Diethylzinc-Assisted Atomic Surface Reduction to Stabilize Li and Mn-Rich NCM

Li and Mn-rich nickel cobalt manganese oxide (LMR-NCM) is one of the most promising cathode materials for realizing next-generation Li-ion batteries due to its high specific capacity of >250 mA h g–1 and operating potential > 4.5 V. Nevertheless, being plagued by severe capacity fading and voltage decay, the commercialization of LMR-NCM appears to be a distant goal. The anionic activity of oxygen and associated phase transformations are the reasons behind the unstable electrochemical performance. The tendency of LMR-NCM to react with CO2 and moisture further makes it prone to interfacial instability and degradation. Here, we report a neoteric method to mitigate the stability issues and improve the electrochemical performance of LMR-NCM by changing the electronic configuration of constituting O and transition metals via diethylzinc-assisted atomic surface reduction (Zn-ASR) using an extremely facile protocol. With the proposed Zn-ASR, a 2–3 nm thin layer of a reduced surface enriched with complex ZnOx or ZnOxRy was obtained on the LMR-NCM particles. X-ray photoelectron spectroscopy suggested the transfer of ethyl groups of diethylzinc to O atoms on the LMR-NCM surface, which ultimately led to the reduction of near-surface Mn and Ni atoms and impeded irreversible anionic activity. The presence of ZnOx/ZnOxRy also resulted in superior charge transfer and resistance against HF. As a result, in contrast to LMR-NCM, the Zn-ASR-treated sample exhibited substantially improved rate capabilities, facilitated charge transfer, enhanced capacity retention, reduced parasitic reactions, and long-term stability as reflected from in-depth electrochemical analysis, in operando gaseous evolution studies, and post-mortem microscopic analysis.