Unveiling the Potential of Pt Nanoparticle-Decorated PEDOT:PSS Membranes for Efficient Gas Separation

In the dynamic landscape of industrial processes, membrane technology offers a paradigm shift beyond energy-intensive separation techniques, exemplifying a progressive leap toward sustainability. In this regard, highly flexible and uniform poly(3,4-ethylenedioxythiophene)polystyrenesulfonate (PEDOT:PSS)-engineered membranes at a reduced thickness have been fabricated on track-etched poly(ethylene terephthalate) (PET) substrates. The membranes were functionalized and embedded with platinum nanoparticles (Pt NPs) having a higher affinity toward H 2 gas. The materials and fabricated membranes were characterized by using high-resolution transmission electron microscopy (HRTEM) and field emission scanning electron microscopy (FESEM) techniques for morphological and structural analysis. FTIR and Raman characterizations were performed to study the characteristic bonds. The uniformity and quantification of Pt nanoparticle binding were tested through inductively coupled plasma mass spectrometry (ICP–MS) studies and FESEM with EDS mapping. The gas separation performance was studied using H 2, N 2, and CO 2 gases in pure and mixed (H 2 /CO 2 in 50:50) states. It was observed that the modified membrane showed a 116% increment in H 2 permeability and 82 and 107% increment in H 2 /CO 2 and H 2 /N 2 selectivity values with pure gas, while a 121% increment in H 2 permeability and 156% increment in H 2 /CO 2 selectivity using mixed gas. The separation performance in pure and mixed gas states with repeated experiments conspicuously highlighted their prospective viability as prime contenders for gas separation applications.