Molecularly tailored SAMs for Ru interconnects: high-temperature stability, suppressed metal diffusion, and enhanced adhesion
Source abstract
Abstract
The miniaturization of integrated circuits (ICs) necessitates alternative diffusion barriers with reduced electrical resistance to mitigate the RC delay effect. Self-assembled monolayers (SAMs), with their molecular-scale thickness (1–2 nm), offer a promising solution for controlling Ru interdiffusion while preserving low resistivity. This study investigates the effectiveness of 2-hydroxybenzylimine-triethoxysilane (2-HBITES), benzyliminetriethoxysilane (BITES), and n-octyltriethoxysilane (OTS) as SAM-based diffusion barriers for Ru metallization. SAM functionalization was confirmed using X-ray photoelectron spectroscopy (XPS) and time-of-flight secondary ion mass spectrometry (ToF-SIMS), while barrier performance was evaluated through sheet resistance measurements, X-ray diffraction (XRD), transmission electron microscopy (TEM), and scanning transmission electron microscopy (STEM) following rapid thermal annealing (RTA). The results demonstrate that SAM-modified substrates effectively suppress Ru silicide formation, with 2-HBITES exhibiting the highest thermal stability, delaying Ru interdiffusion until 800 °C, compared to 775 °C for BITES, 725 °C for OTS, and 600 °C for non-functionalized Ru/Ox/Si. The superior performance of 2-HBITES is attributed to its salicylaldimine terminal group, which enhances Ru adhesion and diffusion suppression. Additionally, this study provides direct XPS evidence of SAM retention within a Ru/SAM/Ox/Si structure post-annealing at 700 °C, highlighting the potential of SAMs as thermally stable, ultrathin diffusion barriers for advanced interconnect technologies. As microchips become smaller and faster, the materials used to connect electronic components face increasing performance and reliability challenges. This study introduces a molecular engineering strategy that uses self-assembled monolayers (SAMs)—extremely thin molecular films—to improve the stability and performance of metal wiring in advanced electronics. By tailoring the molecular structure of the SAM, the team developed a new interface material that enhances adhesion, reduces electrical resistance, and withstands high temperatures. Specifically, the engineered monolayer coating demonstrated strong bonding with ruthenium (a metal used in chip wiring), effectively blocking unwanted diffusion and preserving material integrity even at 700 °C. This work offers a new pathway for creating ultra-thin, high-performance materials critical for next-generation semiconductor devices. This summary was initially drafted using artificial intelligence, then revised and fact-checked by the author. This study demonstrates the use of molecularly tailored self-assembled monolayers (SAMs) as ultrathin diffusion barriers and adhesion liners for Ru interconnects. Compared to non-functionalized and methyl-terminated surfaces, hydroxylated arylimine SAMs such as 2-HBITES effectively suppress Ru interdiffusion, prevent film delamination, and significantly enhance thermal stability up to 700 °C. The SAM-functionalized interfaces exhibit improved adhesion and structural integrity, offering a promising strategy for future scaled interconnect technologies.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Copper Interconnects and Reliability · Semiconductor materials and interfaces · 3D IC and TSV technologies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (100+)
