Enhanced Energy Storage Performance by A–B Site Ambipolar Co-Doping in Antiferroelectrics

Dirui Wu, Wen Dong, Ying Yang, Long Chen, Wenrong Xiao, Chao Zhang, Kailun Zou, Wenjing Zhou, Wei Luo, Guangzu Zhang, Qiuyun Fu, Shenglin Jiang

Publisher page

Abstract

Antiferroelectric materials are promising to be used for power capacitive devices. To improve the energy storage performance, solid-solution and defect engineering are widely used to suppress the long-range order by introducing local heterogeneities. However, both methods generally deteriorate either the maximum polarization or breakdown electric field due to damaged intrinsic polarization or increased leakage. Here, we show that forming defect-dipole clusters by A–B site acceptor–donor co-doping in antiferroelectrics can comprehensively enhance the energy storage performance. We took the La–Mn co-doped (Pb 0.9 Ba 0.04 La 0.04 )(Zr 0.65 Sn 0.3 Ti 0.05 )O 3 (PBLZST) as an example. For co-doping with unequal amounts, high dielectric loss, impurity phase, and decreased polarization were observed. By contrast, La and Mn in an equal amount of co-doping can significantly improve the overall energy storage performance. An over 48% increasement in both the maximum polarization (62.7 μC/cm 2 ) and breakdown electric field (242.6 kV/cm) was obtained in 1 mol % La and 1 mol % Mn equally co-doped PBLZST, followed by a nearly two-time enhancement in W rec (6.52 J/cm 3 ) compared with that of the pure matrix. Moreover, a high energy storage efficiency of 86.3% with an enhanced temperature stability over a wide temperature range can be achieved. The defect-dipole clusters associated with charge-compensated co-doping are suggested to contribute to an enhanced dielectric permittivity, linear polarization behavior, and maximum polarization strength compared with that of the unequal co-doping cases. The defect-dipole clusters are suggested to couple with the host, leading to a high energy storage performance. The proposed strategy is believed to be applicable to modify the energy storage behavior of antiferroelectrics.
Source: openalex_inverted_index · Quality: baseline

Research context

OpenAlex topics: Ferroelectric and Piezoelectric Materials · Dielectric properties of ceramics · Semiconductor materials and devices

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

School of Integrated Circuits & Wuhan National Lab for Optoelectronics Laboratory & Engineering Research Center for Functional Ceramics of the Ministry of Education, Huazhong University of Science and Technology, Wuhan 430074, P. R. China

Funding

Ministry of Education of the People's Republic of China · Ministry of Science and Technology of the People's Republic of China · Science and Technology Department of Hubei Province · Central University Basic Research Fund of China · Huazhong University of Science and Technology · Ministry of Finance · National Natural Science Foundation of China · Wuhan National Laboratory for Optoelectronics · National Development and Reform Commission of the People's Republic

References (38)

Show source-provided references
1. 10.1021/acs.chemrev.0c0126410.1021/acs.chemrev.0c01264 ↗
2. 10.1039/c1cp22659b10.1039/c1cp22659b ↗
3. 10.1002/adma.20090332810.1002/adma.200903328 ↗
4. 10.1016/j.ceramint.2019.03.00110.1016/j.ceramint.2019.03.001 ↗
5. 10.1016/j.ceramint.2012.12.07110.1016/j.ceramint.2012.12.071 ↗
6. 10.1016/j.ceramint.2014.09.04110.1016/j.ceramint.2014.09.041 ↗
7. 10.1126/science.abi768710.1126/science.abi7687 ↗
8. 10.1039/d0nr05709f10.1039/d0nr05709f ↗
9. 10.1039/c8ta09353a10.1039/c8ta09353a ↗
10. 10.1142/s2010135x2140008710.1142/s2010135x21400087 ↗
11. 10.1142/s2010135x2050033210.1142/s2010135x20500332 ↗
12. 10.1016/j.actamat.2017.12.04810.1016/j.actamat.2017.12.048 ↗
13. 10.1039/c9tc02172h10.1039/c9tc02172h ↗
14. 10.1016/j.jallcom.2019.15269510.1016/j.jallcom.2019.152695 ↗
15. 10.1016/j.jallcom.2021.15944010.1016/j.jallcom.2021.159440 ↗
16. 10.1016/j.jallcom.2020.15678810.1016/j.jallcom.2020.156788 ↗
17. 10.1063/1.502067910.1063/1.5020679 ↗
18. 10.1142/s2010135x2130001210.1142/s2010135x21300012 ↗
19. 10.1016/j.jallcom.2018.11.37110.1016/j.jallcom.2018.11.371 ↗
20. 10.1016/j.msea.2006.01.13310.1016/j.msea.2006.01.133 ↗
21. 10.1021/acsami.5b0746710.1021/acsami.5b07467 ↗
22. 10.1021/acsaelm.1c0023610.1021/acsaelm.1c00236 ↗
23. 10.1016/j.actamat.2019.09.04510.1016/j.actamat.2019.09.045 ↗
24. 10.1021/acs.jpclett.7b0138410.1021/acs.jpclett.7b01384 ↗
25. 10.1016/j.jmat.2021.11.01310.1016/j.jmat.2021.11.013 ↗
26. 10.1039/c4dt03919j10.1039/c4dt03919j ↗
27. 10.1016/j.nanoen.2021.10622210.1016/j.nanoen.2021.106222 ↗
28. 10.1111/jace.1609410.1111/jace.16094 ↗
29. 10.1038/nmat369110.1038/nmat3691 ↗
30. 10.1021/acs.chemrev.9b0050710.1021/acs.chemrev.9b00507 ↗
31. 10.1016/j.ceramint.2020.04.13110.1016/j.ceramint.2020.04.131 ↗
32. 10.1111/j.1551-2916.2011.04629.x10.1111/j.1551-2916.2011.04629.x ↗
33. 10.1002/adfm.20200501210.1002/adfm.202005012 ↗
34. 10.1002/admt.20180011110.1002/admt.201800111 ↗
35. 10.1016/j.actamat.2021.11696510.1016/j.actamat.2021.116965 ↗
36. 10.1016/j.apsusc.2013.12.18010.1016/j.apsusc.2013.12.180 ↗
37. 10.1039/c8ta12232f10.1039/c8ta12232f ↗
38. 10.1039/d1ta08167e10.1039/d1ta08167e ↗