Energy absorptions and failure modes of 3D orthogonal hybrid woven composite struck by flat‐ended rod
Source abstract
Abstract
Abstract Three‐dimensional (3D) orthogonal woven composite has high stiffness, strength, and energy absorption capacity along X, Y, and Z directions because there are no crimps in yarn. This paper presents mechanical behaviors and energy absorptions of the 3D orthogonal hybrid woven composite under transverse impact and quasi‐static loading by flat‐ended rod. The failure load and energy absorption of the composite increase with the increase in loading rate. The damage morphology of the composite coupon manifests the compression failure in the front side and tension failure in rear side. There are no delaminations in the composite coupons for both quasi‐static and impact loading for the existence of Z‐yarn in fabric structure. This phenomenon manifests the potential application of the 3D orthogonal woven composite to impact resistance areas. POLYM. COMPOS., 27: 410–416, 2006. © 2006 Society of Plastics Engineers
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Mechanical Behavior of Composites · Fiber-reinforced polymer composites · Textile materials and evaluations
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (22)
Show source-provided references
1. 10.1515/SECM.1996.5.2.8310.1515/SECM.1996.5.2.83 ↗
2. 10.1177/00405175030730010710.1177/004051750307300107 ↗
3. 10.1016/S1359-835X(03)00084-810.1016/S1359-835X(03)00084-8 ↗
4. C.A.Weeks R.S.Bertke M.W.Laber “Soft Body Impact Damage Tolerance of Laminated and 3D Woven Composites ”inProceedings of the 1997 ASME International Mechanical Engineering Congress and Exposition Dallas TX Nov 16–21 1997. American Society of Mechanical Engineers Materials Division MD 80 169(1997).10.1115/IMECE1997-0662 ↗
5. 10.1016/S1359-835X(99)00029-910.1016/S1359-835X(99)00029-9 ↗
6. 10.1016/S0266-3538(03)00021-610.1016/S0266-3538(03)00021-6 ↗
7. 10.1016/S1359-835X(03)00143-X10.1016/S1359-835X(03)00143-X ↗
8. B.A.Gama M.J.Haque J.W.GillespieJr. A.E.Bogdanovich “Impact Damage and Energy Absorption of a 3D Orthogonal Weave Composite Unit Cell Model ”in49th International SAMPE Symposium and Exhibition: Materials and Processing Technology—60 Years of SAMPE Progress SAMPE 2004 Long Beach CA May 16–20 2004. International SAMPE Symposium and Exhibition 49 2637(2004).
9. 10.1016/j.compositesa.2004.07.00810.1016/j.compositesa.2004.07.008 ↗
10. Modeling approaches for 3D orthogonal woven composites10.1177/073168449801700605 ↗
11. Models for predicting thermomechanical properties of three‐dimensional orthogonal woven composites10.1177/073168449901800204 ↗
12. 10.1016/S1359-835X(99)00071-810.1016/S1359-835X(99)00071-8 ↗
13. 10.1016/S1359-835X(99)00070-610.1016/S1359-835X(99)00070-6 ↗
14. 10.1177/07316840177267875110.1177/073168401772678751 ↗
15. 10.1016/S1359-835X(98)00159-610.1016/S1359-835X(98)00159-6 ↗
16. 10.1016/S0263-8223(02)00108-310.1016/S0263-8223(02)00108-3 ↗
17. 10.1016/S1359-835X(03)00213-610.1016/S1359-835X(03)00213-6 ↗
18. 10.1177/07316840177267911010.1177/073168401772679110 ↗
19. 10.1177/07316840212898771610.1177/073168402128987716 ↗
20. T.B.Langston Y.P.Qiu “The Tensile Properties of Three Dimensional Air Textured Aramid Reinforced Composites ”in2003 ASME International Mechanical Engineering Congress Washington DC Nov 15–21 2003. American Society of Mechanical Engineers Textile Engineering Division TED 3 77(2003).10.1115/IMECE2003-55526 ↗
21. 10.1016/S1359-835X(99)00034-210.1016/S1359-835X(99)00034-2 ↗
22. Meyers M.C. · 1995