Highly Efficient Thermoelectricity Based on Self-Doped Carbon Nanotubes through the Repetitive Filtration Process

The superiority of thermoelectric (TE) performance based on single-walled carbon nanotubes (SWCNTs) has conventionally involved the pursuit of a highly pure semiconducting ( s )-SWCNT and subsequent doping. Herein, we report that a minute quantity of metallic ( m )-SWCNT facilitates the doping of s -SWCNT, leading to the highest achieved power factor (PF) and figure of merit ( zT ) among SWCNT film-based TE devices without compromising the Seebeck coefficient (α). The controlled introduction of trace amounts of m -SWCNT in s -SWCNT films is achieved through repetitive filtration (RF) processes for film preparation. Spectroscopic analyses confirm the efficacy of the RF process in elevating s -SWCNT purity to over 99%, while diminishing levels of m -SWCNT, bundling size, and carbonaceous impurities. The doping states of s -SWCNT films, determined by optical bleaching, vary with the number of RF cycles, attributed to self-doping facilitated by endogenous m -SWCNTs possessing different Fermi levels and O 2 /H 2 O redox environments. TE devices derived from this approach demonstrate that, with an α of as high as 645 μV/K and higher doped states around the mid-RF cycle number, the s -SWCNT film achieves peak PF (8309 μW/m·K 2 ) and zT (0.17). This self-doping strategy proves to be effective for positive doping, enhancing electrical conductivity, and improving TE performance without external dopants.