Hierarchical Composite with Self-Adaptive Anisotropic Deformation for Thermal Protection System

Rigid thermal protection materials such as ultra-high-temperature ceramics are desirable for applications in aerospace vehicles, but few materials can currently satisfy the emerging high-temperature sealing requirements for dynamic gaps created by the mismatch of the thermal expansion of different protection layers. Here, we design and fabricate a flexible biomimetic anisotropic deformation composite by multilayer cocuring onto fiber fabrics. It displays superior anisotropic deformation, whose longitudinal expansion ratio is 48 times greater than the transverse expansion ratio at specific temperatures. Furthermore, the ordered carbon structure created by transition-metal-catalyzed graphitization and the C/Si synergistic effect resulting from the combination of biomimetic fiber fabrics and SR enable the in situ formation of a high-temperature-resistant SiC crystalline phase within the char layer, ultimately resulting in exceptional thermal protection properties. By constructing hollow structures in situ, the back temperature of the composite, which is only 4.33 mm thick, is stabilized at 140 °C under the condition of continuous butane flame ablation (1300 °C) for 420 s. Multilayer structure and flexible features can facilitate large-scale preparation and arbitrary cutting and bending, adapted to different thermal protection areas.