Indium tin oxide as a semiconductor material in efficient p-type dye-sensitized solar cells
Source abstract
Abstract
Indium tin oxide (ITO) is a well-known n-type degenerate semiconductor with a wide variety of electronic and optoelectronic applications. Herein ITO is utilized as a photocathode material in p-type dye-sensitized solar cells in place of the commonly applied and highly colored nickel oxide (NiO) semiconductor. The application of mesoporous ITO photocathodes, [Fe(acac)3]0/− as a redox mediator and a new organic dye afforded an impressive energy conversion efficiency of 1.96±0.12%. Comparative transient absorption spectroscopic studies indicated that the recombination rate at the ITO–electrolyte interface is two orders of magnitude faster than that of NiO. Analysis of the operation mechanism of the ITO-based devices with ultraviolet photon spectroscopy and photoelectron spectroscopy in air showed that ITO exhibits a significant local density of states arising below −4.8 eV, which enables electron transfer to occur from the ITO to the excited dye, thus giving rise to the sustained photocathodic current. Switching the usual direction of electron transport in see-through semiconductors may bring efficiency gains to organic photovoltaics. In n-type dye-sensitized solar cells, transparent indium tin oxide (ITO) is widely used to accept electrons from light-stimulated molecules. By exploiting the seldom-studied electron-donating properties of ITO, Udo Bach from Monash University and co-workers have produced an efficient, p-type organic solar cell. They sintered ITO nanoparticles into thin films and coated them with an aromatic donor-bridge-acceptor dye compound and an iron-based electrolyte. By tweaking the length of a thiophene-based bridge in the dye and applying an appropriate driving voltage, the researchers produced a p-type device that harvested sunlight with an efficiency close to the best n-type dye-sensitized unit. Solar cells where both the anodes and cathodes are photoactive could make low-cost organic devices even more attractive. Indium tin oxide (ITO) is a well-known n-type degenerate semiconductor. Herein, mesoporous ITO is utilized as a photocathode material for p-type dye-sensitized solar cells in place of the commonly applied p-type semiconductors, such as nickel oxide. In conjunction with [Fe(acac)3]0/− as redox mediator and a new sensitizer, an impressive energy conversion efficiency of 1.96±0.12% was achieved. Photoelectron spectroscopy in air revealed that ITO exhibits a significant local density of states arising below −4.8 eV, which enables electron transfer to occur from ITO to the excited dye, giving rise to the sustained photocathodic current.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: TiO2 Photocatalysis and Solar Cells · Advanced Photocatalysis Techniques · Copper-based nanomaterials and applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (30)
Show source-provided references
1. Sun, X., Shi, Y., Ji, H., Li, X., Cai, S. & Zheng, C. Nanocasting synthesis of ordered mesoporous indium tin oxide (ITO) materials with controllable particle size and high thermal stability. J. Alloys Compd. 545, 5–11 (2012).10.1016/j.jallcom.2012.08.003 ↗
2. Slocombe, D., Porch, A., Pepper, M. & Edwards, P. P. The Mott transition and optimal performance of transparent conducting oxides in thin-film solar cells. Energy Environ. Sci. 5, 5387–5391 (2012).10.1039/C1EE02585F ↗
3. Ellmer, K. Past achievements and future challenges in the development of optically transparent electrodes. Nat. Photonics 6, 809–817 (2012).10.1038/nphoton.2012.282 ↗
4. Kim, H., Gilmore, C. M., Piqué, A., Horwitz, J. S., Mattoussi, H., Murata, H., Kafafi, J. H. & Chrisey, D. B. Electrical, optical, and structural properties of indium-tin-oxide thin films for organic light-emitting devices. J. Appl. Phys. 86, 6451–6461 (1999).10.1063/1.371708 ↗
5. Hamberg, I., Granqvist, C. G., Berggren, K. F., Sernelius, B. E. & Engström, L. Band-gap widening in heavily Sn-doped In2O3 . Phys. Rev. B 30, 3240–3249 (1984).10.1103/PhysRevB.30.3240 ↗
6. Zhang, Q., Dandeneau, C. S., Zhou, X. & Cao, G. ZnO nanostructures for dye-sensitized solar cells. Adv. Mater. 21, 4087–4108 (2009).10.1002/adma.200803827 ↗
7. Sun, Z., He, J., Kumbhar, A. & Fang, J. Nonaqueous synthesis and photoluminescence of ITO nanoparticles. Langmuir 26, 4246–4250 (2010).10.1021/la903316b ↗
8. Lee, S., Noh, J. H., Bae, S.-T., Cho, I.-S., Kim, J. Y., Shin, H., Lee, J.-K., Jung, H. S. & Hong, K. S. Indium-tin-oxide-based transparent conducting layers for highly efficient photovoltaic devices. J. Phys. Chem. C 113, 7443–7447 (2009).10.1021/jp809011a ↗
9. Hartnagel, H. L., Dawar, A., Jain, A. & Jagadish, C. Semiconducting Transparent Thin Films (Institute of Physics Publishing, Bristol, UK, Philadelphia, PA, USA, 1995).