Show source-provided references
1. Moore, G. E. Cramming more components onto integrated circuits, reprinted from electronics, volume 38, Number 8, April 19, 1965, Pp. 114 Ff. IEEE Solid-State Circuits Soc. Newsl. 11, 33–35 (2006).10.1109/N-SSC.2006.4785860 ↗
2. Kim, J.-S. et al. Addressing interconnect challenges for enhanced computing performance. Science 386, eadk6189 (2024).10.1126/science.adk6189 ↗
3. Kim, H.-W. Recent trends in copper metallization. Electronics 11, 2914 (2022).10.3390/electronics11182914 ↗
4. Adelmann, C. et al. Alternative metals for advanced interconnects. In Proc. IEEE International Interconnect Technology Conference (IEEE: San Hose, CA, USA, 2014) 173–176. https://doi.org/10.1109/IITC.2014.6831863.10.1109/IITC.2014.6831863 ↗
5. Croes, K. et al. Interconnect metals beyond copper: reliability challenges and opportunities. In Proc. 2018 IEEE International Electron Devices Meeting (IEDM) (IEEE: San Francisco, CA, 2018) 5.3.1–5.3.4. https://doi.org/10.1109/IEDM.2018.8614695.10.1109/IEDM.2018.8614695 ↗
6. Tierno, D. et al. Cobalt and ruthenium drift in ultra-thin oxides. Microelectron. Reliab. 100–101, 113407 (2019).10.1016/j.microrel.2019.113407 ↗
7. Xu, H. et al. Effect of thickness scaling on the permeability and thermal stability of Ta(N) diffusion barrier. Appl. Surf. Sci. 498, 143887 (2019).10.1016/j.apsusc.2019.143887 ↗
8. Karabacak, T. Lu, T.-M. Enhanced step coverage by oblique angle physical vapor deposition. J. Appl. Phys. 97 https://doi.org/10.1063/1.1937476 (2005).10.1063/1.1937476 ↗
9. Wang, S.-Q., Schlueter, J., Gondran, C. & Boden, T. Step coverage comparison of Ti/TiN deposited by collimated and uncollimated physical vapor deposition techniques. J. Vac. Sci. Technol. B 14, 1846–1852 (1996).10.1116/1.588565 ↗
10. Lo, C.-L. et al. Opportunities and challenges of 2D materials in back-end-of-line interconnect scaling. J. Appl. Phys. 128, 080903 (2020).10.1063/5.0013737 ↗
11. Ciofi, I. et al. Impact of wire geometry on interconnect RC and circuit delay. IEEE Trans. Electron Devices 63, 2488–2496 (2016).10.1109/TED.2016.2554561 ↗
12. Ahmed, M., Li, Y., Chen, W. & Li, E.-P. Diffusion barrier prediction of graphene and boron nitride for copper interconnects by deep learning. IEEE Access 8, 210542–210549 (2020).10.1109/ACCESS.2020.3039257 ↗
13. Kuo, C.-Y. et al. MoS2 as an effective Cu diffusion barrier with a back-end compatible process. ACS Appl. Mater. Interfaces 15, 47845–47854 (2023).10.1021/acsami.3c12267 ↗
14. Kozhakhmetov, A., Torsi, R., Chen, C. Y. & Robinson, J. A. Scalable low-temperature synthesis of two-dimensional materials beyond graphene. J. Phys. Mater. 4, 012001 (2020).10.1088/2515-7639/abbdb1 ↗
15. Neumaier, D., Pindl, S. & Lemme, M. C. Integrating graphene into semiconductor fabrication lines. Nat. Mater. 18, 525–529 (2019).10.1038/s41563-019-0359-7 ↗
16. Hoofman, R. J. O. M. et al. Challenges in the implementation of low-k dielectrics in the back-end of line. Microelectron. Eng. 80, 337–344 (2005).10.1016/j.mee.2005.04.088 ↗
17. Lee, S.-E. et al. Surface-functionalized interfacial self-assembled monolayers as copper electrode diffusion barriers for oxide semiconductor thin-film transistor. ACS Appl. Electron. Mater. 1, 430–436 (2019).10.1021/acsaelm.8b00132 ↗
