Thermocurable Hyperbranched Polystyrenes for Ultrathin Polymer Dielectrics
Source abstract
Abstract
Thermocurable hyperbranched polystyrenes were successfully synthesized using atom transfer radical polymerization and exhibited superior ultrathin film formation capabilities in comparison with the linear analogues, as assessed by the minimal film thickness attainable by spin-coating without dewetting. They were suitable as ultrathin film organic dielectrics, with parallel plate specific capacitances as high as ∼680 nF/cm2. Similar to high performance inorganic dielectrics, capacitance measurements pointed to the presence of "dead" interfacial capacitance, which could be accounted for by considering the geometric effect of roughness "incommensurability" between metal electrode and polymer film.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Synthesis and properties of polymers · Dendrimers and Hyperbranched Polymers · Advanced Polymer Synthesis and Characterization
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Center for Macromolecular Engineering, Department of Chemistry, Carnegie Mellon University, 4400 Fifth Avenue, Pittsburgh, Pennsylvania 15213
References (54)
Show source-provided references
1. Loschonsky S. · Biomacromolecules · 2008 · 9 · 54310.1021/bm7010714 ↗
2. Ryu D. Y. · Science · 2005 · 308 · 23610.1126/science.1106604 ↗
3. Benhabbour S. R. · Biomaterials · 2008 · 29 · 417710.1016/j.biomaterials.2008.07.016 ↗
4. Boulares-Pender A. · J. Appl. Polym. Sci. · 2009 · 112 · 270110.1002/app.29849 ↗
5. Fang F. · Proc. Natl. Acad. Sci. U.S.A. · 2006 · 103 · 576910.1073/pnas.0509688103 ↗
6. Luo Y. · J. Appl. Polym. Sci. · 2003 · 89 · 151510.1002/app.12229 ↗
7. Nithyanandhan J. · Chem. - Eur. J. · 2004 · 10 · 68910.1002/chem.200305297 ↗
8. Lin W. · J. Phys. Chem. C · 2009 · 113 · 1688410.1021/jp900508p ↗
9. Perez G. P. · Anal. Chem. · 2003 · 75 · 362510.1021/ac0264473 ↗
10. Priya D. N. · ACS Appl. Mater. Interfaces · 2009 · 1 · 268410.1021/am900566n ↗
11. Pinto M. R. · Langmuir · 2003 · 19 · 652310.1021/la034324n ↗
12. Bertrand P. · Macromol. Rapid Commun. · 2000 · 21 · 31910.1002/(SICI)1521-3927(20000401)21:7<319::AID-MARC319>3.0.CO;2-7 ↗
13. Bhattacharya A. · Prog. Polym. Sci. · 2004 · 29 · 76710.1016/j.progpolymsci.2004.05.002 ↗
14. Viswanathan K. · J. Polym. Sci., Part A: Polym. Chem. · 2005 · 43 · 365510.1002/pola.20800 ↗
15. Pallandre A. · Electrophoresis · 2006 · 27 · 58410.1002/elps.200500761 ↗
16. Vestberg R. · J. Polym. Sci., Part A: Polym. Chem. · 2007 · 45 · 283510.1002/pola.22178 ↗
17. Quinn J. F. · Chem. Soc. Rev. · 2007 · 36 · 70710.1039/b610778h ↗
18. Walheim S. · Macromolecules · 1997 · 30 · 499510.1021/ma9619288 ↗