10. Lee, M.-K. & Fan, C.-H. Electrochromic characterization of nickel oxide films grown on ITO/glass by liquid phase deposition. J. Electrochem. Soc. 156, D395–D399 (2009).10.1149/1.3187911 ↗
11. Tsai, T.-H. & Wu, Y.-F. Organic acid mixing to improve ITO film etching in flat panel display manufacturing. J. Electrochem. Soc. 153, C86–C90 (2006).10.1149/1.2135221 ↗
12. Wang, H.-W., Ting, C.-F., Hung, M.-K., Chiou, C.-H., Liu, Y.-L., Liu, Z., Ratinac, K. R. & Ringer, S. P. Three-dimensional electrodes for dye-sensitized solar cells: synthesis of indium-tin-oxide nanowire arrays and ITO/TiO2 core-shell nanowire arrays by electrophoretic deposition. Nanotechnology 20, 055601 (2009).10.1088/0957-4484/20/5/055601 ↗
13. Mbarek, H., Saadoun, M. & Bessaïs, B. Screen-printed Tin-doped indium oxide (ITO) films for NH3 gas sensing. Mater. Sci. Eng. C 26, 500–504 (2006).10.1016/j.msec.2005.10.037 ↗
14. Patel, N. G., Patel, P. D. & Vaishnav, V. S. Indium tin oxide (ITO) thin film gas sensor for detection of methanol at room temperature. Sens. Actuators, B 96, 180–189 (2003).10.1016/S0925-4005(03)00524-0 ↗
15. Zeng, K., Zhu, F., Hu, J., Shen, L., Zhang, K. & Gong, H. Investigation of mechanical properties of transparent conducting oxide thin films. Thin Solid Films 443, 60–65 (2003).10.1016/S0040-6090(03)00915-5 ↗
16. Sberveglieri, G., Groppelli, S. & Coccoli, G. Radio frequency magnetron sputtering growth and characterization of indium-tin oxide (ITO) thin films for NO2 gas sensors. Sens. Actuators 15, 235–242 (1988).10.1016/0250-6874(88)87013-6 ↗
17. Garvey, T. R., Farnum, B. H. & Lopez, R. Pulsed laser deposited porous nano-carpets of indium tin oxide and their use as charge collectors in core-shell structures for dye sensitized solar cells. Nanoscale 7, 2400–2408 (2015).10.1039/C4NR05793G ↗
18. Kato, M., Cardona, T., Rutherford, A. W. & Reisner, E. Photoelectrochemical water oxidation with photosystem II integrated in a mesoporous indium-tin oxide electrode. J. Am. Chem. Soc. 134, 8332–8335 (2012).10.1021/ja301488d ↗
19. Alibabaei, L., Farnum, B. H., Kalanyan, B., Brennaman, M. K., Losego, M. D., Parsons, G. N. & Meyer, T. J. Atomic layer deposition of TiO2 on mesoporous nanoITO: conductive core-shell photoanodes for dye-sensitized solar cells. Nano Lett. 14, 3255–3261 (2014).10.1021/nl5006433 ↗
20. Alibabaei, L., Brennaman, M. K., Norris, M. R., Kalanyan, B., Song, W., Losego, M. D., Concepcion, J. J., Binstead, R. A., Parsons, G. N. & Meyer, T. J. Solar water splitting in a molecular photoelectrochemical cell. Proc. Natl. Acad. Sci. USA 110, 20008–20013 (2013).10.1073/pnas.1319628110 ↗
