Fabrication of continuous carbon fiber reinforced polyamide 6 composites by means of self‐resistance electric heating

Xiaoyu Wang, Yunhuan Liu, Qingzhu He, Can Weng, Zhanyu Zhai

Polymer Composites· Volume 42· Issue 11
Publisher page

Abstract

Abstract In the conventional process of thermoplastic composites, a heating stage from the external heat source usually consumes a large amount of energy. To solve this problem, self‐resistance electric (SRE) heating of carbon fiber‐reinforcement was introduced to form a continuous carbon fiber reinforced polyamide 6 (CF/PA 6) composite based on film stacking technique in this paper. The temperature distribution was first measured to verify the temperature uniformity for SRE heating process. X‐ray photoelectron spectroscopy (XPS) was used to assess effects on the chemical properties of carbon fibers from SRE heating and conventional convective heating. To evaluate forming quality by SRE heating, the physical properties, crystallinity, and mechanical properties of CF/PA 6 composites were measured. The results show that the forming time and energy consumption of SRE heating process are significantly reduced compared with that of the traditional heating process because of fast heating/cooling rate. While fast heating/cooling rate of SRE heating process leads to a higher void content, which finally results in a slightly lower flexural strength and impact properties of composite laminates. It is clear that SRE heating technique is one of the energy‐ and cost‐effective ways to fabricate continuous carbon fiber reinforced thermoplastic composites although the forming quality is still improved in future investigation.
Source: crossref · Quality: baseline

Research context

OpenAlex topics: Fiber-reinforced polymer composites · Mechanical Behavior of Composites · Smart Materials for Construction

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

College of Mechanical and Electrical Engineering Central South University Changsha China

State Key Laboratory of High Performance and Complex Manufacturing Central South University Changsha China

Funding

National Natural Science Foundation of China

References (40)

Show source-provided references
1. IEA.CO2 Emissions from Fuel Combustion 2019. 2019.
2. 10.2495/HPSM12021110.2495/HPSM120211 ↗
3. 10.1007/s10443-012-9258-710.1007/s10443-012-9258-7 ↗
4. Britnell D. J. · 2002
5. 10.1177/08927057880010030510.1177/089270578800100305 ↗
6. 10.1016/S0266-3538(99)00175-X10.1016/S0266-3538(99)00175-X ↗
7. 10.1179/174328008X32522310.1179/174328008X325223 ↗
8. 10.1016/j.promfg.2018.07.25410.1016/j.promfg.2018.07.254 ↗
9. 10.3390/polym1007072010.3390/polym10070720 ↗
10. 10.1016/s1359-835x(99)00016-010.1016/s1359-835x(99)00016-0 ↗
11. 10.1002/pc.1032310.1002/pc.10323 ↗
12. 10.1016/S1359-835X(98)00056-610.1016/S1359-835X(98)00056-6 ↗
13. 10.1016/B978-185617495-4/50007-X10.1016/B978-185617495-4/50007-X ↗
14. Dave R. · 2012
15. 10.1177/089270571141969510.1177/0892705711419695 ↗
16. 10.1016/B978-0-323-37468-2.00002-610.1016/B978-0-323-37468-2.00002-6 ↗
17. 10.1115/1.291932410.1115/1.2919324 ↗
18. 10.1163/156855194X0001510.1163/156855194X00015 ↗
19. 10.1016/j.compositesa.2013.10.02410.1016/j.compositesa.2013.10.024 ↗
20. 10.1177/002199830203600417110.1177/0021998302036004171 ↗
21. A.Geyer T.Koslowski&C.Bontenpresented at Regional Conf. Graz (PPS Graz) September 2015.https://doi.org/10.1063/1.4965564.10.1063/1.4965564 ↗
22. 10.1365/s35725-012-0102-710.1365/s35725-012-0102-7 ↗
23. 10.1016/S0266-3538(99)00112-810.1016/S0266-3538(99)00112-8 ↗
24. 10.1007/s00170-019-03707-010.1007/s00170-019-03707-0 ↗
25. 10.1177/073168441775105810.1177/0731684417751058 ↗
26. 10.11648/j.ajmme.20190301.1210.11648/j.ajmme.20190301.12 ↗
27. 10.2495/HPSM14025110.2495/HPSM140251 ↗
28. ASTM American Society of Testing Materials Standard Test Methods for Void Content of Reinforced Plastics. D2734/D2734M‐03 ASTM International West Conshohocken PA2003.
29. ASTM American Society of Testing Materials Standard Test Method for Tensile Properties of Polymer Matrix Composite Materials. D3039/D3039M‐08 ASTM International West Conshohocken PA2008.
30. ASTM American Society of Testing Materials Standard Test Method for Flexural Properties of Polymer Matrix Composite Materials. D7264/D7264M‐15 ASTM International West Conshohocken PA2015.
31. ASTM American Society of Testing Materials Standard Test Method for Measuring the Damage Resistance of a Fiber‐Reinforced Polymer‐Matrix Composite to a Concentrated Quasi‐Static Indentation Force D6264/D6264M‐12 ASTM International West Conshohocken PA2012.
32. Moulder J. · 1992
33. 10.1016/j.apsusc.2013.10.09310.1016/j.apsusc.2013.10.093 ↗
34. 10.1002/pc.2502010.1002/pc.25020 ↗
35. 10.1016/j.apsusc.2011.04.12910.1016/j.apsusc.2011.04.129 ↗
36. 10.1016/j.apsusc.2011.03.04710.1016/j.apsusc.2011.03.047 ↗
37. 10.16490/j.cnki.issn.1001-3660.2016.04.01510.16490/j.cnki.issn.1001-3660.2016.04.015 ↗
38. 10.1016/j.polymer.2014.09.05210.1016/j.polymer.2014.09.052 ↗
39. 10.1016/j.eurpolymj.2004.12.00910.1016/j.eurpolymj.2004.12.009 ↗
40. 10.1016/j.compstruct.2017.06.00710.1016/j.compstruct.2017.06.007 ↗