18. Khaderbad, M. A. et al. Porphyrin self-assembled monolayer as a copper diffusion barrier for advanced CMOS technologies. IEEE Trans. Electron Devices 59, 1963–1969 (2012).10.1109/TED.2012.2195184 ↗
19. Liu, X., Wang, Q., Wu, S. & Liu, Z. Enhanced CVD of copper films on self-assembled monolayers as ultrathin diffusion barriers. J. Electrochem. Soc. 153, C142 (2006).10.1149/1.2158577 ↗
20. Weiss, E. A. et al. Influence of defects on the electrical characteristics of mercury-drop junctions: self-assembled monolayers of n-alkanethiolates on rough and smooth silver. J. Am. Chem. Soc. 129, 4336–4349 (2007).10.1021/ja0677261 ↗
21. Witt, C. et al. Testing the limits of TaN barrier scaling. In Proc. 2018 IEEE International Interconnect Technology Conference (IITC) 2018; 54–56. https://doi.org/10.1109/IITC.2018.8430289.10.1109/IITC.2018.8430289 ↗
22. Maitani, M. M., Daniel, T. A., Cabarcos, O. M. & Allara, D. L. Nascent metal atom condensation in self-assembled monolayer matrices: coverage-driven morphology transitions from buried adlayers to electrically active metal atom nanofilaments to overlayer clusters during aluminum atom deposition on alkanethiolate/gold monolayers. J. Am. Chem. Soc. 131, 8016–8029 (2009).10.1021/ja901376w ↗
23. Gandhi, D. D. et al. Annealing-induced interfacial toughening using a molecular nanolayer. Nature 447, 299–302 (2007).10.1038/nature05826 ↗
24. Chung, Y. et al. Coupled self-assembled monolayer for enhancement of Cu diffusion barrier and adhesion properties. RSC Adv. 4, 60123–60130 (2014).10.1039/C4RA08134J ↗
25. Parambadath, S., Mathew, A., Mohan, A. & Ha, C.-S. Chelation dependent selective adsorption of metal ions by schiff base modified SBA-15 from aqueous solutions. J. Environ. Chem. Eng. 8, 104248 (2020).10.1016/j.jece.2020.104248 ↗
26. De Clercq, B. & Verpoort, F. Ring-closing metathesis, kharasch addition and enol ester synthesis catalysed by a novel class of ruthenium(II) complexes. Tetrahedron Lett. 42, 8959–8963 (2001).10.1016/S0040-4039(01)01952-9 ↗
27. De Clercq, B. & Verpoort, F. A new class of ruthenium complexes containing schiff base ligands as promising catalysts for atom transfer radical polymerization and ring opening metathesis polymerization. J. Mol. Catal. Chem. 180, 67–76 (2002).10.1016/S1381-1169(01)00451-4 ↗
28. Maestre Caro, A., Maes, G., Borghs, G. & Whelan, C. M. Screening self-assembled monolayers as Cu diffusion barriers. Microelectron. Eng. 85, 2047–2050 (2008).10.1016/j.mee.2008.04.014 ↗
29. Lee, S. et al. Tailored self-assembled monolayer using chemical coupling for indium–gallium–zinc oxide thin-film transistors: multifunctional copper diffusion barrier. ACS Appl. Mater. Interfaces 14, 56310–56320 (2022).10.1021/acsami.2c16593 ↗
30. Organosiloxane nanolayer as diffusion barrier for Cu metallization on Si. Appl. Surf. Sci. 567, 150800. https://doi.org/10.1016/j.apsusc.2021.150800 (2021).10.1016/j.apsusc.2021.150800 ↗
31. Mikami, N., Hata, N., Kikkawa, T. & Machida, H. Robust self-assembled monolayer as diffusion barrier for copper metallization. Appl. Phys. Lett. 83, 5181–5183 (2003).10.1063/1.1635665 ↗
32. Krishnamoorthy, A., Chanda, K., Murarka, S. P., Ramanath, G. & Ryan, J. G. Self-assembled near-zero-thickness molecular layers as diffusion barriers for Cu metallization. Appl. Phys. Lett. 78, 2467–2469 (2001).10.1063/1.1365418 ↗
33. Caro, A. M. et al. Bottom-up engineering of subnanometer copper diffusion barriers using NH2-derived self-assembled monolayers. Adv. Funct. Mater. 20, 1125–1131 (2010).10.1002/adfm.200902072 ↗