19. Becker J. · Nat. Mater. · 2003 · 2 · 5910.1038/nmat788 ↗
20. Prucker O. · J. Am. Chem. Soc. · 1999 · 121 · 876610.1021/ja990962+ ↗
21. Chan E. W. L. · J. Am. Chem. Soc. · 2002 · 124 · 1223810.1021/ja026159o ↗
22. Fan X. · J. Am. Chem. Soc. · 2005 · 127 · 1584310.1021/ja0532638 ↗
23. Chua L. L. · Appl. Phys. Lett. · 2004 · 84 · 340010.1063/1.1710716 ↗
24. Gao C. · Prog. Polym. Sci. · 2004 · 29 · 18310.1016/j.progpolymsci.2003.12.002 ↗
25. Gao H. · Prog. Polym. Sci. · 2009 · 34 · 31710.1016/j.progpolymsci.2009.01.001 ↗
26. Ishizu K. · Polymer · 2000 · 41 · 608110.1016/S0032-3861(99)00850-2 ↗
27. Nunez C. M. · Macromolecules · 2000 · 33 · 172010.1021/ma991044z ↗
28. Du J. · Macromolecules · 2004 · 37 · 632210.1021/ma0359382 ↗
29. Lu X. · Colloid Polym. Sci. · 2007 · 285 · 59910.1007/s00396-006-1609-1 ↗
30. Braunecker W. A. · Prog. Polym. Sci. · 2007 · 32 · 9310.1016/j.progpolymsci.2006.11.002 ↗
31. Matyjaszewski K. · 200210.1002/0471220450 ↗
32. Matyjaszewski K. · 200710.1002/9783527631421 ↗
33. Frechet J. M. J. · Science · 1995 · 269 · 108010.1126/science.269.5227.1080 ↗
34. Matyjaszewski K. · Macromolecules · 1997 · 30 · 704210.1021/ma970635r ↗
35. Matyjaszewski K. · Macromol. Rapid Commun. · 1998 · 19 · 66510.1002/(SICI)1521-3927(19981201)19:12<665::AID-MARC665>3.0.CO;2-V ↗
36. Wang J. S. · J. Am. Chem. Soc. · 1995 · 117 · 561410.1021/ja00125a035 ↗
37. Patten T. E. · Science · 1996 · 272 · 86610.1126/science.272.5263.866 ↗
38. Tsarevsky N. V. · Chem. Rev. · 2007 · 107 · 227010.1021/cr050947p ↗
39. Ouchi M. · Chem. Rev. · 2009 · 109 · 496310.1021/cr900234b ↗
40. Matyjaszewski K. · Nat. Chem. · 2009 · 1 · 27610.1038/nchem.257 ↗
41. Jakubowski W. · Macromolecules · 2005 · 38 · 413910.1021/ma047389l ↗
42. Matyjaszewski K. · Proc. Natl. Acad. Sci. U.S.A. · 2006 · 103 · 1530910.1073/pnas.0602675103 ↗
43. Jakubowski W. · Angew. Chem., Int. Ed. · 2006 · 45 · 448210.1002/anie.200600272 ↗
44. Isaure F. · J. Mater. Chem. · 2003 · 13 · 270110.1039/B303321J ↗
45. Isaure F. · Macromolecules · 2004 · 37 · 209610.1021/ma030445i ↗
46. Wong K. H. · Chem. Mater. · 2010 · 22 · 187810.1021/cm9034165 ↗
47. Gao H. · Macromolecules · 2009 · 42 · 803910.1021/ma901675r ↗
48. Van Camp W. · J. Polym. Sci., Part A: Polym. Chem. · 2010 · 48 · 201610.1002/pola.23970 ↗
49. Litvinenko G. I. · Macromolecules · 1999 · 32 · 241010.1021/ma981548h ↗
50. Stengel M. · Nature · 2006 · 443 · 67910.1038/nature05148 ↗
51. Sinnamon L. J. · Appl. Phys. Lett. · 2002 · 81 · 70310.1063/1.1494837 ↗
52. Basceri C. · J. Appl. Phys. · 1997 · 82 · 249710.1063/1.366062 ↗
53. Hickmott T. W. · J. Appl. Phys. · 2001 · 89 · 550210.1063/1.1366653 ↗
54. Facchetti A. · Adv. Mater. · 2005 · 17 · 170510.1002/adma.200500517 ↗