Comparative Study of Vinylene Carbonate and Lithium Difluoro(oxalate)borate Additives in a SiOx/Graphite Anode Lithium-Ion Battery in the Presence of Fluoroethylene Carbonate

Xiaozhou Huang, John Shea, Junxiang Liu, Nader Marandian Hagh, Shubha Nageswaran, Jing Wang, Xianyang Wu, Gihan Kwon, Seoung-Bum Son, Tongchao Liu, Jihyeon Gim, Chi-Cheung Su, Pei Dong, Chengcheng Fang, Matthew Li, Khalil Amine, Umamaheswari Jankairaman

Publisher page

Abstract

The SiO x /graphite composite is recognized as a promising anode material for lithium-ion batteries (LIBs), owing to the high theoretical capacity of SiO x combined with the excellent stability of graphite. However, the inherent disadvantage of volume expansion in silicon-based anodes places significant challenges on the solid electrolyte interphase (SEI) and severely degrades the electrochemical performance. Rational formulation of electrolyte, including its additives, is crucial in accommodating and optimizing the composition of the SEI and enhancing the cell performance. In this work, we present a comparative study of vinylene carbonate (VC) and lithium difluoro(oxalate)borate (LiDFOB) additives combined with fluoroethylene carbonate (FEC) in the electrolyte for SiO x /graphite∥LiNi 1– x – y – z Co x Mn y Al z O 2 full cells. VC outperformed LiDFOB as an additive, delivering higher capacity cycling, higher Coulombic efficiency, and better cycle stability up to 400 cycles. XPS and impedance analyses reveal that LiDFOB contributed to SEI/CEI with both a lower proportion of LiF and a higher proportion of poly(VC), which tended to produce higher cell impedance. XRD and XANES further indicated that using the LiDFOB additive, the NCMA cycled to a shallower degree than that of the VC additive. Although the VC additive maintained a higher capacity up to 400 cycles, microstrain and SEM analyses show a higher strained NCMA along with clear evidence of cracking over the surface of the NCMA particle in VC-based electrolyte but not in LiDFOB. This suggests that the negative influence of LiDFOB at the anode (inferior SEI) supersedes the negative impact of both a cracked NCMA and a deeper cycled NCMA and SiO x -based anode.
Source: openalex_inverted_index · Quality: baseline

Research context

OpenAlex topics: Advancements in Battery Materials · Advanced Battery Materials and Technologies · Advanced Battery Technologies Research

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Chemical Sciences and Engineering Division

Argonne National Laboratory

Department of Mechanical Engineering

George Mason University

Advanced Battery Cell Engineering

General Motors

National Synchrotron Light Source II

Brookhaven National Laboratory

Department of Chemical Engineering and Materials Science

Michigan State University

Funding

Vehicle Technologies Office · General Motors Corporation

References (38)

Show source-provided references
1. 10.1149/2.0251701jes10.1149/2.0251701jes ↗
2. 10.1002/adfm.20231155110.1002/adfm.202311551 ↗
3. 10.1016/j.nanoen.2024.10927910.1016/j.nanoen.2024.109279 ↗
4. 10.1021/acscentsci.7b0028810.1021/acscentsci.7b00288 ↗
5. 10.1021/acs.chemrev.1c0056510.1021/acs.chemrev.1c00565 ↗
6. 10.1149/1945-7111/ad264810.1149/1945-7111/ad2648 ↗
7. 10.1016/j.ensm.2022.01.04210.1016/j.ensm.2022.01.042 ↗
8. 10.1016/j.jechem.2021.04.01310.1016/j.jechem.2021.04.013 ↗
9. 10.3866/PKU.WHXB20230805310.3866/PKU.WHXB202308053 ↗
10. 10.31635/ccschem.023.20230280810.31635/ccschem.023.202302808 ↗
11. 10.3866/PKU.WHXB20230600610.3866/PKU.WHXB202306006 ↗
12. 10.3390/batteries910048510.3390/batteries9100485 ↗
13. 10.1002/smll.20210264110.1002/smll.202102641 ↗
14. 10.1016/j.jpowsour.2017.07.07310.1016/j.jpowsour.2017.07.073 ↗
15. 10.1021/acsenergylett.7b0016310.1021/acsenergylett.7b00163 ↗
16. 10.1002/anie.20171290710.1002/anie.201712907 ↗
17. 10.1149/2.1441712jes10.1149/2.1441712jes ↗
18. 10.1149/1945-7111/acdd2610.1149/1945-7111/acdd26 ↗
19. 10.1016/j.electacta.2016.12.12610.1016/j.electacta.2016.12.126 ↗
20. 10.1002/anie.20070428710.1002/anie.200704287 ↗
21. 10.1021/jacs.8b0340810.1021/jacs.8b03408 ↗
22. 10.1007/s10800-012-0398-010.1007/s10800-012-0398-0 ↗
23. 10.1149/2.076205jes10.1149/2.076205jes ↗
24. 10.1021/acsomega.7b0119610.1021/acsomega.7b01196 ↗
25. 10.1021/acs.chemmater.3c0149610.1021/acs.chemmater.3c01496 ↗
26. 10.1021/acsami.7b1539510.1021/acsami.7b15395 ↗
27. 10.1016/j.mtener.2022.10124210.1016/j.mtener.2022.101242 ↗
28. 10.1016/j.electacta.2018.03.10810.1016/j.electacta.2018.03.108 ↗
29. 10.1016/j.mtsust.2022.10017110.1016/j.mtsust.2022.100171 ↗
30. 10.1038/s41560-018-0199-810.1038/s41560-018-0199-8 ↗
31. 10.1039/C8EE00364E10.1039/C8EE00364E ↗
32. 10.1149/2.0731412jes10.1149/2.0731412jes ↗
33. 10.1021/acsami.4c0103210.1021/acsami.4c01032 ↗
34. 10.1149/1945-7111/ac315810.1149/1945-7111/ac3158 ↗
35. 10.1016/j.nanoen.2020.10528210.1016/j.nanoen.2020.105282 ↗
36. 10.1002/aenm.20180306610.1002/aenm.201803066 ↗
37. 10.1021/acsenergylett.8b0249910.1021/acsenergylett.8b02499 ↗
38. 10.1016/j.solidstatesciences.2010.11.02410.1016/j.solidstatesciences.2010.11.024 ↗