Highly Conductive Supramolecular Salt Gel Electrolyte for Flexible Supercapacitors

Conductive gels have greatly facilitated the development of flexible energy storage devices, including supercapacitors, batteries, and triboelectric nanogenerators. However, it is challenging for gel electrolytes to tackle the trade-off issues between mechanical properties and conductivity. Herein, a strategy of all inorganic salt-driven supramolecular networks is presented to construct gel electrolytes with high conductivity and reliable mechanical performance for flexible supercapacitors. The salt gel is successfully fabricated by combining a salt supramolecular network constructed by NH 4 Mo 7 O 24 ·4H 2 O and FeCl 3 ·6H 2 O and a polymer network of poly(vinyl alcohol). The inorganic salt supramolecular network serves as a rigid self-supporting framework in the hydrogel system for improving the mechanical properties and providing abundant active sites for accelerating ion transport. Furthermore, the salt gel-enabled supercapacitors are equipped and exhibit a high specific capacitance (199.4 mF cm –2 ) and excellent energy density (27.69 μWh cm –2 ). Moreover, the flexible supercapacitors not only present remarkable cyclic stability after 3000 charging/discharging cycles but also exhibit good electrochemical stability even under severe deformation conditions. The strategy of salt-gel-driven flexible supercapacitors would provide fresh thinking for the development of advanced flexible energy storage fields.