Scalable Dry Process for Fabricating a Na Superionic Conductor-Type Solid Electrolyte Sheet

The cost reduction and mass production of oxide-based solid electrolytes are critical for the commercialization of all-solid-state batteries. In this study, an environmentally friendly, low-cost, and high-density oxide-based Na superionic conductor-type solid electrolyte sheet was fabricated via a dry process without the use of any solvent. The polytetrafluoroethylene (PTFE), used as a binder, was transformed into thin thread-like structures via shear force, resulting in a flexible solid electrolyte sheet. The solid electrolyte powder quantity was limited to 50 wt % for fabricating a uniform green sheet via the wet process. However, when the dry process was employed for green sheet fabrication, the solid electrolyte powder quantity could be increased to values exceeding 95 wt %. Therefore, the green sheets produced by using the dry process demonstrated a higher density than those fabricated by using the wet process. The binder content and particle size affected the ionic conductivity of a solid electrolyte sheet fabricated via a dry process. The sheet obtained via the blending of 3 wt % PTFE binder with a solid electrolyte powder, finely ground using a planetary ball mill, which exhibited the highest total ionic conductivity of 1.03 mS cm –1 .