34. Ramanath, G. et al. Self-assembled subnanolayers as interfacial adhesion enhancers and diffusion barriers for integrated circuits. Appl. Phys. Lett. 83, 383–385 (2003).10.1063/1.1591232 ↗
35. Hsu, B.-F. et al. Functionalizing self-assembled monolayers to reduce interface scattering in ruthenium/dielectric for next-generation microelectronic interconnects. Appl. Surf. Sci. 645, 158870 (2024).10.1016/j.apsusc.2023.158870 ↗
36. Dutta, J., Richmond, M. G. & Bhattacharya, S. Cycloruthenation of N-(Naphthyl)salicylaldimine and related ligands: utilization of the Ru–C bond in catalytic transfer hydrogenation. Eur. J. Inorg. Chem. 2014, 4600–4610 (2014).10.1002/ejic.201402236 ↗
37. Bernhard, P. et al. Ligand dehydrogenation in ruthenium−amine complexes: reactivity of 1,2-ethanediamine and 1,1,1-tris(aminomethyl)ethane. Inorg. Chem. 36, 2804–2815 (1997).10.1021/ic961021q ↗
38. Sangeetha, S. & Murali, M. Cytotoxic ruthenium(II) complexes containing a dangling pyridine: selectivity for diseased cells mediated by pH-dependent DNA binding. Inorg. Chem. 61, 2864–2882 (2022).10.1021/acs.inorgchem.1c03399 ↗
39. Majumdar, A. et al. Chemical composition and bond structure of carbon-nitride films deposited by CH4/N2 dielectric barrier discharge. Surf. Coat. Technol. 201, 6437–6444 (2007).10.1016/j.surfcoat.2006.12.011 ↗
40. Majumdar, A., Das, G., Basvani, K. R., Heinicke, J. & Hippler, R. Role of nitrogen in the formation of HC−N films by CH4/N2 barrier discharge plasma: aliphatic tendency. J. Phys. Chem. B 113, 15734–15741 (2009).10.1021/jp906654m ↗
41. Smith, E. A. & Chen, W. How to prevent the loss of surface functionality derived from aminosilanes. Langmuir 24, 12405–12409 (2008).10.1021/la802234x ↗
42. Zhu, M., Lerum, M. Z. & Chen, W. How to prepare reproducible, homogeneous, and hydrolytically stable aminosilane-derived layers on silica. Langmuir 28, 416–423 (2012).10.1021/la203638g ↗
43. Huayao, C. et al. Highly efficient alginate sodium encapsulated chlorpyrifos/copper(II) schiff base mesoporous silica sustained release system with pH and ion response for pesticide delivery. RSC Adv. 6, 114714–114721 (2016).10.1039/C6RA23836J ↗
44. Vig, J. R. UV/Ozone cleaning of surfaces. J. Vac. Sci. Technol. A 3, 1027–1034 (1985).10.1116/1.573115 ↗
45. Mathieson, I. & Bradley, R. H. Improved adhesion to polymers by UV/ozone surface oxidation. Int. J. Adhes. Adhes. 16, 29–31 (1996).10.1016/0143-7496(96)88482-X ↗
46. Fan, S. et al. A novel Schiff base-containing branched polysiloxane as a self-crosslinking flame retardant for PA6 with low heat release and excellent anti-dripping performance. Compos. Part B Eng. 183, 107684 (2020).10.1016/j.compositesb.2019.107684 ↗
47. Schiff, H. Mittheilungen Aus Dem Universitätslaboratorium in Pisa: Eine Neue Reihe Organischer Basen. Justus Liebigs Ann. Chem. 131, 118–119 (1864).10.1002/jlac.18641310113 ↗
48. Ghorbanloo, M., Monfared, H. H. & Janiak, C. The catalytic function of a silica gel-immobilized Mn(II)-hydrazide complex for alkene epoxidation with H2O2. J. Mol. Catal. Chem. 345, 12–20 (2011).10.1016/j.molcata.2011.05.014 ↗
49. Remaud, G., Debon, A. A., Martin, Y., Martin, G. G. & Martin, G. J. Authentication of bitter almond oil and cinnamon oil: application of the SNIF-NMR method to benzaldehyde. J. Agric. Food Chem. 45, 4042–4048 (1997).10.1021/jf970143d ↗
50. Seitz, O. et al. Control and stability of self-assembled monolayers under biosensing conditions. J. Mater. Chem. 21, 4384 (2011).10.1039/c1jm10132c ↗