21. Huang, Z., He, M., Yu, M., Click, K., Beauchamp, D. & Wu, Y. Dye-controlled interfacial electron transfer for high-current indium tin oxide photocathodes. Angew. Chem. Int. Ed. 54, 6857–6861 (2015).10.1002/anie.201500274 ↗
22. Furmansky, Y., Sasson, H., Liddell, P., Gust, D., Ashkenasy, N. & Visoly-Fisher, I. Porphyrins as ITO photosensitizers: substituents control photo-induced electron transfer direction. J. Mater. Chem. 22, 20334–20341 (2012).10.1039/c2jm34118b ↗
23. Mathew, S., Yella, A., Gao, P., Humphry-Baker, R., Curchod, B. F. E., Ashari-Astani, N., Tavernelli, I., Rothlisberger, U., Nazeeruddin, M. K. & Grätzel, M. Dye-sensitized solar cells with 13% efficiency achieved through the molecular engineering of porphyrin sensitizers. Nat. Chem. 6, 242–247 (2014).10.1038/nchem.1861 ↗
24. Perera, I. R., Daeneke, T., Makuta, S., Yu, Z., Tachibana, Y., Mishra, A., Bäuerle, P., Ohlin, C. A., Bach, U. & Spiccia, L. Application of the tris(acetylacetonato)iron(III)/(II) redox couple in p-type dye-sensitized solar cells. Angew. Chem. Int. Ed. 54, 3758–3762 (2015).10.1002/anie.201409877 ↗
25. Nattestad, A., Mozer, A. J., Fischer, M. K. R., Cheng, Y.-B., Mishra, A., Bäuerle, P. & Bach, U. Highly efficient photocathodes for dye-sensitized tandem solar cells. Nat. Mat. 9, 31–35 (2010).10.1038/nmat2588 ↗
26. Powar, S., Daeneke, T., Ma, M. T., Fu, D., Duffy, N. W., Götz, G., Weidelener, M., Mishra, A., Bäuerle, P., Spiccia, L. & Bach, U. Highly efficient p-type dye-sensitized solar cells based on tris(1,2-diaminoethane)cobalt(II)/(III) electrolytes. Angew. Chem. Int. Ed. 52, 602–605 (2013).10.1002/anie.201206219 ↗
27. Aouaj, M. A., Diaz, R., Belayachi, A., Rueda, F. & Abd-Lefdil, M. Comparative study of ITO and FTO thin films grown by spray pyrolysis. Mater. Res. Bull. 44, 1458–1461 (2009).10.1016/j.materresbull.2009.02.019 ↗
28. Daeneke, T., Yu, Z., Lee, G. P., Fu, D., Duffy, N. W., Makuta, S., Tachibana, Y., Spiccia, L., Mishra, A., Bäuerle, P. & Makuta, S. Dominating energy losses in NiO p-type dye-sensitized solar cells. Adv. Energy Mater. 5, 1401387 (2015).10.1002/aenm.201401387 ↗
29. Daeneke, T., Mozer, A. J., Uemura, Y., Makuta, S., Fekete, M., Tachibana, Y., Koumura, N., Bach, U. & Spiccia, L. Dye regeneration kinetics in dye-sensitized solar cells. J. Am. Chem. Soc. 134, 16925–16928 (2012).10.1021/ja3054578 ↗
30. Mori, S. & Asano, A. Light intensity independent electron transport and slow charge recombination in dye-sensitized In2O3 solar cells: in contrast to the case of TiO2 . J. Phys. Chem. C 114, 13113–13117 (2010).10.1021/jp1019203 ↗