbio.2010.02.036 ↗
23. 10.1016/j.msec.2014.05.05610.1016/j.msec.2014.05.056 ↗
24. 10.1002/app.2942410.1002/app.29424 ↗
25. 10.1002/app.3693610.1002/app.36936 ↗
26. 10.1016/j.jmbbm.2014.10.01210.1016/j.jmbbm.2014.10.012 ↗
27. 10.5185/amlett.2015.588810.5185/amlett.2015.5888 ↗
28. 10.1016/j.compscitech.2011.02.00610.1016/j.compscitech.2011.02.006 ↗
29. Xia H. · Soft Matter · 2005 · 1 · 3886
30. 10.1016/j.actbio.2008.06.01510.1016/j.actbio.2008.06.015 ↗
31. 10.1016/j.polymdegradstab.2005.08.00110.1016/j.polymdegradstab.2005.08.001 ↗
32. 10.1016/j.polymer.2012.06.02010.1016/j.polymer.2012.06.020 ↗
33. 10.1002/marc.20050065810.1002/marc.200500658 ↗
34. 10.1002/polb.2106910.1002/polb.21069 ↗
35. Kumar N.A. · Eur. Polym. J. · 2008 · 44 · 57910.1016/j.eurpolymj.2007.12.009 ↗
36. 10.1016/j.colsurfa.2009.10.01910.1016/j.colsurfa.2009.10.019 ↗
37. 10.1016/j.carbon.2006.04.00510.1016/j.carbon.2006.04.005 ↗
38. 10.1002/macp.20060026610.1002/macp.200600266 ↗
39. 10.1088/0957-4484/19/49/49570710.1088/0957-4484/19/49/495707 ↗
40. 10.1007/978-1-4899-3176-410.1007/978-1-4899-3176-4 ↗
41. 10.1021/ma60017a02110.1021/ma60017a021 ↗
42. 10.1016/j.polymer.2004.01.04910.1016/j.polymer.2004.01.049 ↗
43. 10.1016/j.polymer.2005.03.02110.1016/j.polymer.2005.03.021 ↗
44. Petrovi Z.S. · Polymer · 2013 · 54 · 37210.1016/j.polymer.2012.10.019 ↗
45. 10.4012/dmj.2010-13510.4012/dmj.2010-135 ↗
46. 10.1016/j.matchemphys.2011.05.02810.1016/j.matchemphys.2011.05.028 ↗
47. 10.1002/app.2762510.1002/app.27625 ↗
48. 10.1016/j.compositesa.2004.10.00410.1016/j.compositesa.2004.10.004 ↗
49. 10.1016/j.diamond.2006.11.08610.1016/j.diamond.2006.11.086 ↗
50. 10.1016/j.msea.2011.06.05310.1016/j.msea.2011.06.053 ↗
51. Agarwal B. D. · 2006
52. 10.1063/1.12068010.1063/1.120680 ↗
53. 10.1063/1.157956810.1063/1.1579568 ↗
54. 10.1002/mats.20120007010.1002/mats.201200070 ↗
55. 10.1016/j.eurpolymj.2011.10.01110.1016/j.eurpolymj.2011.10.011 ↗
56. 10.1016/j.polymer.2007.06.04610.1016/j.polymer.2007.06.046 ↗
57. 10.1002/mame.20050033510.1002/mame.200500335 ↗
58. 10.1016/j.compscitech.2010.07.02110.1016/j.compscitech.2010.07.021 ↗
59. 10.1016/j.polymer.2013.11.00310.1016/j.polymer.2013.11.003 ↗
60. Patterson W. · Engineering · 1976 · 16
61. Nielsen L.E. · 1994
62. Thostenson E.T. · J. Phys. D: Appl. Phys. · 2003 · 47 · 57310.1088/0022-3727/36/5/323 ↗
63. Skipaa T. · Polymer · 2010 · 51 · 20110.1016/j.polymer.2009.11.047 ↗
64. 10.1002/pen.1100710.1002/pen.11007 ↗
65. 10.1016/j.polymer.2006.10.01410.1016/j.polymer.2006.10.014 ↗
66. 10.1002/pat.325510.1002/pat.3255 ↗
67. Larraz L. · Eur. Polym. J. · 2009 · 45 · 209610.1016/j.eurpolymj.2009.03.013 ↗
68. 10.1016/S0142-9612(01)00289-710.1016/S0142-9612(01)00289-7 ↗
69. Gorna K. · Polym. Degrad. Stab. · 2003 · 49 · 47510.1016/S0141-3910(02)00363-4 ↗
70. 10.1039/C4RA02442G10.1039/C4RA02442G ↗