Critical Contribution of Imbalanced Charge Loss to Performance Deterioration of Si-Based Lithium-Ion Cells during Calendar Aging

Increasing the energy density of lithium-ion batteries, and thereby reducing costs, is a major target for industry and academic research. One of the best opportunities is to replace the traditional graphite anode with a high-capacity anode material, such as silicon. However, Si-based lithium-ion batteries have been widely reported to suffer from a limited calendar life for automobile applications. Heretofore, there lacks a fundamental understanding of calendar aging for rationally developing mitigation strategies. Both open-circuit voltage and voltage-hold aging protocols were utilized to characterize the aging behavior of Si-based cells. Particularly, a high-precision leakage current measurement was applied to quantitatively measure the rate of parasitic reactions at the electrode/electrolyte interface. The rate of parasitic reactions at the Si anode was found 5 times and 15 times faster than those of LiNi 0.8 Mn 0.1 Co 0.1 O 2 and LiFePO 4 cathodes, respectively. The imbalanced charge loss from parasitic reactions plays a critical role in exacerbating performance deterioration. In addition, a linear relationship between capacity loss and charge consumption from parasitic reactions provides fundamental support to assess calendar life through voltage-hold tests. These new findings imply that longer calendar life can be achieved by suppressing parasitic reactions at the Si anode to balance charge consumption during calendar aging.