journal article·2018-12-12

Restricting Molecular Mobility in Polymer Nanocomposites with Self-Assembling Low-Molecular-Weight Gel Additives

Symone L. M. Alexander, LaShanda T. J. Korley

ACS Applied Materials & Interfaces· Volume 10· Issue 49
Publisher page

Abstract

Multiscale investigation of molecular gel additives in polymer matrices guides understanding of how solution-state assemblies result in mechanically enhanced, solid-state nanocomposites. Model polymers, poly(ethylene oxide- co-epichlorohydrin) (EO-EPI) and poly(vinyl acetate) (PVAc), were utilized as matrices and reinforced by cholesterol-pyridine (CP) nanofiber networks. The CP nanofillers suppress ethylene oxide segment melting for EO-EPI composites, whereas for PVAc nanocomposites, cause a polymer-gel dissociation transition. Incorporation of crystalline CP fiber networks led to an order of magnitude increase in tensile storage modulus due to restrictions on polymer chain mobility. This decrease in molecular mobility was confirmed by decreased loss moduli for both EO-EPI and PVAc composites. Excitingly, PVAc nanocomposites display an additional relaxation mode caused by release of PVAc chains from the transient molecular gel assembly. For both EO-EPI and PVAc composites, bulk flow can be suppressed to temperatures up to 100 °C by simply increasing the CP concentration.
Source: openalex_inverted_index · Quality: baseline

Research context

OpenAlex topics: Supramolecular Self-Assembly in Materials · biodegradable polymer synthesis and properties · Advanced Polymer Synthesis and Characterization

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Department of Materials Science and Engineering, University of Delaware, Newark, Delaware 19716, United States

Department of Chemical and Biomolecular Engineering, University of Delaware, Newark, Delaware 19716, United States

Funding

Division of Graduate Education

References (20)

Show source-provided references
1. 10.1039/c0sm01262a10.1039/c0sm01262a ↗
2. 10.1002/adfm.20100074410.1002/adfm.201000744 ↗
3. 10.1039/c2sm25918d10.1039/c2sm25918d ↗
4. 10.1002/chem.20080211710.1002/chem.200802117 ↗
5. 10.1039/C1SM06580G10.1039/C1SM06580G ↗
6. Landel R. F. · 199310.1201/b16929 ↗
7. 10.1038/s41428-018-0076-010.1038/s41428-018-0076-0 ↗
8. 10.1016/j.tet.2007.05.02710.1016/j.tet.2007.05.027 ↗
9. 10.1039/C6CC02824A10.1039/C6CC02824A ↗
10. 10.1021/ma402618z10.1021/ma402618z ↗
11. Turi E. · 1981
12. 10.1007/s10853-017-1344-710.1007/s10853-017-1344-7 ↗
13. 10.1016/j.ijsolstr.2015.05.01910.1016/j.ijsolstr.2015.05.019 ↗
14. Gupta M. K. · Indian J. Fibre Text. Res. · 2016 · 41 · 235
15. 10.1039/C7RA00686A10.1039/C7RA00686A ↗
16. 10.1016/j.compositesb.2016.03.02810.1016/j.compositesb.2016.03.028 ↗
17. 10.1002/app.4624210.1002/app.46242 ↗
18. 10.1177/09673911080160020310.1177/096739110801600203 ↗
19. Menard K. P. · 200810.1201/9781420053135 ↗
20. Weiss R. G. · 200610.1007/1-4020-3689-2 ↗