High Dielectric Constant Polycarbonate/Nylon Multilayer Films Capacitors with Self-Healing Capability
Source abstract
Abstract
With the fast development of high-temperature metal oxide semiconductor field effect transistors for power electronics in electric vehicles, current state-of-the-art biaxially oriented polypropylene (BOPP) film capacitors need further improvement because they have a temperature rating of only 85 °C without derating the voltage to maintain a long lifetime. If a high-temperature polymer can replace BOPP without sacrificing the overall dielectric performance and cost, it is possible to remove the current water-cooling system for capacitors and significantly reduce the cost of the power electronic unit. In this work, we demonstrated new polycarbonate (PC)/nylon multilayer films (MLFs), which has a potential for even higher temperature rating because of the higher melting temperature for nylons (e.g., nylon-6). Structural and dielectric studies showed that these PC/nylon MLFs had a similar dielectric performance, such as dielectric constant, dielectric loss, and breakdown strength, as the PC/poly(vinylidene fluoride) PVDF MLFs, which were developed in the past. These PC/nylon MLFs could perform well up to 120 °C, which was limited by the glass transition temperature of PC at 145 °C. More intriguingly, packaged PC/nylon-12 MLF capacitors exhibited a self-healing capability, which had been difficult for packaged high-temperature film capacitors. Because self-healing is such a fundamental requirement for polymer film capacitors, our PC/nylon MLFs offer a potential for next-generation high-temperature and high-energy density film capacitors.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Dielectric materials and actuators · Advanced Sensor and Energy Harvesting Materials · Synthesis and properties of polymers
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Macromolecular Science and Engineering, Case Western Reserve University, Cleveland, Ohio 44106-7202, United States
PolymerPlus, LLC, 7700 Hub Parkway, Valley View, Ohio 44125, United States
SBE, Inc., 81 Parker Road, Barre, Vermont 05641-9106 United States
National Synchrotron Light Source II, Brookhaven National Laboratory, Upton, New York 11973, United States
Funding
Division of Industrial Innovation and Partnerships
References (37)
Show source-provided references
1. Husain, I. Electric and Hybrid Vehicles: Design Fundamentals; CRC Press: Boca Raton, FL, 2010, 274 pages.
2. Setter N. · 199310.1007/978-3-0348-7551-6 ↗
3. 10.1002/adma.20180215510.1002/adma.201802155 ↗
4. 10.1038/nmat229710.1038/nmat2297 ↗
5. 10.1016/S0378-7753(96)80003-610.1016/S0378-7753(96)80003-6 ↗
6. 10.1109/27.73602010.1109/27.736020 ↗
7. 10.1109/5.93147510.1109/5.931475 ↗
8. 10.1002/adma.20120279010.1002/adma.201202790 ↗
9. Montanari, D.; Saarinen, K.; Scagliarini, F.; Zeidler, D.; Niskala, M.; Nender, C. Film Capacitors for Automotive and Industrial Applications. Proceedings of CARTS U.S.A. 2009; Jacksonville, FL, March 30–April 2, 2009.
10. Ho J. · 2009
11. 10.1007/s11664-014-3440-710.1007/s11664-014-3440-7 ↗
12. Zhang X.-M. · Rev. Adv. Mater. Sci. · 2016 · 46 · 22
13. 10.1146/annurev-matsci-070317-12443510.1146/annurev-matsci-070317-124435 ↗
14. 10.1021/acs.macromol.6b0266910.1021/acs.macromol.6b02669 ↗
15. Demeuse M. T. · 201110.1533/9780857092953 ↗
16. Schosseler L. · Bodo’s Power Systems · 2016 · 50
17. 10.1021/jz501831q10.1021/jz501831q ↗
18. 10.1021/acs.macromol.7b0113710.1021/acs.macromol.7b01137 ↗
19. Langhe D. · 2015
20. 10.1021/ma202405710.1021/ma2024057 ↗
21. 10.1109/CEIDP.1993.37896210.1109/CEIDP.1993.378962 ↗
22. 10.1002/pol.1968.16006030410.1002/pol.1968.160060304 ↗
23. Wunderlich B. · 2005
24. 10.1021/acs.macromol.5b0273910.1021/acs.macromol.5b02739 ↗
25. 10.1002/polb.2237510.1002/polb.22375 ↗
26. Fried J. R. · 2007 · 21710.1007/978-0-387-69002-5_13 ↗
27. 10.1063/1.472234810.1063/1.4722348 ↗
28. 10.1021/ma401660k10.1021/ma401660k ↗
29. 10.1021/acsaem.7b0021110.1021/acsaem.7b00211 ↗
30. 10.1021/acs.macromol.8b0103710.1021/acs.macromol.8b01037 ↗
31. 10.1021/acsami.5b0294410.1021/acsami.5b02944 ↗
32. 10.1021/ma50002a00610.1021/ma50002a006 ↗
33. 10.1063/1.35378910.1063/1.353789 ↗
34. 10.1016/j.polymer.2013.11.04210.1016/j.polymer.2013.11.042 ↗
35. 10.1039/C7TC03653A10.1039/C7TC03653A ↗
36. 10.1088/0022-3727/42/17/17530410.1088/0022-3727/42/17/175304 ↗
37. 10.1021/ma500249p10.1021/ma500249p ↗