Proton Conducting Silicon Oxide Membranes as a Fluorine Free Alternative to Nafion for Low Temperature Water Electrolysis

Driven by environmental and health concerns related to per- and polyfluoroalkyl substances (PFAS), there has been growing interest in developing fluorine-free proton (H + ) exchange membrane (PEM) materials for fuel cells and water electrolyzers. In this study, we present a side-by-side comparison of the key transport properties of submicron thick, PFAS-free amorphous silicon dioxide (SiO 2 ) membranes to Nafion, a fluorinated polymer electrolyte membrane that represents the industry standard for PEM fuel cells and electrolyzers. Measurements of proton (H + ) conductivity (σ H + ), hydrogen (H 2 ) permeability ( P H 2 ), and electrical resistivity (ρ e – ) were conducted using model thin films comprised of SiO 2 membranes deposited by atomic layer deposition (ALD). Although the H + conductivity of the SiO 2 membranes is 2–3 orders of magnitude lower than Nafion, the addition of phosphorus dopants (PO x ) improves H + conductivity such that the area specific membrane resistance of thin (<50 nm) PO x -doped SiO 2 membranes is more than an order of magnitude lower than Nafion-117. Importantly, the safe operation of such nanoscale membranes within a PEM electrolyzer is feasible thanks to the low H 2 permeability of dense SiO 2 -based membranes, which are predicted to limit H 2 crossover rates to acceptable levels for pressures up to ≈ 100 bar. As a proof-of-principle demonstration, a chip-scale water electrolyzer based on 100 nm thick PO x -SiO 2 membrane is shown to achieve a current density of 2 A cm –2 at a potential of 2.5 V. If this technology can be successfully scaled up, H + conducting oxide membranes offer an attractive PFAS-free alternative to Nafion for efficient and durable water electrolysis and fuel cell technologies.