Extremely Low Lattice Thermal Conductivity and Significantly Enhanced Near-Room-Temperature Thermoelectric Performance in α-Cu₂Se through the Incorporation of Porous Carbon

In this work, a series of Cu 2 Se/ x wt % porous carbon (PC) ( x = 0, 0.2, 0.4, 0.6, 0.8, 1) composite materials were synthesized by ball milling and spark plasma sintering (SPS). The highly ordered porous carbon was synthesized by a hydrothermal method using mesoporous silica (SBA-15) as the template. X-ray diffraction results show that the incorporation of porous carbon induces a phase transition of Cu 2 Se from the β phase to the α phase. Meanwhile, the addition of porous carbon reduces the carrier concentration from 2.7 × 10 21 to 2.45 × 10 20 cm –3 by 1 order of magnitude. The decrease of the carrier concentration leads to the reduction of electrical conductivity and the increase of the Seebeck coefficient, which results in the enhancement of the power factor. On the other hand, the incorporation of porous carbon into Cu 2 Se increases the porosity of the composites and also introduces more interfaces between the two materials, which is evidenced by positron annihilation lifetime measurements. Both pores and interfaces greatly enhance phonon scattering, leading to extremely low lattice thermal conductivity. In addition, the decrease of electrical conductivity also causes a sufficient reduction in electronic thermal conductivity. Due to the above synergistic effects, the thermoelectric performance of the Cu 2 Se/PC composite is significantly enhanced with a maximum ZT value of 0.92 at 403 K in the Cu 2 Se/1 wt % PC composite, which is close to that of the Bi 2 Te 3 -based materials. Our work shows that α-Cu 2 Se has great potential for near-room-temperature thermoelectric materials.