51. Rozlosnik, N., Gerstenberg, M. C. & Larsen, N. B. Effect of solvents and concentration on the formation of a self-assembled monolayer of octadecylsiloxane on silicon (001). Langmuir 19, 1182–1188 (2003).10.1021/la025906s ↗
52. Spinke, J. et al. Molecular recognition at self-assembled monolayers: optimization of surface functionalization. J. Chem. Phys. 99, 7012–7019 (1993).10.1063/1.465447 ↗
53. Gong, Y., Wang, M. C. P., Zhang, X., Ng, H. W. & Gates, B. D. Optimizing the quality of monoreactive perfluoroalkylsilane-based self-assembled monolayers. Langmuir 28, 11790–11801 (2012).10.1021/la301742s ↗
54. Fryxell, G. E. et al. Nucleophilic displacements in mixed self-assembled monolayers. Langmuir 12, 5064–5075 (1996).10.1021/la9506842 ↗
55. Bunker, B. C. et al. The impact of solution agglomeration on the deposition of self-assembled monolayers. Langmuir 16, 7742–7751 (2000).10.1021/la000502q ↗
56. Angst, D. L. & Simmons, G. W. Moisture absorption characteristics of organosiloxane self-assembled monolayers. Langmuir 7, 2236–2242 (1991).10.1021/la00058a043 ↗
57. Singh, M., Kaur, N. & Comini, E. The role of self-assembled monolayers in electronic devices. J. Mater. Chem. C 8, 3938–3955 (2020).10.1039/D0TC00388C ↗
58. Howarter, J. A. & Youngblood, J. P. Optimization of silica silanization by 3-aminopropyltriethoxysilane. Langmuir 22, 11142–11147 (2006).10.1021/la061240g ↗
59. Osterholtz, F. D. & Pohl, E. R. Kinetics of the hydrolysis and condensation of organofunctional alkoxysilanes: a review. J. Adhes. Sci. Technol. https://doi.org/10.1163/156856192X00106 (1992).10.1163/156856192X00106 ↗
60. Dufil, Y., Gadenne, V., Carrière, P., Nunzi, J.-M. & Patrone, L. Growth and organization of (3-trimethoxysilylpropyl) diethylenetriamine within reactive amino-terminated self-assembled monolayer on silica. Appl. Surf. Sci. 508, 145210 (2020).10.1016/j.apsusc.2019.145210 ↗
61. Tian, R. et al. Infrared characterization of interfacial Si−O bond formation on silanized flat SiO2/Si surfaces. Langmuir 26, 4563–4566 (2010).10.1021/la904597c ↗
62. Wasserman, S. R., Tao, Y. T. & Whitesides, G. M. Structure and reactivity of alkylsiloxane monolayers formed by reaction of alkyltrichlorosilanes on silicon substrates. Langmuir 5, 1074–1087 (1989).10.1021/la00088a035 ↗
63. Tillman, N., Ulman, A., Schildkraut, J. S. & Penner, T. L. Incorporation of phenoxy groups in self-assembled monolayers of trichlorosilane derivatives. effects on film thickness, wettability, and molecular orientation. J. Am. Chem. Soc. 110, 6136–6144 (1988).10.1021/ja00226a031 ↗
64. Aswal, D. K., Lenfant, S., Guerin, D., Yakhmi, J. V. & Vuillaume, D. Self assembled monolayers on silicon for molecular electronics. Anal. Chim. Acta 568, 84–108 (2006).10.1016/j.aca.2005.10.027 ↗
65. Xu, S., Miller, S., Laibinis, P. E. & Liu, G. Fabrication of nanometer scale patterns within self-assembled monolayers by nanografting. Langmuir 15, 7244–7251 (1999).10.1021/la9906727 ↗
66. Kibria, M., Zhang, F., Lee, T., Kim, M. & Howlader, M. Comprehensive investigation of sequential plasma activated Si/Si bonded interfaces for nano-integration on the wafer scale. Nanotechnology 21, 134011 (2010).10.1088/0957-4484/21/13/134011 ↗
67. Bryk, P. et al. What is the value of water contact angle on silicon?. Materials 13, 1554 (2020).10.3390/ma13071554 ↗
