Effects of LiCl on crystallization, thermal, and mechanical properties of polyamide 6/wood fiber composites

In the presented study, lithium chloride (LiCl) was used as a modifier to reduce the melting point of polyamide 6 (PA6) and low melting point PA6/wood fiber composites (LPA6/WFC) were prepared with a hot‐press machine. Non‐isothermal crystallization analysis revealed that as little as 3 wt% LiCl decreased the crystallinity of LPA6/WFC from 21.43% to approximately 10% and reduced the melting point of composites from above 220°C to below 200°C, hence the composites can be produced industrially as well as severe degradation of wood fibers can be avoided. Both LiCl and wood fibers increased the glass transition temperature (T_g) of LPA6/WFC, and the T_g of the composites can reach up to 83.2°C, indicating that composites subjected to high temperature circumstances can still retain good dimensional stability and rigidity. In addition, the composites exhibited good mechanical properties, revealed by a flexural strength of the composites of up to 92 MPa. POLYM. COMPOS., 39:E1574–E1580, 2018. © 2017 Society of Plastics Engineers