Ethylene vinyl acetate/Mg‐Al LDH nanocomposites by solution blending

Abstract Partially exfoliated ethylene vinyl acetate (EVA‐40, 40% vinyl acetate content)/layered double hydroxide (LDH) nanocomposites using organically modified layered double hydroxide (DS‐LDH) have been synthesized by solution intercalation method. X‐ray diffraction (XRD) and transmission electron microscopy (TEM) studies of nanocomposites shows the formation of exfoliated LDH nanolayers in EVA‐40 matrix at lower DS‐LDH contents and partially intercalated/exfoliated EVA‐40/MgAl LDH nanocomposites at higher DS‐LDH contents. These EVA‐40/MgAl LDH nanocomposites demonstrate a significant improvement in tensile strength and elongation at break for 3 wt% of DS‐LDH filler loading compare to neat EVA‐40 matrix. Thermogravimetric analysis also shows that the thermal stability of the nanocomposites increases with DS‐LDH content in EVA‐40. POLYM. COMPOS., 2009. © 2008 Society of Plastics Engineers