68. Kulisch, W. et al. Investigation of the UV/O3 treatment of ultrananocrystalline diamond films. Surf. Interface Anal. 42, 1152–1155 (2010).10.1002/sia.3264 ↗
69. Pyo, C. E. & Chang, J. H. Hydrophobic mesoporous silica particles modified with nonfluorinated alkyl Silanes. ACS Omega 6, 16100–16109 (2021).10.1021/acsomega.1c01981 ↗
70. Jung, M.-H. & Choi, H.-S. Characterization of octadecyltrichlorosilane self-assembled monolayers on silicon (100) surface. Korean J. Chem. Eng. 26, 1778–1784 (2009).10.1007/s11814-009-0249-9 ↗
71. Wei, D. et al. J. Photocatalytic hydroxylation of benzene to phenol over organosilane-functionalized FeVO 4 nanorods. Catal. Sci. Technol. 11, 5931–5937 (2021).10.1039/D1CY00890K ↗
72. Sahu, B. S., Kapoor, A., Srivastava, P., Agnihotri, O. P. & Shivaprasad, S. M. Study of thermally grown and photo-CVD deposited silicon oxide–silicon nitride stack layers. Semicond. Sci. Technol. 18, 670–675 (2003).10.1088/0268-1242/18/7/312 ↗
73. Della Ciana, M. et al. Native silicon oxide properties determined by doping. Langmuir 39, 12430–12451 (2023).10.1021/acs.langmuir.3c01652 ↗
74. Boudaden, J. et al. Towards coloured glazed thermal solar collectors. Sol. Energy Mater. Sol. Cells 84, 225–239 (2004).10.1016/j.solmat.2004.02.042 ↗
75. Bashouti, M. Y., Ristein, J., Haick, H., Christiansen, S. A non-oxidative approach towards hybrid silicon nanowire- based solar cell heterojunctions. https://doi.org/10.2478/hyma-2013-0002 (2014).10.2478/hyma-2013-0002 ↗
76. Dietrich, P. M. et al. Synchrotron-radiation XPS analysis of ultra-thin silane films: specifying the organic silicon. Appl. Surf. Sci. 363, 406–411 (2016).10.1016/j.apsusc.2015.12.052 ↗
77. Zhang, L., Kuramoto, N. & Kurokawa, A. XPS analysis of a 28Si-enriched sphere for realization of the kilogram. IEEE Trans. Instrum. Meas. 70, 1–5 (2021).10.1109/TIM.2021.3127641 ↗
78. Cui, N.-Y., Liu, C. & Yang, W. XPS and AFM characterization of the self-assembled molecular monolayers of a 3-aminopropyltrimethoxysilane on silicon surface, and effects of substrate pretreatment by UV-irradiation. Surf. Interface Anal. 43, 1082–1088 (2011).10.1002/sia.3698 ↗
79. Lee, J. K., Chi, Y. S. & Choi, I. S. Reactivity of acetylenyl-terminated self-assembled monolayers on gold: triazole formation. Langmuir 20, 3844–3847 (2004).10.1021/la049748b ↗
80. Liu, H. & Hamers, R. J. An X-ray photoelectron spectroscopy study of the bonding of unsaturated organic molecules to the Si(001) surface. Surf. Sci. 416, 354–362 (1998).10.1016/S0039-6028(98)00507-X ↗
81. Contarini, S., Howlett, S. P., Rizzo, C. & De Angelis, B. A. XPS study on the dispersion of carbon additives in silicon carbide powders. Appl. Surf. Sci. 51, 177–183 (1991).10.1016/0169-4332(91)90400-E ↗
82. Gheorghe, N. G., Lungu, G. A., Costescu, R. M. & Teodorescu, C. M. Significantly different contamination of atomically clean Si(001) when investigated by XPS and AES. Phys. Status Solidi B 248, 1919–1924 (2011).10.1002/pssb.201147220 ↗
83. Riedo, E. et al. Structural properties and surface morphology of laser-deposited amorphous carbon and carbon nitride films. Surf. Coat. Technol. 125, 124–128 (2000).10.1016/S0257-8972(99)00591-5 ↗
84. Scharf, T. W., Ott, R. D., Yang, D. & Barnard, J. A. Structural and tribological characterization of protective amorphous diamond-like carbon and amorphous CNx overcoats for next generation hard disks. J. Appl. Phys. 85, 3142–3154 (1999).10.1063/1.369654 ↗
