Robust Activity and Stability of P-Doped Fe–Carbon Composites Derived from MOF for Bromate Reduction

Iron-based materials are effective for the reductive removal of the disinfection byproduct bromate in water, while the construction of highly stable and active Fe-based materials with wide pH adaptability remains greatly challenging. In this study, highly dispersed iron phosphide-decorated porous carbon (Fe 2 P( x )@P( z )NC- y ) was prepared via the thermal hydrolysis of Fe@ZIF-8, followed by phosphorus doping (P-doping) and pyrolysis. The reduction performances of Fe 2 P( x )@P( z )NC- y for bromate reduction were evaluated. Characterization results showed that the Fe, P, and N elements were homogeneously distributed in the carbonaceous matrix. P-doping regulated the coordination environment of Fe atoms and enhanced the conductivity, porosity, and wettability of the carbonaceous matrix. As a result, Fe 2 P( x )@P(1.0)NC-950 exhibited enhanced reactivity and stability with an intrinsic reduction kinetic constant ( k int ) 1.53–1.85 times higher than Fe( x )@NC-950 without P-doping. Furthermore, Fe 2 P(0.125)@P(1.0)NC-950 displayed superior reduction efficiency and prominent stability with very low Fe leaching (4.53–22.98 μg L –1 ) in a wide pH range of 4.0–10.0. The used Fe 2 P(0.125)@P(1.0)NC-950 could be regenerated by phosphating, and the regenerated Fe 2 P(0.125)@P(1.0)NC-950 maintained 85% of its primary reduction activity after five reuse cycles. The study clearly demonstrates that Fe 2 P-decorated porous carbon can be applied as a robust and stable Fe-based material in aqueous bromate reduction.