Mode I and Mode II delamination resistance and mechanical properties of woven glass/epoxy–PU IPN composites
Source abstract
Abstract
Abstract The effect of polyurethane on the mechanical properties and Mode I and Mode II interlaminar fracture toughness of glass/epoxy composites were studied. Polyurethanes (PU) synthesized using polyols and toluene diisocyanate were employed as modifier for epoxy resin by forming interpenetrating polymer network. The PU/Epoxy IPN was used as matrix material for GFRP. PU modified epoxy composite laminates having varying PU contents were prepared. The effect of PU content on the mechanical properties like interlaminar fracture toughness (Mode I, G1c and Mode II, GIIc), tensile strength, flexural strength, and Izod impact strength were studied. The morphological studies were conducted on the fractured surface of the composite specimen by scanning electron microscopy (SEM). Tensile strength, flexural strength, and impact strength of PU‐modified epoxy composite laminates were found to increase inline with interlaminar fracture toughness (G1c and GIIc) with increasing PU content to a certain limit and then it was found to decrease with increase in PU content. It was observed that toughening of epoxy with PU increases the Mode I and Mode II delamination toughness up to 17 and 120% higher than that of untoughened composite specimen, respectively. POLYM. COMPOS., 2008. © 2008 Society of Plastics Engineers
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Mechanical Behavior of Composites · Structural Analysis of Composite Materials · Epoxy Resin Curing Processes
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (23)
Show source-provided references
1. 10.1016/S0032-3861(00)00641-810.1016/S0032-3861(00)00641-8 ↗
2. 10.1016/S0014-3057(99)00113-510.1016/S0014-3057(99)00113-5 ↗
3. 10.1016/S0266-3538(02)00316-010.1016/S0266-3538(02)00316-0 ↗
4. 10.1016/0266-3538(92)90099-O10.1016/0266-3538(92)90099-O ↗
5. 10.1016/j.polymer.2004.08.02010.1016/j.polymer.2004.08.020 ↗
6. 10.1016/0266-3538(94)90103-110.1016/0266-3538(94)90103-1 ↗
7. 10.1016/0266-3538(95)00089-510.1016/0266-3538(95)00089-5 ↗
8. 10.1016/S1359-835X(01)00109-910.1016/S1359-835X(01)00109-9 ↗
9. 10.1016/j.ijsolstr.2004.06.01010.1016/j.ijsolstr.2004.06.010 ↗
10. 10.1016/S0266-3538(98)00167-510.1016/S0266-3538(98)00167-5 ↗
11. 10.1016/S0266-3538(00)00080-410.1016/S0266-3538(00)00080-4 ↗
12. ASTM D5528‐01 Annual Book of ASTM Standards 15.03 Philadelphia (2000).
13. 10.1016/S0266-3538(97)00102-410.1016/S0266-3538(97)00102-4 ↗
14. 10.1016/S0266-3538(03)00088-510.1016/S0266-3538(03)00088-5 ↗
15. Chatterjee S.N. · J. Compos. Mater. · 1991 · 25 · 47010.1177/002199839102500501 ↗
16. 10.1016/j.compositesa.2003.09.02810.1016/j.compositesa.2003.09.028 ↗
17. J.W.Hutchinson Department of Solids Mechanics Master's thesis. The Technical University of Denmark (1989).
18. ASTM D790M‐84. Philadelphia (1984).
19. 10.1016/j.compositesa.2003.10.00510.1016/j.compositesa.2003.10.005 ↗
20. 10.1016/0266-3538(96)00052-810.1016/0266-3538(96)00052-8 ↗
21. 10.1016/S0032-3861(98)00464-910.1016/S0032-3861(98)00464-9 ↗
22. 10.1016/0010-4361(95)93669-B10.1016/0010-4361(95)93669-B ↗
23. 10.1016/j.mseb.2006.02.02610.1016/j.mseb.2006.02.026 ↗