Dissolution Mechanism of Eutectic and Hypereutectic Mg–Sn Alloy Anodes for Magnesium Rechargeable Batteries

Xize Chen, Shanghai Wei, Yigang Yan, Fanglei Tong, Geoffrey I. N. Waterhouse, Tilo Söhnel, Mark P. Taylor, Peng Cao

ACS Applied Materials & Interfaces· Volume 15· Issue 27
Publisher page

Abstract

Magnesium rechargeable batteries (MRBs) are presently attracting much attention due to their low cost, high safety, and high theoretical volumetric capacity. Traditionally, pure magnesium metal has been used as an anode for MRBs, but its poor cycle performance, modest compatibility with conventional electrolytes, and sluggish kinetics limit the further development of MRBs. In this work, eutectic and hypereutectic Mg–Sn alloys were designed and studied as anodes for MRBs. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) results confirmed that these alloys contained unique microstructures consisting of α-Mg, Mg 2 Sn, and eutectic phases. The dissolution processes of the Mg–Sn alloys were studied in an all-phenyl-complex (APC) electrolyte. A multiple-step electrochemical dissolution process and a special adsorption interface layer were established for the Mg–Sn alloy anodes with an eutectic phase. Hypereutectic alloys with mixed phases showed better battery performance than the eutectic alloy owing to their superior mechanical properties. In addition, the morphology and Mg dissolution mechanism of the Mg–Sn alloys during the 1 st dissolution process were characterized and discussed.
Source: openalex_inverted_index · Quality: baseline

Research context

OpenAlex topics: Magnesium Alloys: Properties and Applications · Hydrogen Storage and Materials · Aluminum Alloys Composites Properties

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Department of Chemical and Materials Engineering, Faculty of Engineering, The University of Auckland, Auckland 1142, New Zealand

Institute of New Energy and Low-Carbon Technology, Sichuan University, Chengdu 610065, China

School of Chemical Sciences, University of Auckland, Auckland 1010, New Zealand

MacDiarmid Institute for Advanced Materials and Nanotechnology, Victoria University of Wellington, PO Box 600, Wellington 6140, New Zealand

New Zealand Product Accelerator, Faculty of Engineering, The University of Auckland, Auckland 1142, New Zealand

Funding

Ministry of Business, Innovation and Employment · Marsden Fund

References (51)

Show source-provided references
1. 10.1016/j.jpowsour.2012.10.06010.1016/j.jpowsour.2012.10.060 ↗
2. Yuan X. · 2011
3. Scrosati B. · 201310.1002/9781118615515 ↗
4. 10.1016/j.esci.2022.04.00510.1016/j.esci.2022.04.005 ↗
5. 10.1016/j.jpowsour.2010.07.02010.1016/j.jpowsour.2010.07.020 ↗
6. 10.1016/j.electacta.2012.05.00110.1016/j.electacta.2012.05.001 ↗
7. 10.1149/1.138798010.1149/1.1387980 ↗
8. 10.1016/j.pmatsci.2014.04.00110.1016/j.pmatsci.2014.04.001 ↗
9. 10.1016/j.biomaterials.2005.10.00310.1016/j.biomaterials.2005.10.003 ↗
10. 10.1016/j.actbio.2010.02.02810.1016/j.actbio.2010.02.028 ↗
11. 10.1021/ja109851210.1021/ja1098512 ↗
12. 10.1039/c3ee40871j10.1039/c3ee40871j ↗
13. 10.1557/mrs.2014.6110.1557/mrs.2014.61 ↗
14. 10.1021/acs.jpclett.6b0038410.1021/acs.jpclett.6b00384 ↗
15. 10.1039/c2ee03029b10.1039/c2ee03029b ↗
16. 10.1016/j.ccr.2014.11.00510.1016/j.ccr.2014.11.005 ↗
17. 10.1002/eem2.1248610.1002/eem2.12486 ↗
18. 10.1002/idm2.1200410.1002/idm2.12004 ↗
19. 10.1002/adma.20070149510.1002/adma.200701495 ↗
20. 10.1038/3503755310.1038/35037553 ↗
21. 10.1149/1.280617510.1149/1.2806175 ↗
22. 10.1016/j.jpowsour.2010.11.14110.1016/j.jpowsour.2010.11.141 ↗
23. 10.1016/j.ensm.2022.03.04610.1016/j.ensm.2022.03.046 ↗
24. 10.1002/adma.20220188610.1002/adma.202201886 ↗
25. 10.1016/j.elecom.2011.12.01010.1016/j.elecom.2011.12.010 ↗
26. 10.1039/c2cc34673g10.1039/c2cc34673g ↗
27. 10.1002/celc.20160040010.1002/celc.201600400 ↗
28. 10.1016/j.jpowsour.2017.09.05410.1016/j.jpowsour.2017.09.054 ↗
29. 10.1021/acs.chemmater.7b0412410.1021/acs.chemmater.7b04124 ↗
30. 10.1002/admi.20180103910.1002/admi.201801039 ↗
31. 10.1002/aenm.20200069710.1002/aenm.202000697 ↗
32. 10.1016/j.jma.2020.09.01710.1016/j.jma.2020.09.017 ↗
33. 10.1039/d0ta05828a10.1039/d0ta05828a ↗
34. 10.1016/j.electacta.2021.13933610.1016/j.electacta.2021.139336 ↗
35. 10.1016/j.msea.2013.07.05110.1016/j.msea.2013.07.051 ↗
36. 10.1021/cm040132h10.1021/cm040132h ↗
37. 10.1016/j.corsci.2020.10869510.1016/j.corsci.2020.108695 ↗
38. 10.1103/physrevb.54.1116910.1103/physrevb.54.11169 ↗
39. 10.1016/0927-0256(96)00008-010.1016/0927-0256(96)00008-0 ↗
40. 10.1103/physrevb.54.1653310.1103/physrevb.54.16533 ↗
41. 10.1080/0141861930820715810.1080/01418619308207158 ↗
42. 10.1016/S0378-7753(03)00132-010.1016/S0378-7753(03)00132-0 ↗
43. 10.1149/2.118306jes10.1149/2.118306jes ↗
44. 10.1149/1.139094910.1149/1.1390949 ↗
45. 10.1016/j.matchemphys.2016.07.04210.1016/j.matchemphys.2016.07.042 ↗
46. 10.1016/j.corsci.2012.05.01910.1016/j.corsci.2012.05.019 ↗
47. 10.1016/j.scriptamat.2007.10.02710.1016/j.scriptamat.2007.10.027 ↗
48. 10.1149/1.221810810.1149/1.2218108 ↗
49. 10.1149/1.137982810.1149/1.1379828 ↗
50. 10.1038/nenergy.2016.1010.1038/nenergy.2016.10 ↗
51. 10.1021/acsenergylett.0c0234310.1021/acsenergylett.0c02343 ↗