journal article·2018

Anomalous isoelectronic chalcogen rejection in 2D anisotropic vdW TiS 3(1−x) Se 3x trichalcogenides

Ashutosh Agarwal, Ying Qin, Bin Chen, Mark Blei, Kedi Wu, Lei Liu, Yuxia Shen, David Wright, Matthew D. Green, Houlong Zhuang, Sefaattin Tongay

Nanoscale· Volume 10· Issue 33
Publisher page

Abstract

Alloying in semiconductors has enabled many civilian technologies in electronics, optoelectronics, photonics, and others. While the alloying phenomenon is well established in traditional bulk semiconductors owing to a vast array of available ternary phase diagrams, alloying in 2D materials still remains at its seminal stages. This is especially true for transition metal trichalcogenides (TMTCs) such as TiS3 which has been recently predicted to be a direct gap, high carrier mobility, pseudo-1D semiconductor. In this work, we report on an unusual alloying rejection behavior in TiS3(1-x)Se3x vdW crystals. TEM, SEM, EDS, and angle-resolved Raman measurements show that only a miniscule amount (8%) of selenium can be successfully alloyed into a TiS3 host matrix despite vastly different precursor amounts as well as growth temperatures. This unusual behavior contrasts with other vdW systems such as TiS2(1-x)Se2x, MoS2(1-x)Se2x, Mo1-xWxS2, WS2(1-x)Se2x, where continuous alloying can be attained. Angle-resolved Raman and kelvin probe force microscopy measurements offer insights into how selenium alloying influences in-plane structural anisotropy as well as electron affinity values of exfoliated sheets. Our cluster expansion theory calculations show that only the alloys with a small amount of Se can be attained due to energetic instability above/below a certain selenium concentration threshold in the ternary phase diagrams. The overall findings highlight potential challenges in achieving stable Ti based TMTCs alloys.
Source: openalex_inverted_index · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: 2D Materials and Applications · Chalcogenide Semiconductor Thin Films · MXene and MAX Phase Materials

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

School for Engineering of Matter

Transport and Energy

Arizona State University

Tempe

USA

LeRoy Eyring Center for Solid State Science

Funding

National Science Foundation · Army Research Office

References (36)

Show source-provided references
1. Kang · J. Appl. Phys. · 2013 · 11310.1063/1.4799126 ↗
2. Lin · ACS Nano · 2018 · 12 · 89410.1021/acsnano.7b08782 ↗
3. Wang · Nat. Commun. · 2015 · 6 · 1011010.1038/ncomms10110 ↗
4. Huang · Phys. Rev. Lett. · 2015 · 115 · 12680610.1103/PhysRevLett.115.126806 ↗
5. Tongay · Appl. Phys. Lett. · 2014 · 104 · 410.1063/1.4834358 ↗
6. Wang · Chem. Soc. Rev. · 2015 · 44 · 266410.1039/C4CS00287C ↗
7. Xie · Nanoscale · 2015 · 7 · 1839210.1039/C5NR05712D ↗
8. Joshua · 2D Mater. · 2017 · 4 · 02200310.1088/2053-1583/aa6ca6 ↗
9. Island · Sci. Rep. · 2016 · 6 · 2221410.1038/srep22214 ↗
10. Biele · Nano Res. · 2018 · 11 · 22510.1007/s12274-017-1622-3 ↗
11. Aierken · Phys. Chem. Chem. Phys. · 2016 · 18 · 1443410.1039/C6CP01809B ↗
12. Lee · Nat. Commun. · 2015 · 6 · 857310.1038/ncomms9573 ↗
13. Pant · Nanoscale · 2016 · 8 · 1625910.1039/C6NR05238J ↗
14. Wang · Nat. Nanotechnol. · 2015 · 10 · 51710.1038/nnano.2015.71 ↗
15. Ferrer · Thin Solid Films · 2013 · 535 · 39810.1016/j.tsf.2012.10.033 ↗
16. Wu · Nat. Commun. · 2016 · 7 · 1295210.1038/ncomms12952 ↗
17. Kang · Phys. Chem. Chem. Phys. · 2016 · 18 · 1480510.1039/C6CP01125J ↗
18. Lipatov · Nanoscale · 2015 · 7 · 1229110.1039/C5NR01895A ↗
19. Wu · Nano Lett. · 2016 · 16 · 588810.1021/acs.nanolett.6b02766 ↗
20. Lin · ACS Nano · 2015 · 9 · 1124910.1021/acsnano.5b04851 ↗
21. Chenet · Nano Lett. · 2015 · 15 · 566710.1021/acs.nanolett.5b00910 ↗
22. Kong · Nanoscale · 2017 · 9 · 417510.1039/C7NR00711F ↗
23. Huang · ACS Nano · 2016 · 10 · 896410.1021/acsnano.6b05002 ↗
24. Chen · Adv. Mater. · 2017 · 29 · 170120110.1002/adma.201701201 ↗
25. Philipp · Phys. Status Solidi RRL · 2016 · 10 · 18510.1002/pssr.201510412 ↗
26. Kang · Phys. Rev. B: Condens. Matter Mater. Phys. · 2015 · 92 · 07541310.1103/PhysRevB.92.075413 ↗
27. Island · Adv. Mater. · 2015 · 27 · 259510.1002/adma.201405632 ↗
28. Yang · Nanoscale · 2017 · 9 · 1228810.1039/C7NR02397A ↗
29. Silva-Guillén · 2D Mater. · 2017 · 4 · 02508510.1088/2053-1583/aa6b92 ↗
30. Kasai · Nat. Mater. · 2018 · 17 · 24910.1038/s41563-017-0012-2 ↗
31. Kresse · Phys. Rev. B: Condens. Matter Mater. Phys. · 1996 · 54 · 1116910.1103/PhysRevB.54.11169 ↗
32. Van de Walle · CALPHAD: Comput. Coupling Phase Diagrams Thermochem. · 2009 · 33 · 26610.1016/j.calphad.2008.12.005 ↗
33. Perdew · Phys. Rev. Lett. · 1996 · 77 · 386510.1103/PhysRevLett.77.3865 ↗
34. Blöchl · Phys. Rev. B: Condens. Matter Mater. Phys. · 1994 · 50 · 1795310.1103/PhysRevB.50.17953 ↗
35. Kresse · Phys. Rev. B: Condens. Matter Mater. Phys. · 1999 · 59 · 175810.1103/PhysRevB.59.1758 ↗
36. Dudarev · Phys. Rev. B: Condens. Matter Mater. Phys. · 1998 · 57 · 150510.1103/PhysRevB.57.1505 ↗