Effect of Electrode/Electrolyte Coupling on Birnessite (δ-MnO₂) Mechanical Response and Degradation

Understanding the deformation of energy storage electrodes at a local scale and its correlation to electrochemical performance is crucial for designing effective electrode architectures. In this work, the effect of electrolyte cation and electrode morphology on birnessite (δ-MnO 2 ) deformation during charge storage in aqueous electrolytes was investigated using a mechanical cyclic voltammetry approach via operando atomic force microscopy (AFM) and molecular dynamics (MD) simulation. In both K 2 SO 4 and Li 2 SO 4 electrolytes, the δ-MnO 2 host electrode underwent expansion during cation intercalation, but with different potential dependencies. When intercalating Li +, the δ-MnO 2 electrode presents a nonlinear correlation between electrode deformation and electrode height, which is morphologically dependent. These results suggest that the stronger cation–birnessite interaction is the reason for higher local stress heterogeneity when cycling in Li 2 SO 4 electrolyte, which might be the origin of the pronounced electrode degradation in this electrolyte.