85. Fadeev, A. Y. & McCarthy, T. J. Self-assembly is not the only reaction possible between alkyltrichlorosilanes and surfaces: monomolecular and oligomeric covalently attached layers of dichloro- and trichloroalkylsilanes on silicon. Langmuir 16, 7268–7274 (2000).10.1021/la000471z ↗
86. Sha, X. et al. Quartz crystal microbalance (QCM): useful for developing procedures for immobilization of proteins on solid surfaces. Anal. Chem. 84, 10298–10305 (2012).10.1021/ac302275r ↗
87. Henss, A. et al. High resolution imaging and 3D analysis of Ag nanoparticles in cells with ToF-SIMS and delayed extraction. Biointerphases 13, 03B410 (2018).10.1116/1.5015957 ↗
88. Nygren, H., Hagenhoff, B., Malmberg, P., Nilsson, M. & Richter, K. Bioimaging TOF-SIMS: high resolution 3D imaging of single cells. Microsc. Res. Tech. 70, 969–974 (2007).10.1002/jemt.20502 ↗
89. Arunagiri, T. N., Zhang, Y., Chyan, O., Kim, M. J. & Hurd, T. Q. Interfacial diffusion studies of Cu ∕ (5 Nm Ru) ∕ Si structures: physical vapor deposited vs electrochemically deposited Cu. J. Electrochem. Soc. 152, G808 (2005).10.1149/1.2039939 ↗
90. Hale, L. V. A. et al. The mechanism of acceptorless amine double dehydrogenation by N,N,N-amide ruthenium(II) hydrides: a combined experimental and computational study. ACS Catal. 6, 4799–4813 (2016).10.1021/acscatal.6b01465 ↗
91. Banerjee, K., Souri, S. J., Kapur, P. & Saraswat, K. C. 3-D ICs: a novel chip design for improving deep-submicrometer interconnect performance and systems-on-chip integration. Proc. IEEE 89, 602–633 (2001).10.1109/5.929647 ↗
92. Porter, M. et al. Reliability considerations for implantable medical ICs. In Proc. 2008 IEEE International Reliability Physics Symposium 2008, 516–523. https://doi.org/10.1109/RELPHY.2008.4558939.10.1109/RELPHY.2008.4558939 ↗
93. Petrone, G., Spagnuolo, G., Teodorescu, R., Veerachary, M. & Vitelli, M. Reliability issues in photovoltaic power processing systems. IEEE Trans. Ind. Electron. 55, 2569–2580 (2008).10.1109/TIE.2008.924016 ↗
94. Latt, K. M., Lee, Y. K., Osipowicz, T. & Park, H. S. Interfacial reactions and failure mechanism of Cu/Ta/SiO2/Si multilayer structure in thermal annealing. Mater. Sci. Eng. B 94, 111–120 (2002).10.1016/S0921-5107(02)00093-4 ↗
95. Holloway, K. et al. Tantalum as a diffusion barrier between copper and silicon: failure mechanism and effect of nitrogen additions. J. Appl. Phys. 71, 5433–5444 (1992).10.1063/1.350566 ↗
96. Khanna, V. K. Adhesion–delamination phenomena at the surfaces and interfaces in microelectronics and MEMS structures and packaged devices. J. Phys. Appl. Phys. 44, 034004 (2010).10.1088/0022-3727/44/3/034004 ↗
97. Balakumar, S., Wong, G., Fo Tsang, C., Hara, T. & Yoo, W. J. Enhancement of adhesion strength of Cu layer on single and multi-layer dielectric film stack in Cu/Low k multi-level interconnects. Microelectron. Eng. 75, 183–193 (2004).10.1016/j.mee.2004.05.003 ↗
98. Schmitz, J. Low Temperature thin films for next-generation microelectronics (invited). Surf. Coat. Technol. 343, 83–88 (2018).10.1016/j.surfcoat.2017.11.013 ↗
99. Luce, F. P. et al. Methodology for thermal budget reduction of SPER down to 450 °C for 3D sequential integration. Nucl. Instrum. Methods Phys. Res. Sect. B 370, 14–18 (2016).10.1016/j.nimb.2015.12.021 ↗
100. Nagy, G. & Walker, A. V. Dynamics of the interaction of vapor-deposited copper with alkanethiolate monolayers: bond insertion, complexation, and penetration pathways. J. Phys. Chem. B 110, 12543–12554 (2006).10.1021/jp055040+ ↗