Facile Interfacial Reduction Suppresses Redox Chemical Expansion and Promotes the Polaronic to Ionic Transition in Mixed Conducting (Pr,Ce)O2−δ Nanoparticles
Source abstract
Abstract
Mixed ionic/electronic conductors (MIECs) are essential components of solid-state electrochemical devices, such as solid oxide fuel/electrolysis cells. For efficient performance, MIECs are typically nanostructured, to enhance the reaction kinetics. However, the effect of nanostructuring on MIEC chemo-mechanical coupling and transport properties, which also impact cell durability and efficiency, has not yet been well understood. In this work, Pr 0.2 Ce 0.8 O 2−δ (PCO20) nanopowders were prepared by coprecipitation, then sintered in a modified dilatometer at three different temperatures (600, 725, and 850 °C) for microstructure evolution, resulting in three samples with different average particle sizes (23, 30, and 53 nm). The chemical strain and electronic/ionic conductivity were then measured simultaneously on stable nanostructures in four isotherms from 550 to 400 °C with steps in pO 2 (1 to 10 –4 atm O 2 ). A microcrystalline bar was prepared and measured for comparison. Particle size reduction led to a monotonically decreasing isothermal redox chemical strain, confirmed by in situ high-temperature, controlled-atmosphere XRD measurements. The corresponding conductivity measurements provided defect chemical insight into the particle size-dependent chemical expansion behavior. The significant weakening of the pO 2 dependence and decreased activation energy for electrical conduction with decreasing particle size indicated a decrease in the reduction enthalpy of PCO, shifting the transition from (Pr) polaronic to ionic behavior to higher pO 2 . STEM-EELS measurements confirmed the majority of Pr was reduced to 3+ in the nanoparticles, while Ce remained 4+. These results demonstrate suppression of deleterious chemical expansion and tailoring of the dominant charge carrier simply through controlling the particle size, providing insights for MIEC microstructural design.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Advancements in Solid Oxide Fuel Cells · Magnetic and transport properties of perovskites and related materials · Electronic and Structural Properties of Oxides
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Materials Science & Engineering, The Grainger College of Engineering, University of Illinois Urbana−Champaign, 1304 W. Green Street, Urbana, Illinois 61801, United States
Materials Research Laboratory, University of Illinois Urbana−Champaign, 104 S. Goodwin Avenue, Urbana, Illinois 61801, United States
Center for Nanophase Materials Sciences, Oak Ridge, Tennessee 37830, United States
Funding
U.S. Department of Energy · National Science Foundation · PPG Industries
References (69)
Show source-provided references
1. 10.1007/s10008-024-05870-110.1007/s10008-024-05870-1 ↗
2. 10.1021/acs.energyfuels.0c0188710.1021/acs.energyfuels.0c01887 ↗
3. 10.3390/ma910085810.3390/ma9100858 ↗
4. 10.1016/j.nanoen.2017.12.04410.1016/j.nanoen.2017.12.044 ↗
5. 10.1016/S0965-9773(97)00142-610.1016/S0965-9773(97)00142-6 ↗
6. 10.1016/S0167-2738(01)00678-610.1016/S0167-2738(01)00678-6 ↗
7. 10.1016/S0167-2738(01)00677-410.1016/S0167-2738(01)00677-4 ↗
8. 10.1002/aenm.20150037710.1002/aenm.201500377 ↗
9. 10.1039/C4CP05421K10.1039/C4CP05421K ↗
10. 10.1002/adma.20180536010.1002/adma.201805360 ↗
11. 10.1039/D1TA06455J10.1039/D1TA06455J ↗
12. 10.1002/adfm.20240185410.1002/adfm.202401854 ↗
13. 10.1146/annurev-matsci-070813-11332910.1146/annurev-matsci-070813-113329 ↗
14. 10.1016/S0167-2738(96)00588-710.1016/S0167-2738(96)00588-7 ↗
15. 10.1016/j.actamat.2003.12.02010.1016/j.actamat.2003.12.020 ↗
16. 10.1021/acs.chemmater.1c0273910.1021/acs.chemmater.1c02739 ↗
17. 10.1039/D2TA06756K10.1039/D2TA06756K ↗
18. 10.1039/c2cp40754j10.1039/c2cp40754j ↗
19. 10.1016/j.jeurceramsoc.2011.05.03410.1016/j.jeurceramsoc.2011.05.034 ↗
20. 10.1149/2.016212jes10.1149/2.016212jes ↗
21. 10.1007/s10832-014-9946-910.1007/s10832-014-9946-9 ↗
22. 10.1007/s10832-005-6580-610.1007/s10832-005-6580-6 ↗
23. 10.1021/acs.chemmater.7b0512910.1021/acs.chemmater.7b05129 ↗
24. 10.1002/aenm.20220210110.1002/aenm.202202101 ↗
25. 10.1149/1.183709810.1149/1.1837098 ↗
26. 10.1016/j.jpowsour.2016.06.13410.1016/j.jpowsour.2016.06.134 ↗
27. 10.1016/j.apcatb.2006.02.02110.1016/j.apcatb.2006.02.021 ↗
28. 10.1016/j.jpowsour.2012.08.04410.1016/j.jpowsour.2012.08.044 ↗
29. 10.1016/j.joule.2018.07.01610.1016/j.joule.2018.07.016 ↗
30. 10.1016/S0167-2738(99)00319-710.1016/S0167-2738(99)00319-7 ↗
31. 10.1039/c0cp02920c10.1039/c0cp02920c ↗
32. 10.1149/1.327047510.1149/1.3270475 ↗
33. Stefanik, T. S. Electrical properties and defect structures of praseodymium-cerium oxide solid solutions. Massachusetts Institute of Technology, 2003.
