Poly(ether imide) Film Doped with Protonated Tetra(aniline) Molecules for Efficiently Enhancing the Capacitive Energy Storage Performance
Source abstract
Abstract
The polymer dielectric spacer plays a key role in the performance of film capacitors. However, currently, commercial polymer dielectric films generally have low relative dielectric constants (<4) and low capacitive energy storage densities (<3 J cm –3 ). Here, we report the use of protonated tetra(aniline) (TANI) molecules with a length of 1.3 nm to improve the energy storage performance of poly(ether imide) (PEI) films. With only a small content of TANI doping, i.e., 0.7 wt %, both the dielectric constant and energy storage density of PEI film can be significantly improved, while the dielectric loss remains as low as that of pure PEI. A maximum energy density of 9.4 J cm –3 is achieved. To manifest the efficacy of protonated TANI, polyaniline and deprotonated TANI are also prepared and used as dopants in PEI. The PANI filler can also increase the dielectric constant, while the dielectric loss is increased as well. The deprotonated TANI doped in PEI has no influence on both the dielectric constant and energy density, implying that the protonated amino groups of TANI molecules are responsible for the enhanced dielectric constant of the PEI/TANI composite. The correlation between protonation of TANI dopants and dielectric properties is discussed in detail.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Dielectric materials and actuators · Advanced Sensor and Energy Harvesting Materials · Conducting polymers and applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
School of Materials Science and Engineering, Beihang University, Beijing 100083, China
School of Materials Science and Technology, China University of Geosciences, Beijing 100083, China
Funding
National Natural Science Foundation of China
References (37)
Show source-provided references
1. 10.1016/j.compscitech.2022.10985610.1016/j.compscitech.2022.109856 ↗
2. 10.1002/adma.20180567210.1002/adma.201805672 ↗
3. 10.1021/acsaem.1c0373510.1021/acsaem.1c03735 ↗
4. 10.1002/adfm.20220415510.1002/adfm.202204155 ↗
5. 10.1039/D3MH00907F10.1039/D3MH00907F ↗
6. 10.1021/acs.chemrev.1c0079310.1021/acs.chemrev.1c00793 ↗
7. 10.1002/macp.20210004910.1002/macp.202100049 ↗
8. 10.1002/smll.20230051010.1002/smll.202300510 ↗
9. 10.1002/adfm.20220084810.1002/adfm.202200848 ↗
10. 10.1021/acsami.2c0096910.1021/acsami.2c00969 ↗
11. 10.1039/D1TA00974E10.1039/D1TA00974E ↗
12. 10.1021/acsami.2c1811310.1021/acsami.2c18113 ↗
13. 10.1038/s41467-019-12391-310.1038/s41467-019-12391-3 ↗
14. 10.1002/adma.20220745110.1002/adma.202207451 ↗
15. 10.1002/adma.20230780410.1002/adma.202307804 ↗
16. 10.1002/adma.20230417510.1002/adma.202304175 ↗
17. 10.1039/D3TC04715F10.1039/D3TC04715F ↗
18. 10.1109/TDEI.2023.334211110.1109/TDEI.2023.3342111 ↗
19. 10.1038/s41467-020-17760-x10.1038/s41467-020-17760-x ↗
20. 10.1016/S0079-6700(98)00008-210.1016/S0079-6700(98)00008-2 ↗
21. 10.1039/D1MH01081F10.1039/D1MH01081F ↗
22. 10.1016/j.polymer.2004.05.00710.1016/j.polymer.2004.05.007 ↗
23. 10.1016/j.electacta.2020.13622910.1016/j.electacta.2020.136229 ↗
24. 10.1016/j.apsusc.2018.10.18010.1016/j.apsusc.2018.10.180 ↗
25. 10.1021/am100293r10.1021/am100293r ↗
26. 10.1021/ja101418410.1021/ja1014184 ↗
27. 10.1039/C5TC02093J10.1039/C5TC02093J ↗
28. 10.1002/marc.20210011610.1002/marc.202100116 ↗
29. 10.1016/j.ceramint.2022.04.01710.1016/j.ceramint.2022.04.017 ↗
30. 10.1016/j.matlet.2022.13351010.1016/j.matlet.2022.133510 ↗
31. 10.1021/acsami.3c0677810.1021/acsami.3c06778 ↗
32. 10.1007/s10118-024-3068-x10.1007/s10118-024-3068-x ↗
33. 10.1016/j.compscitech.2020.10852810.1016/j.compscitech.2020.108528 ↗
34. 10.1016/j.mtener.2022.10116110.1016/j.mtener.2022.101161 ↗
35. 10.1016/j.compscitech.2020.10850110.1016/j.compscitech.2020.108501 ↗
36. 10.1021/acs.macromol.7b0063310.1021/acs.macromol.7b00633 ↗
37. 10.1016/j.comptc.2014.07.02010.1016/j.comptc.2014.07.020 ↗