Influence of High-κ Dielectrics Integration on ALD-Based MoS2 Field-Effect Transistor Performance

Reyhaneh Mahlouji, Yue Zhang, Marcel A. Verheijen, Saurabh Karwal, Jan P. Hofmann, Wilhelmus M. M. Kessels, Ageeth A. Bol

ACS Applied Nano Materials· Volume 7· Issue 16

Abstract

High Resolution Image Download MS PowerPoint Slide The integration of high-κ dielectrics on MoS 2 field-effect transistors (FETs) is essential for the realization of MoS 2 in ultrascaled nanoelectronic devices and circuits. Most studies covering this topic are based on exfoliated MoS 2 flakes or chemical vapor deposition (CVD) grown MoS 2 films, whereas other techniques, such as atomic layer deposition (ALD), are also gaining attention for the growth of MoS 2 in recent years. In this work, we grow large-area MoS 2 by means of plasma-enhanced (PE-)ALD and evaluate the influence of high-κ dielectrics on the properties of ALD-based MoS 2 FETs through electrical characterization combined with surface-chemical and high-resolution scanning transmission electron microscopy (HR-STEM) analyses. We grow HfO x, AlO x, or both by means of PE-ALD or thermal ALD on our fabricated devices and show that, in addition to the dielectric constant, three other major parameters related to the processing of the dielectrics can simultaneously affect the MoS 2 FET electrical characteristics and govern its doping. These parameters are the stoichiometry of the dielectric, its carbon impurity content, and the degree to which the MoS 2 surface oxidizes upon the dielectric growth. When grown at 100 °C, our HfO x films are oxygen-vacant whereas our AlO x films are oxygen-rich. In addition, carbon impurities are incorporated into the dielectrics at low deposition temperatures, being one of the likely causes of the MoS 2 FET overall n -type performance in all of the studied cases. Our investigations also reveal that PE-ALD of HfO x or AlO x oxidizes the MoS 2 surface, whereas thermal ALD AlO x leaves MoS 2 almost intact. In this respect, if thermal ALD AlO x of proper thickness is grown between MoS 2 and HfO x, it can reduce the degree to which the MoS 2 surface oxidizes by HfO x and meanwhile improve the total dielectric constant, altogether leading to the most optimal electrical performance in ALD-based MoS 2 FETs.
Source: openalex_inverted_index · Quality: baseline

Research context

OpenAlex topics: Nanowire Synthesis and Applications · Semiconductor materials and devices · Advanced Memory and Neural Computing

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Department of Applied Physics, Eindhoven University of Technology, P.O. Box 513, 5600 MB Eindhoven, The Netherlands

Laboratory of Inorganic Materials and Catalysis, Department of Chemical Engineering and Chemistry, Eindhoven University of Technology, P.O. Box 513, 5600 MB Eindhoven, The Netherlands

Eurofins Materials Science, High Tech Campus 11, 5656 AE Eindhoven, The Netherlands

Netherlands Organization for Applied Scientific Research (TNO), 2628 CK Delft, The Netherlands

Surface Science Laboratory, Department of Materials and Earth Sciences, Technical University of Darmstadt, Otto-Berndt-Strasse 3, 64287 Darmstadt, Germany

Department of Chemistry, University of Michigan, 930 N. University Ave., Ann Arbor, Michigan 48109, United States

Funding

H2020 European Research Council

References (70)

