Effect of the Synergistic Interaction of Micro- and Nanostructures with Silver Ions on the Biocompatibility and Antimicrobial Properties of Ti-15Mo-2.5Ag

Titanium and titanium alloys have the advantages of a low density and a close elastic modulus to natural bone, which can reduce the stress-shielding effect and become one of the first choices for human hard tissue replacement and repair. However, implant site infection is still one of the main reasons for implantation failure. In this paper, 2.5 wt % Ag element was added to Ti-15Mo to obtain a low modulus, and a surface anodization was applied to improve the surface biocompatibility. The elastic modulus, micromorphology, surface elemental valence, corrosion resistance, antimicrobial properties, and cytocompatibility were investigated by mechanical tests, scanning electron microscopy, X-ray photoelectron spectroscopy, electrochemical tests, inductively coupled plasma spectroscopy, plate counting method, and cellular tests. The experimental results showed that the anodized Ti-15Mo-2.5Ag sample exhibited an elastic modulus of 79 GPa, a strong corrosion resistance, a strong antimicrobial ability of ≥99.99%, and good biocompatibility. It was demonstrated that the formation of Ag 2 O on the surface and Ag ion release improved the antimicrobial properties and that the structural synergism of silver ions with micro- and nanostructures played an important role in promoting the early spreading of cells and improving the cytocompatibility.