34. 10.1007/s10832-004-5195-710.1007/s10832-004-5195-7 ↗
35. 10.1557/jmr.2012.13010.1557/jmr.2012.130 ↗
36. 10.1016/j.ssi.2011.04.01210.1016/j.ssi.2011.04.012 ↗
37. 10.1107/S002188981300353110.1107/S0021889813003531 ↗
38. 10.1016/j.ssi.2011.03.02210.1016/j.ssi.2011.03.022 ↗
39. 10.1021/acsami.8b1691110.1021/acsami.8b16911 ↗
40. 10.1002/adfm.20140020310.1002/adfm.201400203 ↗
41. 10.1016/j.micron.2005.10.00610.1016/j.micron.2005.10.006 ↗
42. 10.1002/jrs.298710.1002/jrs.2987 ↗
43. 10.1080/0950083050047433910.1080/09500830500474339 ↗
44. 10.1063/1.489659010.1063/1.4896590 ↗
45. 10.1103/PhysRevB.32.510710.1103/PhysRevB.32.5107 ↗
46. 10.1063/1.33351710.1063/1.333517 ↗
47. 10.1103/PhysRevB.36.174510.1103/PhysRevB.36.1745 ↗
48. 10.1103/PhysRevA.32.224210.1103/PhysRevA.32.2242 ↗
49. 10.1016/j.ultramic.2016.04.00910.1016/j.ultramic.2016.04.009 ↗
50. 10.1063/5.000794410.1063/5.0007944 ↗
51. 10.1021/jp710363j10.1021/jp710363j ↗
52. 10.1002/adfm.20120210410.1002/adfm.201202104 ↗
53. 10.1021/cm503440v10.1021/cm503440v ↗
54. 10.1021/cm403066p10.1021/cm403066p ↗
55. 10.1021/acs.chemmater.6b0330710.1021/acs.chemmater.6b03307 ↗
56. 10.1557/opl.2011.147510.1557/opl.2011.1475 ↗
57. 10.1039/C7CP00088J10.1039/C7CP00088J ↗
58. 10.1002/adfm.20110264810.1002/adfm.201102648 ↗
59. 10.1021/acs.jpcc.1c0833410.1021/acs.jpcc.1c08334 ↗
60. 10.1016/j.actamat.2009.04.01710.1016/j.actamat.2009.04.017 ↗
61. 10.1021/cm300574v10.1021/cm300574v ↗
62. 10.1039/C7CP04106C10.1039/C7CP04106C ↗
63. 10.1016/j.actamat.2008.12.01110.1016/j.actamat.2008.12.011 ↗
64. 10.1149/1.357009410.1149/1.3570094 ↗
65. 10.1016/j.physe.2016.08.03510.1016/j.physe.2016.08.035 ↗
66. 10.1038/s41598-017-11074-710.1038/s41598-017-11074-7 ↗
67. 10.2298/PAC1903310M10.2298/PAC1903310M ↗
68. 10.1016/j.actamat.2005.11.03210.1016/j.actamat.2005.11.032 ↗
69. 10.1016/S0022-0248(98)01086-010.1016/S0022-0248(98)01086-0 ↗