Show source-provided references
1. 10.1109/TED.2012.221828310.1109/TED.2012.2218283 ↗
2. 10.1038/s41586-019-1573-910.1038/s41586-019-1573-9 ↗
3. 10.1038/s41699-020-00181-110.1038/s41699-020-00181-1 ↗
4. 10.1109/TED.2015.244303910.1109/TED.2015.2443039 ↗
5. Asselberghs I. · 2021 · 40.2.1
6. 10.1038/s41598-021-85968-y10.1038/s41598-021-85968-y ↗
7. 10.1021/acsnano.0c0907810.1021/acsnano.0c09078 ↗
8. 10.1021/acs.nanolett.6b0271310.1021/acs.nanolett.6b02713 ↗
9. 10.1038/s41586-021-03472-910.1038/s41586-021-03472-9 ↗
10. 10.1038/s41928-019-0334-y10.1038/s41928-019-0334-y ↗
11. 10.1021/acsaelm.8b0005910.1021/acsaelm.8b00059 ↗
12. 10.1038/nnano.2010.27910.1038/nnano.2010.279 ↗
13. 10.1021/nn506567r10.1021/nn506567r ↗
14. 10.1109/LED.2017.276860210.1109/LED.2017.2768602 ↗
15. 10.1038/s41467-020-19053-910.1038/s41467-020-19053-9 ↗
16. 10.1038/ncomms1494810.1038/ncomms14948 ↗
17. 10.1051/epjap:200420610.1051/epjap:2004206 ↗
18. 10.1149/1.220956810.1149/1.2209568 ↗
19. 10.1021/cr900056b10.1021/cr900056b ↗
20. 10.1063/1.370359510.1063/1.3703595 ↗
21. 10.1021/nn404775u10.1021/nn404775u ↗
22. 10.1109/LED.2012.218452010.1109/LED.2012.2184520 ↗
23. 10.1063/1.486914910.1063/1.4869149 ↗
24. 10.1021/am303261c10.1021/am303261c ↗
25. 10.1063/1.490563410.1063/1.4905634 ↗
26. 10.1063/1.502710210.1063/1.5027102 ↗
27. 10.1021/acsami.7b0053810.1021/acsami.7b00538 ↗
28. Chang W. H. · 2019 · 1
29. 10.1088/1361-6528/aac85310.1088/1361-6528/aac853 ↗
30. 10.1038/s41467-020-16640-810.1038/s41467-020-16640-8 ↗
31. 10.1063/1.496460610.1063/1.4964606 ↗
32. 10.1021/acsanm.9b0050510.1021/acsanm.9b00505 ↗
33. 10.1103/PhysRevLett.98.13680510.1103/PhysRevLett.98.136805 ↗
34. 10.1103/PhysRevX.4.01104310.1103/PhysRevX.4.011043 ↗
35. 10.1103/PhysRevB.85.11531710.1103/PhysRevB.85.115317 ↗
36. Ghatak, S.; Mukherjee, S.; Jain, M.; Sarma, D. D.; Ghosh, A. Microscopic Origin of Charged Impurity Scattering and Flicker Noise in MoS2 Field-Effect Transistors, 2014; pp 1–29.10.1063/1.4895955 ↗
37. 10.1116/1.497422010.1116/1.4974220 ↗
38. 10.1063/1.480392010.1063/1.4803920 ↗
39. 10.1109/TDMR.2013.228221610.1109/TDMR.2013.2282216 ↗
40. 10.1063/1.339977610.1063/1.3399776 ↗
41. 10.1021/acs.nanolett.5b0255910.1021/acs.nanolett.5b02559 ↗
42. 10.1002/adma.20160196610.1002/adma.201601966 ↗
43. 10.1109/TED.2018.286677210.1109/TED.2018.2866772 ↗
44. 10.1088/2053-1583/2/4/04500910.1088/2053-1583/2/4/045009 ↗
45. 10.1021/acs.nanolett.5b0031410.1021/acs.nanolett.5b00314 ↗
46. 10.1021/acs.chemmater.8b0117110.1021/acs.chemmater.8b01171 ↗
47. 10.1021/acsami.9b1155010.1021/acsami.9b11550 ↗
48. 10.1021/acsnano.7b0410010.1021/acsnano.7b04100 ↗
49. 10.1021/nn405194e10.1021/nn405194e ↗
50. 10.1002/adma.20170303110.1002/adma.201703031 ↗
51. 10.1039/C8NR02339E10.1039/C8NR02339E ↗
52. 10.1021/nl400747910.1021/nl4007479 ↗
53. 10.1063/1.496740610.1063/1.4967406 ↗
54. 10.1021/acsnano.9b0746710.1021/acsnano.9b07467 ↗
55. 10.1088/1361-6528/ab759310.1088/1361-6528/ab7593 ↗
56. 10.1116/1.493016110.1116/1.4930161 ↗
57. 10.1021/acsaelm.1c0037910.1021/acsaelm.1c00379 ↗
58. 10.1116/1.497221010.1116/1.4972210 ↗
59. 10.1149/1.273762910.1149/1.2737629 ↗
60. 10.1021/acsami.6b1472210.1021/acsami.6b14722 ↗
61. 10.1021/nn503988x10.1021/nn503988x ↗
62. 10.1021/nl404350510.1021/nl4043505 ↗
63. 10.1116/1.360997410.1116/1.3609974 ↗
64. 10.1149/1.351743010.1149/1.3517430 ↗
65. Frohlich, K.; Micusik, M.; Dobrocka, E.; Siffalovic, P.; Gucmann, F.; Fedor, J. Properties of Al2O3 Thin Films Grown by Atomic Layer Deposition. In The Ninth International Conference on Advanced Semiconductor Devices and Mircosystems; IEEE: 2012; pp 171–174. 10.1109/ASDAM.2012.6418575.10.1109/ASDAM.2012.6418575 ↗
66. 10.1063/1.180796810.1063/1.1807968 ↗
67. 10.1063/1.369809510.1063/1.3698095 ↗
68. 10.1063/1.347377310.1063/1.3473773 ↗
69. 10.1143/JJAP.45.91910.1143/JJAP.45.919 ↗
70. 10.1149/2.006202ssl10.1149/2.006202ssl ↗