Properties on novel PVDF‐HFP‐based composite polymer electrolyte with vinyltrimethoxylsilane‐modified ZSM‐5
Source abstract
Abstract
Abstract A kind of novel poly(vinylidene fluoride‐co‐hexafluoropropylene) (PVDF‐HFP)‐based composite polymer electrolyte doped with vinyltrimethoxylsilane (DB171 silane)‐modified ZSM‐5 is prepared by phase inversion method (denoted as M‐ZSM‐5 membrane). Physical and chemical properties of M‐ZSM‐5 membrane are studied by SEM, FTIR, TG‐DSC, EIS, and LSV. The results show that thermal and electrochemical stability can reach 400°C and 5 V, respectively; temperature dependence of ionic conductivity follows Vogel–Tamman–Fulcher relation and ionic conductivity at room temperature is up to 4.2 mS/cm; the interfacial resistance reaches a stable value about 325 Ω after 5 days storage at room temperature, which suggests that it can be potentially suitable as electrolyte in polymer lithium ion battery. POLYM. COMPOS., 2012. © 2012 Society of Plastics Engineers
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Advanced Battery Materials and Technologies · Conducting polymers and applications · Supercapacitor Materials and Fabrication
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (38)
Show source-provided references
1. 10.1016/j.jpowsour.2006.07.03810.1016/j.jpowsour.2006.07.038 ↗
2. 10.1016/j.eurpolymj.2005.09.01710.1016/j.eurpolymj.2005.09.017 ↗
3. 10.1016/S0378-7753(98)00193-110.1016/S0378-7753(98)00193-1 ↗
4. 10.1016/j.electacta.2011.08.04810.1016/j.electacta.2011.08.048 ↗
5. 10.1016/j.jpowsour.2011.10.14110.1016/j.jpowsour.2011.10.141 ↗
6. 10.1016/j.memsci.2011.05.04310.1016/j.memsci.2011.05.043 ↗
7. 10.1016/0013-4686(94)00345-210.1016/0013-4686(94)00345-2 ↗
8. 10.1016/j.electacta.2008.10.01110.1016/j.electacta.2008.10.011 ↗
9. 10.1016/j.memsci.2009.02.01810.1016/j.memsci.2009.02.018 ↗
10. 10.1016/j.jpowsour.2010.10.09610.1016/j.jpowsour.2010.10.096 ↗
11. 10.1016/j.electacta.2009.04.00210.1016/j.electacta.2009.04.002 ↗
12. 10.1016/j.jpowsour.2009.08.01510.1016/j.jpowsour.2009.08.015 ↗
13. 10.1016/j.jpowsour.2008.03.04510.1016/j.jpowsour.2008.03.045 ↗
14. 10.1016/S0032-3861(02)00215-X10.1016/S0032-3861(02)00215-X ↗
15. 10.1016/j.electacta.2006.02.03810.1016/j.electacta.2006.02.038 ↗
16. 10.1016/S0378-7753(01)01008-410.1016/S0378-7753(01)01008-4 ↗
17. 10.1016/j.jpowsour.2008.03.02710.1016/j.jpowsour.2008.03.027 ↗
18. 10.1016/j.electacta.2008.08.00710.1016/j.electacta.2008.08.007 ↗
19. 10.1016/j.electacta.2008.05.08210.1016/j.electacta.2008.05.082 ↗
20. 10.1016/j.matchemphys.2011.01.04610.1016/j.matchemphys.2011.01.046 ↗
21. 10.1016/j.electacta.2007.10.05810.1016/j.electacta.2007.10.058 ↗
22. 10.1016/j.jpowsour.2009.05.01110.1016/j.jpowsour.2009.05.011 ↗
23. 10.1016/j.elecom.2008.08.03610.1016/j.elecom.2008.08.036 ↗
24. 10.1016/j.jpowsour.2007.05.05110.1016/j.jpowsour.2007.05.051 ↗
25. 10.1016/j.jpowsour.2006.02.03510.1016/j.jpowsour.2006.02.035 ↗
26. 10.1016/j.electacta.2009.01.01410.1016/j.electacta.2009.01.014 ↗
27. 10.1016/j.ssi.2006.01.03210.1016/j.ssi.2006.01.032 ↗
28. 10.1016/j.ssi.2005.02.01610.1016/j.ssi.2005.02.016 ↗
29. 10.1016/j.jpowsour.2005.10.01010.1016/j.jpowsour.2005.10.010 ↗
30. 10.1016/j.electacta.2006.01.01610.1016/j.electacta.2006.01.016 ↗
31. 10.1016/j.ssi.2006.06.01610.1016/j.ssi.2006.06.016 ↗
32. 10.1016/j.electacta.2010.05.07210.1016/j.electacta.2010.05.072 ↗
33. 10.1016/j.progpolymsci.2007.07.00410.1016/j.progpolymsci.2007.07.004 ↗
34. 10.1016/j.jpowsour.2004.03.07810.1016/j.jpowsour.2004.03.078 ↗
35. 10.1016/j.ssi.2010.09.05710.1016/j.ssi.2010.09.057 ↗
36. 10.1016/j.polymer.2010.07.03710.1016/j.polymer.2010.07.037 ↗
37. 10.1016/j.electacta.2005.02.02510.1016/j.electacta.2005.02.025 ↗
38. 10.1016/j.jpowsour.2006.02.02910.1016/j.jpowsour.2006.02.029 ↗