Implementation of Different Conversion/Alloy Active Materials as Anodes for Lithium-Based Solid-State Batteries

To complement or outperform lithium-ion batteries with liquid electrolyte as energy storage devices, a high-energy as well as high-power anode material must be used in solid-state batteries. An overlooked class of anode materials is the one of conversion/alloy active materials (e.g., SnO 2, which is already extensively studied in liquid electrolyte-based batteries). Conversion/alloy active materials offer high specific capacities and often also fast lithium-ion diffusion and reaction kinetics, which are required for high C-rates and application in high-energy and high-power devices such as battery electric vehicles. To date, there are only very few reports on conversion/alloy active materials─namely, SnO 2 ─as anode material in sulfide-based solid-state batteries, with a relatively complex electrode design. Otherwise, conversion-alloy active materials are used as a seed layer or interlayer for a homogeneous Li deposition or to mitigate the formation and growth of the SEI, respectively. Within this work, four different conversion/alloy active materials─SnO 2, Sn 0.9 Fe 0.1 O 2, ZnO, and Zn 0.9 Fe 0.1 O─are synthesized and incorporated as negative active materials (“anodes”) in composite electrodes into SSBs with Li 6 PS 5 Cl as solid electrolyte. The structure and the microstructure of the as-synthesized active materials and composite electrodes are investigated by XRD, SEM, and FIB-SEM. All active materials are evaluated based on their C-rate performance and long-term cyclability by galvanostatic cycling under a constant pressure of 40 MPa. Furthermore, light is shed on the degradation processes that take place at the interface between the active material and solid electrolyte. It is evidenced that the decomposition of Li 6 PS 5 Cl to LiCl, Li 2 S, and Li 3 P at the anode is amplified by Fe substitution. Lastly, a 2D sheet electrode is designed and cycled to tackle the interfacial degradation processes. This approach leads to an improved C-rate performance (factor of 3) as well as long-term cyclability (factor of 2.3).