Nanocomposites of Triethoxysilane Functionalized Solution Polymerized Styrene‐Butadiene Rubber by Hydrosilylation as High‐Performance Green Tire
Source abstract
Abstract
ABSTRACT In this study, a novel and efficient rubber modification, triethoxysilane (TES) functionalized solution polymerized styrene‐butadiene rubber (FSSBR) in‐chain via hydrosilylation is applied and corresponding FSSBR/silica nanocomposites are investigated as green tire tread. The ethoxy groups of FSSBR significantly enhance filler–rubber interaction to improve silica dispersion. As a consequence, the silica nanoparticles in the FSSBR/silica nanocomposite are effectively isolated. Compared to the SSBR/silica nanocomposite, the FSSBR with 10% molar percentage of TES to 1,2‐butadiene/silica nanocomposite exhibits a reduction in rolling resistance, heat build‐up, and Akron abrasion by 30.6%, 38.0%, and 35.6%, respectively, and an improvement in wet‐skid resistance by 88%. The application of in‐chain FSSBR through hydrosilylation nanocomposites offers a promising route for the development of high‐performance, eco‐friendly tires.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Polymer Nanocomposites and Properties · Tribology and Wear Analysis · Polymer composites and self-healing
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
The Key Laboratory of Beijing City on Preparation and Processing of Novel Polymer Materials Beijing University of Chemical Technology Beijing China
References (66)
Show source-provided references
1. 10.1007/s11356‐022‐20894‐810.1007/s11356‐022‐20894‐8 ↗
2. 10.1016/j.compscitech.2022.10941310.1016/j.compscitech.2022.109413 ↗
3. 10.1016/j.compositesa.2004.10.00410.1016/j.compositesa.2004.10.004 ↗
4. 10.5254/1.354497210.5254/1.3544972 ↗
5. 10.2346/1.214879410.2346/1.2148794 ↗
6. 10.1002/app.2574410.1002/app.25744 ↗
7. 10.1016/j.polymer.2014.02.06710.1016/j.polymer.2014.02.067 ↗
8. 10.1021/acs.iecr.8b0645810.1021/acs.iecr.8b06458 ↗
9. 10.1016/S0014‐3057(00)00157‐910.1016/S0014‐3057(00)00157‐9 ↗
10. 10.1021/acs.iecr.6b0351710.1021/acs.iecr.6b03517 ↗
11. 10.1016/j.compositesb.2017.02.02110.1016/j.compositesb.2017.02.021 ↗
12. 10.1021/acs.iecr.1c0370210.1021/acs.iecr.1c03702 ↗
13. 10.1002/app.4665310.1002/app.46653 ↗
14. 10.5254/rct.19.8152210.5254/rct.19.81522 ↗
15. 10.1016/j.polymer.2023.12608210.1016/j.polymer.2023.126082 ↗
16. 10.1021/acs.iecr.3c0004610.1021/acs.iecr.3c00046 ↗
17. 10.1021/acs.iecr.8b0573810.1021/acs.iecr.8b05738 ↗
18. 10.1039/C9RA02783A10.1039/C9RA02783A ↗
19. 10.1039/C4RA09492A10.1039/C4RA09492A ↗
20. 10.5254/1.353838010.5254/1.3538380 ↗
21. 10.1002/masy.20045110310.1002/masy.200451103 ↗
22. 10.1039/C9RA08325A10.1039/C9RA08325A ↗
23. 10.1002/pen.1036710.1002/pen.10367 ↗
24. 10.1039/C4RA17281G10.1039/C4RA17281G ↗
25. 10.1016/j.ccr.2010.12.02510.1016/j.ccr.2010.12.025 ↗
26. 10.1016/S0022‐328X(00)99347‐110.1016/S0022‐328X(00)99347‐1 ↗
27. 10.1021/ja01561a05410.1021/ja01561a054 ↗
28. 10.1002/cjoc.20170002410.1002/cjoc.201700024 ↗
29. 10.1002/anie.20030174210.1002/anie.200301742 ↗
30. 10.1021/ma00226a00110.1021/ma00226a001 ↗
31. 10.1021/ma00028a05810.1021/ma00028a058 ↗
32. 10.1039/JM992020105710.1039/JM9920201057 ↗
33. 10.1016/j.jcat.2019.01.02610.1016/j.jcat.2019.01.026 ↗
34. 10.1002/app.4706910.1002/app.47069 ↗
35. 10.1016/j.polymer.2018.04.03910.1016/j.polymer.2018.04.039 ↗
36. 10.1016/j.molcata.2009.04.01910.1016/j.molcata.2009.04.019 ↗
37. 10.1016/S0032‐3861(99)00160‐310.1016/S0032‐3861(99)00160‐3 ↗
38. 10.1021/acs.macromol.2c0196910.1021/acs.macromol.2c01969 ↗
39. 10.1016/j.polymertesting.2019.10617310.1016/j.polymertesting.2019.106173 ↗
40. 10.1016/j.polymer.2024.12755010.1016/j.polymer.2024.127550 ↗
41. 10.1080/09276440.2017.124155910.1080/09276440.2017.1241559 ↗
42. 10.3390/ma1418524610.3390/ma14185246 ↗
43. 10.1002/app.4266810.1002/app.42668 ↗
44. 10.1002/app.4791810.1002/app.47918 ↗
45. 10.1002/pc.3008410.1002/pc.30084 ↗
46. 10.5254/1.354826210.5254/1.3548262 ↗
47. 10.1002/app.2744410.1002/app.27444 ↗
48. 10.5254/1.354737510.5254/1.3547375 ↗
49. 10.1016/j.polymer.2024.12668210.1016/j.polymer.2024.126682 ↗
50. 10.1002/app.2862110.1002/app.28621 ↗
51. 10.1002/app.2684310.1002/app.26843 ↗
52. 10.1016/j.compositesb.2020.10830110.1016/j.compositesb.2020.108301 ↗
53. 10.1016/j.polymer.2020.12224410.1016/j.polymer.2020.122244 ↗
54. 10.1016/j.compscitech.2020.10860110.1016/j.compscitech.2020.108601 ↗
55. 10.1007/s13726‐019‐00761‐z10.1007/s13726‐019‐00761‐z ↗
56. 10.1016/j.carbpol.2012.09.05410.1016/j.carbpol.2012.09.054 ↗
57. 10.1002/pc.2936310.1002/pc.29363 ↗
58. 10.1016/j.compositesa.2014.03.00710.1016/j.compositesa.2014.03.007 ↗
59. 10.2346/tire.18.46010310.2346/tire.18.460103 ↗
60. 10.1002/pc.2761010.1002/pc.27610 ↗
61. 10.1016/j.coco.2024.10183610.1016/j.coco.2024.101836 ↗
62. 10.1016/j.apsusc.2021.14981910.1016/j.apsusc.2021.149819 ↗
63. 10.1021/acsami.1c2160510.1021/acsami.1c21605 ↗
64. 10.1016/j.cej.2022.13911310.1016/j.cej.2022.139113 ↗
65. 10.1016/j.engfracmech.2020.10719510.1016/j.engfracmech.2020.107195 ↗
66. 10.1016/j.matdes.2013.07.02410.1016/j.matdes.2013.07.024 ↗